Luminous material which can be excited by ultraviolet light and near ultraviolet light to emit green light and preparation method and application thereof

A luminescent material, near-ultraviolet technology, applied in the field of fluorescent materials, can solve the problems of scarcity of green luminescent materials, low color rendering index of devices, lack of red light components, etc., achieve wide excitation spectrum range, low reaction temperature, simple and feasible method Effect

Active Publication Date: 2018-09-07
DONGGUAN UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the first way, due to the lack of red light components, the color rendering index of the device is low
[0004] In order to overcome the above defects, the three primary color phosphors excited by near-ultraviolet have shown certain competitiveness in the market, while the green light-emitting materials on the existing market are relatively scarce, and the existing ultraviolet or near-ultraviolet excited green light The material mainly uses energy transfer to excite Tb 3+ Ions produce narrowband emission, this green light not only excites the spectral range, but also causes energy loss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Luminous material which can be excited by ultraviolet light and near ultraviolet light to emit green light and preparation method and application thereof
  • Luminous material which can be excited by ultraviolet light and near ultraviolet light to emit green light and preparation method and application thereof
  • Luminous material which can be excited by ultraviolet light and near ultraviolet light to emit green light and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Potassium carbonate, barium carbonate, europium trioxide, and silicon dioxide were selected as starting materials, and the molar ratio of each element K:Ba:Eu:Si =2:2.97:0.03:8, corresponding to x=0.03, were weighed Four kinds of raw materials, the total weight of the control raw material mixture is 20 grams. Carry out thorough grinding and mixing, put it into a nitrogen-hydrogen mixed reducing atmosphere high-temperature furnace, bake at 950 ° C for 4 hours, take it out when it is cooled to room temperature, and after grinding and dispersing, a green luminescent material suitable for ultraviolet and near-ultraviolet excitation is obtained. Composed of K 2 Ba 2.97 Eu0.03 Si 8 o 20 .

[0034] figure 1 The XRD figure that is suitable for ultraviolet and near ultraviolet excitation green luminescent material that the embodiment 1 of the present invention obtains, as can be seen from the figure, spectrum and K 2 Ba 3 Si 8 o 20 Consistent with each other, it proves ...

Embodiment 2

[0036] Select lithium carbonate, barium carbonate, europium trioxide, and silicon dioxide as starting materials, and weigh them respectively according to the molar ratio of each element Li:Ba:Eu:Si =2:2.999:0.001:8, corresponding to x=0.001 Four kinds of raw materials, the total weight of the control raw material mixture is 20 grams. Carry out thorough grinding and mixing, put it into a nitrogen-hydrogen mixed reducing atmosphere high-temperature furnace, bake at 850 ° C for 10 hours, take it out when it is cooled to room temperature, and after grinding and dispersing, a green luminescent material suitable for ultraviolet and near-ultraviolet excitation is obtained. Composed of Li 2 Ba 2.999 Eu 0.001 Si 8 o 20 . The fluorescent spectral properties of the green luminescent material are similar to those in Example 1.

Embodiment 3

[0038] Select sodium carbonate, barium carbonate, europium trioxide, and silicon dioxide as starting materials, and weigh them respectively according to the molar ratio of each element Na:Ba:Eu:Si =2:2:1:8, corresponding to x=1 Four kinds of raw materials, the total weight of the control raw material mixture is 20 grams. Carry out thorough grinding and mixing, put it into a nitrogen-hydrogen mixed reducing atmosphere high-temperature furnace, bake at 1150 ° C for 1 hour, take it out when it is cooled to room temperature, and after grinding and dispersing, a green luminescent material suitable for ultraviolet and near-ultraviolet excitation is obtained. Composed of Na 2 Ba 2 EuSi 8 o 20 . The fluorescent spectral properties of the green luminescent material are similar to those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a luminous material which can be excited by ultraviolet light and near ultraviolet light to emit green light and a preparation method and application thereof. A chemical formula of the luminous material is A2B3-xEuxSi8O20, wherein A+ refers to one or two of alkaline metal ions Li+, Na+ and K+ according to the formula, B refers to one or two of alkaline-earth metal Ca and Sr or Ba, and x is greater than or equal to 0.005 and smaller than or equal to 1. When the provided luminous material capable of emitting the green light is excited by ultraviolet light or near ultraviolet light and other laser light sources, the green light the wavelength of which ranges from 450 to 580 nm (the peak value is 502 nm) can be emitted, the excited spectrum range is wide, a strong absorption effect is achieved within the range from 300 nm to 420 nm, and the luminous material is perfectly matched with an ultraviolet chip and a near ultraviolet chip. The preparation method of the provided luminous material is mild in condition, low in reaction temperature, simple, feasible, easy to operate, free of pollution and low in cost, and mass production is easily achieved.

Description

technical field [0001] The invention belongs to the field of fluorescent materials, and in particular relates to a luminescent material capable of being excited by ultraviolet and near ultraviolet to emit green light, a preparation method and application thereof. Background technique [0002] White LED (Light Emitting Diode) has many advantages such as non-toxic, long life (100,000 hours), high efficiency and energy saving, all solid state, low working voltage, shock resistance and good safety, and can be widely used in various lighting facilities. Including indoor lights, traffic lights, street lights, automobile tail lights, direction lights, brake lights, outdoor super-large screens, display screens and advertising boards, etc., is an environmentally friendly, energy-saving green lighting source, is generally considered to be 21 A new light source that replaces traditional lighting devices in the century. However, the efficiency of the developed white LED green luminesce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K11/59H01L33/50
CPCC09K11/7734H01L33/504
Inventor 康晓娇吕伟凌东雄
Owner DONGGUAN UNIV OF TECH