Environment-friendly ecological plate and preparation method thereof
An ecological board, an environmentally friendly technology, applied in the field of building materials, can solve problems affecting physical and mental health, achieve the effect of improving human body feeling and internal circulation system, reducing consumption, and reducing consumption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
example 1
[0026] Take 36g of trimethylolethane, 240g of stearic acid, 200g of myristic acid, and 300g of glyceryl monostearate into a beaker, raise the temperature to 60°C at 5°C / min, and keep it warm at a vacuum of 60kPa. Stir for 1 hour to obtain the substrate impregnating liquid. Take the substrate and soak it in the substrate impregnating liquid, absorb it with 150W ultrasonic power for 20min, then raise the temperature to 80°C at 5°C / min, continue to absorb for 20min, take out the substrate, drain and cool to room temperature, and obtain the inner Core layer, get 10g bamboo charcoal, 5g algae calcium, 2g polyvinyl alcohol, 0.5g cellulose ether, 0.5g wood fiber, 2g tourmaline, 5g bark, 6g environmental protection glue, put into horizontal sand mill, with Grind and disperse at 800r / min for 2 hours to obtain air purification material. Take 5g of nano-silicon chips and 1g of chitosan, add them to 80g of melamine modified resin, stir at 300r / min for 20min, and then impregnate printing pa...
example 2
[0028] Take 45g of trimethylolethane, 300g of stearic acid, 225g of myristic acid, and 375g of glyceryl monostearate into a beaker, raise the temperature to 65°C at 5°C / min, and keep it warm at a vacuum of 70kPa Stir for 1 hour to obtain the substrate impregnating liquid. Take the substrate and soak it in the substrate impregnating liquid, absorb it with 150W ultrasonic power for 25 minutes, then raise the temperature to 85°C at 5°C / min, continue to absorb for 25 minutes, take out the substrate, drain and cool to room temperature, and obtain the inner For the core layer, take 13g bamboo charcoal, 7g algae calcium, 2g polyvinyl alcohol, 0.75g cellulose ether, 0.75g wood fiber, 2.5g tourmaline, 6.5g bark, 8g environmental protection glue, and put them into a horizontal sand mill , grind and disperse at 900r / min for 2h to obtain an air-purifying material, take 7g of nano-silicon chips and 2g of chitosan, add them to 90g of melamine-modified resin, stir at 350r / min for 25min, and t...
example 3
[0030]Take 54g of trimethylolethane, 360g of stearic acid, 250g of myristic acid, and 450g of glyceryl monostearate into a beaker, raise the temperature to 70°C at 5°C / min, and keep it warm at a vacuum of 80kPa. Stir for 2 hours to obtain the substrate impregnating solution. Take the substrate and soak it in the substrate impregnating solution, absorb it with 150W ultrasonic power for 30min, then raise the temperature to 90℃ at 5℃ / min, continue to absorb for 30min, take out the substrate, drain and cool to room temperature, and obtain the inner Core layer, take 15g bamboo charcoal, 10g algae calcium, 3g polyvinyl alcohol, 1.0g cellulose ether, 1.0g wood fiber, 3g tourmaline, 8g bark, 10g environmental protection glue, put into the horizontal sand mill, with Grind and disperse at 1000r / min for 3 hours to obtain air purification materials. Take 8g of nano-silicon chips and 3g of chitosan, add them to 100g of melamine modified resin, stir at 400r / min for 30min, and then impregnate...