Electroplate grade PC/ABS alloy material and preparation method thereof

An alloy material and electroplating-grade technology, applied in the field of electroplating grade PC/ABS alloy products and its preparation, electroplating grade PC/ABS alloy material and its preparation, can solve the problem of surface defects after plating, damage to material strength, and low yield And other problems, to achieve good electroplating binding force, improve chemical resistance, high electroplating binding force effect

Active Publication Date: 2018-07-06
WANHUA CHEM GRP CO LTD
View PDF11 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current methods used to improve the bonding force of PC / ABS electroplating, in addition to adding a large amount of ABS or high rubber powder to increase the rubber phase, and adding inorganic fillers to increase the etching point, these two methods will destroy the strength and other properties of the material, and In the electroplating process, there will be shortcomings such as low yield rate and defects on the surface after plating. Therefore, it is urgent to prepare an electroplating grade PC / ABS alloy material with high electroplating bonding force, less defects after plating, and excellent comprehensive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electroplate grade PC/ABS alloy material and preparation method thereof
  • Electroplate grade PC/ABS alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] It includes the following raw materials by weight: PC-1: 10 parts, ABS-1: 70 parts, carboxyl-terminated nitrile rubber 20 parts, antioxidant 0.3 part, lubricant 0.4 part. The material composition is added into a high-speed mixer for mixing, then added into a twin-screw extruder, extruded and granulated, and the temperature in the processing temperature zone is controlled at 200-240°C. After the granulation is completed, dry at 70-90°C for 3-4 hours to fully remove moisture, control the injection mold temperature at 60-90°C, barrel temperature at 220-250°C, injection speed at 30-70mm / s, and injection pressure at 30-70bar. An electroplating grade PC / ABS alloy injection molded product of 140×90×3 mm was obtained.

Embodiment 2

[0050] It includes the following raw materials by weight: PC-1: 30 parts, ABS-1: 45 parts, carboxyl-terminated nitrile rubber 25 parts, antioxidant 0.3 part, lubricant 0.4 part. The material composition is added into a high-speed mixer for mixing, then added into a twin-screw extruder, extruded and granulated, and the temperature in the processing temperature zone is controlled at 200-240°C. After the granulation is completed, dry at 70-90°C for 3-4 hours to fully remove moisture, control the injection mold temperature at 60-90°C, barrel temperature at 220-250°C, injection speed at 30-70mm / s, and injection pressure at 30-70bar. An electroplating grade PC / ABS alloy injection molded product of 140×90×3 mm was obtained.

Embodiment 3

[0052] It includes the following raw materials by weight: PC-1: 40 parts, ABS-1: 35 parts, carboxy-terminated nitrile rubber 25 parts, antioxidant 0.3 part, lubricant 0.4 part. The material composition is added into a high-speed mixer for mixing, then added into a twin-screw extruder, extruded and granulated, and the temperature in the processing temperature zone is controlled at 200-240°C. After the granulation is completed, dry at 70-90°C for 3-4 hours to fully remove moisture, control the injection mold temperature at 60-90°C, barrel temperature at 220-250°C, injection speed at 30-70mm / s, and injection pressure at 30-70bar. An electroplating grade PC / ABS alloy injection molded product of 140×90×3 mm was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides an electroplate grade PC / ABS alloy material with high electroplate binding force and a preparation method of the electroplate grade PC / ABS alloy material. The electroplate gradePC / ABS alloy material comprises: in parts by weight, 10-70 parts of polycarbonate (PC), 10-70 parts of styrene-butadiene-acrylonitrile copolymer (ABS), 20-35 parts of terminated nitrile rubber and acertain parts of optional additives, wherein the total amount of the polycarbonate, styrene-butadiene-acrylonitrile copolymer and terminated nitrile rubber are 100 parts by weight. The injection molding process of the electroplate grade PC / ABS alloy material is further optimized, and a finished product which is made from the electroplate grade PC / ABS alloy material has the advantages of easy electroplating, high electroplate binding force, high yield and few surface defects.

Description

technical field [0001] The invention relates to the field of polymer composite materials, in particular to an electroplating grade PC / ABS alloy material and a preparation method thereof. The present invention further relates to an electroplating grade PC / ABS alloy product and a preparation method thereof. Background technique [0002] Polycarbonate PC has the advantages of high impact strength, high light transmittance, excellent mechanical properties, good heat resistance, flame retardancy, and good dimensional stability. It is widely used in automobiles, electronic appliances, construction and other industries, but it also has some Disadvantages, such as high melt viscosity and large residual internal stress, lead to stress cracking and notch sensitivity. On the other hand, ABS is mainly composed of graft copolymers (polybutadiene as the main chain, styrene and acrylonitrile as branched copolymers), copolymers of styrene and acrylonitrile, and ungrafted polybutadiene. , ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L69/00C08L13/00C08K5/134C08K5/526C08K5/103
CPCC08L13/00C08L55/02C08L69/00C08L2205/03C08K5/1345C08K5/526C08K5/103
Inventor 张钊潘勇军黄岐善
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com