Permanent antibiosis mildew-resistant nontoxicity and innocuousness polyester material and preparation method thereof

An antibacterial, mildew-proof, non-toxic and harmless technology, applied in the field of materials, can solve the problems of lack of clear explanation, limited heat resistance, risk of bacterial and mold resistance, and improve the quality of life and health, and the antibacterial effect is reliable. , Improve the effect of physical and mechanical properties

Inactive Publication Date: 2018-08-24
DONGGUAN JISU PLASTIC TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese invention patent application CN105670238A discloses a bactericidal polyester resin. The application uses zeolite powder, nano-titanium dioxide, nano-silver oxide and polyhexamethylene guanidine phosphate as antibacterial agents. The antibacterial efficiency is as high as 99.97%, but it contains organic strong Antibacterial agents, there are risks of bacterial and fungal drug resistance, and heat resistance is limited. In addition, whether there is migration of antibacterial agents is not clearly explained in the invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent antibiosis mildew-resistant nontoxicity and innocuousness polyester material and preparation method thereof
  • Permanent antibiosis mildew-resistant nontoxicity and innocuousness polyester material and preparation method thereof
  • Permanent antibiosis mildew-resistant nontoxicity and innocuousness polyester material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) In terms of parts by mass, first mix 0.2 parts of zeolite silver ion antibacterial agent (IM10D-F) and 0.1 part of air purification material based on titanium dioxide photocatalyst (from Chinese invention patent example 1, patent number is 201610066352.6) Dry at 90°C for 2 hours, then put the dried two substances into a high-speed mixer, add 0.18 parts by weight of new active silicone powder, control the temperature at 100°C, and process for 30 minutes to obtain A materials.

[0036] (2) Dry the bottle-grade polyester at 170°C for 2 hours for later use. In terms of parts by mass, 98.67 parts of bottle-grade polyester chips, 0.25 parts of antioxidant (1010:168=0.15:0.1), 0.3 parts of anti-ultraviolet additive UV234 and 0.3 parts of new active silicone powder (RM4‐ 7051) was added into a high-speed mixer, blended for 5 minutes, and stirred evenly to obtain material B.

[0037] (3) Add material B from the main feeding port of the twin-screw extruder, add material A f...

Embodiment 2

[0039] (1) In terms of parts by mass, first mix 0.22 parts of zeolite silver ion antibacterial agent (IM10D-F) and 0.13 parts of air purification material based on titanium dioxide photocatalyst (from Chinese invention patent example 1, patent number is 201610066352.6) Dry at 90°C for 2 hours, then put the dried two substances into a high-speed mixer, add 0.22 parts by weight of new active silicone powder, control the temperature at 100°C, and process for 30 minutes to obtain A materials.

[0040] (2) Dry the bottle-grade polyester at 170°C for 2 hours for later use. In terms of parts by mass, 98.58 parts of fiber-grade polyester chips, 0.25 parts of antioxidant (1010:168=0.15:0.1), 0.3 parts of anti-ultraviolet additive UV234 and 0.3 parts of new active silicone powder (RM4‐ 7051) was added into a high-speed mixer, blended for 5 minutes, and stirred evenly to obtain material B.

[0041] (3) Add material B from the main feeding port of the twin-screw extruder, add material A...

Embodiment 3

[0043] (1) In terms of parts by mass, first mix 0.22 parts of zeolite silver ion antibacterial agent (IM10D-F) and 0.13 parts of air purification material based on titanium dioxide photocatalyst (from Chinese invention patent example 1, patent number is 201610066352.6) Dry at 90°C for 2 hours, then put the dried two substances into a high-speed mixer, add 0.22 parts by weight of new active silicone powder, control the temperature at 100°C, and process for 30 minutes to obtain A materials.

[0044] (2) Dry the film-grade polyester at 170°C for 2 hours for later use. In terms of parts by mass, 98.58 parts of film-grade polyester chips, 0.25 parts of antioxidant (1010:168=0.15:0.1), 0.3 parts of anti-ultraviolet additive UV234 and 0.3 parts of new active silicone powder (RM4‐ 7051) was added into a high-speed mixer, blended for 5 minutes, and stirred evenly to obtain material B.

[0045] (3) Add material B from the main feeding port of the twin-screw extruder, add material A fr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a permanent antibiosis mildew-resistant nontoxicity and innocuousness polyester material and a preparation method thereof. According to the invention, polyester, a zeolite silver ion antiseptic, an air cleaning material by taking a titanium dioxide photocatalyst as a basic material, an anti-oxidant, an ultraviolet-resistant auxiliary agent, and a dispersant are mixed to prepare the material; wherein the dispersant is active siloxane powder of an American Dow Corning company, and a model is RM4-7051. The preparation method employs novel active siloxane powder as a dispersant, the antibiosis powder is easily enriched at the surface of a carrier, the antibiosis powder is firmly controlled in the carrier resin without migration, long-term biological security and stability can be kept, a contact area of the antiseptic and microbe can be greatly enhanced, and the antibiosis deodorizing efficiency of the antiseptic and the permanence of the antiseptic in the carrier resin can be enhanced. The material has higher antibiosis efficiency and biological safety, better processing performance, smooth surface, excellent mechanical properties, and nontoxicity and innocuousness.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a permanent antibacterial, mildewproof, nontoxic and harmless polyester material and a preparation method thereof. Background technique [0002] With the continuous improvement of the economy and living standards, people will pay more and more attention to their own health. Many articles in daily life contain a large number of microorganisms, and various pathogenic microorganisms that are contaminated or bred on the products we come into contact with every day are threatening our health all the time and hiding unexpected hazards. According to the statistics of the World Health Organization (WHO) in 1998, the annual death toll in the world is about 52 million, of which the number of deaths caused by microorganism-related diseases accounts for about 33%. In 1996, a food poisoning incident of native Escherichia coli O-157 occurred in Japan, which caused panic all over...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L83/04C08K13/04C08K7/26C08K3/22C08K5/134C08K5/526C08K5/3475C08K3/38
CPCC08L67/02C08K2003/2241C08K2003/387C08K2201/014C08L2203/12C08L2203/20C08L83/04C08K13/04C08K7/26C08K3/22C08K5/1345C08K5/526C08K5/3475C08K3/38
Inventor 汪品洋
Owner DONGGUAN JISU PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com