Baking-free brick adopting waste as raw material and preparation method of baking-free brick
A technology of waste and non-burning bricks, which is applied in the field of non-burning bricks, can solve environmental pollution and other problems, and achieve good benefits, reduce production costs, and low costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] This embodiment relates to a burn-free brick using waste as raw material, including the following raw materials in parts by weight: 10 parts of waste plastic film, 8 parts of waste bagasse, 7 parts of aquatic product waste, 6 parts of steel slag sand, 15 parts of cement, 10 parts of modified fly ash, 11 parts of ceramic sand, 9 parts of attapulgite, 6 parts of yellow sand, 3 parts of sodium hexametaphosphate, 2 parts of activator, and 1 part of curing agent.
[0032] Wherein, described modified fly ash adopts following method to make:
[0033] (1) First dry the fly ash in an oven at 100°C;
[0034] (2) Then put the dried fly ash into a high-speed kneader, add 3% aluminate coupling agent equivalent to the weight of fly ash, 2% sodium lignosulfonate, 2% tricitric acid Ethyl ester, 1% liquid paraffin and 2% talcum powder are mixed at high speed, dried, crushed and ground into superfine powder.
[0035] Wherein, the aquatic product waste refers to shells of aquatic produc...
Embodiment 2
[0048] This embodiment relates to a non-burning brick with waste as raw material, including the following raw materials in parts by weight: 15 parts of waste plastic film, 13 parts of waste bagasse, 12 parts of aquatic product waste, 14 parts of steel slag sand, 25 parts of cement, 30 parts of modified fly ash, 18 parts of ceramic sand, 15 parts of attapulgite, 13 parts of yellow sand, 6 parts of sodium hexametaphosphate, 4 parts of activator, and 3 parts of curing agent.
[0049] Wherein, described modified fly ash adopts following method to make:
[0050] (1) First dry the fly ash in an oven at 110°C;
[0051](2) Then put the dried fly ash into a high-speed kneader, add 5% aluminate coupling agent equivalent to the weight of fly ash, 4% sodium lignosulfonate, 4% tricitric acid Ethyl ester, 2% liquid paraffin and 5% talcum powder are mixed at high speed, dried, crushed and ground into superfine powder.
[0052] Wherein, the aquatic product waste refers to shells of aquatic ...
Embodiment 3
[0065] This embodiment relates to a burn-free brick using waste as raw material, including the following raw materials in parts by weight: 12 parts of waste plastic film, 10 parts of waste bagasse, 9 parts of aquatic product waste, 8 parts of steel slag sand, 18 parts of cement, 20 parts of modified fly ash, 15 parts of ceramic sand, 10 parts of attapulgite, 7 parts of yellow sand, 4 parts of sodium hexametaphosphate, 2.5 parts of activator, and 1.8 parts of curing agent.
[0066] Wherein, described modified fly ash adopts following method to make:
[0067] (1) First dry the fly ash in an oven at 102°C;
[0068] (2) Then put the dried fly ash into a high-speed kneader, add 3.5% aluminate coupling agent equivalent to the weight of fly ash, 2.5% sodium lignosulfonate, 2.5% tricitric acid Ethyl ester, 1.2% liquid paraffin and 3% talcum powder are mixed at high speed, dried, crushed and ground into superfine powder.
[0069] Wherein, the aquatic product waste refers to shells of...