Preparation method of absorbable biological film
A biofilm and copolymer technology, applied in the medical and health field, can solve problems such as difficult organ repair, life-threatening, bleeding, etc., and achieve good biocompatibility, optimized mechanical properties, and simple operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] The absorbable biofilm of this embodiment includes the following raw materials in parts by weight: 50 parts by weight of polylactide, 100 parts by weight of gelatin, 120 parts by weight of polylactic acid-glycolic acid copolymer, and 30 parts by weight of aloin. The thickness of the absorbable biofilm is 2mm.
[0023] Its preparation method is as follows:
[0024] (1) Take the polylactide, gelatin, polylactic acid-glycolic acid copolymer, and aloin in parts by weight, add to water, heat the mixed solution to 60°C, add plasticizer glycerin, stir evenly, and Spinning solution was obtained after degassing for 0.5h in the environment of -0.05Mpa;
[0025] (2) Put the spinning solution described in step (1) into an electrospinning device with a temperature of 60°C, use hot air as the medium, and the air velocity is 0.5m / min, and adjust the feeding rate of the solution to 100ul / min, the distance between the spinneret and the collector is 10cm, under the voltage of 20kv, th...
Embodiment 2
[0027] The absorbable biofilm of this embodiment includes the following raw materials in parts by weight: 100 parts by weight of polylactide, 65 parts by weight of gelatin, 100 parts by weight of polylactic acid-glycolic acid copolymer, and 80 parts by weight of aloin. The thickness of the absorbable biofilm is 5mm.
[0028] Its preparation method is as follows:
[0029] (1) Take the polylactide, gelatin, polylactic acid-glycolic acid copolymer, and aloin in parts by weight, add to water, heat the mixed solution to 80°C, add plasticizer glycerin, stir evenly, and Spinning solution was obtained after degassing in the environment of -0.1Mpa for 2 hours;
[0030] (2) Put the spinning solution described in step (1) into an electrospinning device with a temperature of 60°C, use hot air as the medium, and the air velocity is 1.5m / min, and adjust the feeding rate of the solution to 50ul / min, the distance between the spinneret and the collector is 20cm, under the voltage of 25kv, t...
Embodiment 3
[0032] The absorbable biofilm of this embodiment includes the following raw materials in parts by weight: 75 parts by weight of polylactide, 30 parts by weight of gelatin, 150 parts by weight of polylactic acid-glycolic acid copolymer, and 55 parts by weight of aloin. The thickness of the absorbable biofilm is 0.8mm.
[0033] Its preparation method is as follows:
[0034] (1) Take the polylactide, gelatin, polylactic acid-glycolic acid copolymer, and aloin in parts by weight, add to water, heat the mixed solution to 60°C, add plasticizer glycerin, stir evenly, and Spinning solution was obtained after degassing in the environment of -0.1Mpa for 2 hours;
[0035] (2) Put the spinning solution described in step (1) into an electrospinning device with a temperature of 50°C, use hot air as the medium, and the air velocity is 0.5m / min, and adjust the feeding rate of the solution to 50ul / min, the distance between the spinneret and the collector is 20cm, under the voltage of 25kv, ...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap