Autoclaved aerated concrete plate and molding process thereof

An autoclaved aerated concrete technology, applied in the field of building materials, can solve the problems of rough surface of autoclaved aerated concrete slabs, affecting the aesthetics of partition boards, etc., and achieve the effects of superior stability, wide usability, and thermal insulation surface.

Inactive Publication Date: 2018-09-28
南京兴陶预制品有限责任公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above-mentioned autoclaved aerated concrete slab is made of granite waste, and most of t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0045] Example one:

[0046] A preparation method of powder filler includes the following steps:

[0047] (1) Ingredients: weigh 70g of power generator ash cleaning, 5g of activated alumina, 20g of cement clinker powder, 10g of fluorspar powder and 0.3g of sodium dipolyphosphate;

[0048] (2) Drying: Dry the ash of 70g generator furnace at a high temperature of 600℃ for 1h;

[0049] (3) Calcination: 10g of fluorspar powder is calcined in a tubular heating furnace at low temperature, the temperature is 150℃, and the time is 2h;

[0050] (4) Mixing: Pour the dried 70g generator furnace ash into the mixing mixer, and add 5g activated alumina, 20g cement clinker powder, 10g fluorspar powder and 0.3g sodium dipolyphosphate in sequence for mixing Discharge after 30 minutes of stirring.

Example Embodiment

[0051] Embodiment two:

[0052] A preparation method of powder filler includes the following steps:

[0053] (1) Ingredients: weighing 75g of power generator ash cleaning, 5g of activated alumina, 23g of cement clinker powder, 10g of fluorspar powder and 0.3g of sodium tripolyphosphate;

[0054] (2) Drying: Dry the ash of 75g generator furnace at a high temperature of 600℃ for 1h;

[0055] (3) Calcination: 10g of fluorspar powder is calcined in a tubular heating furnace at low temperature, the temperature is 150℃, and the time is 2h;

[0056] (4) Mixing: Pour the dried 75g generator furnace ash into the mixing mixer, and add 5g activated alumina, 23g cement clinker powder, 10g fluorspar powder and 0.3g sodium tripolyphosphate in sequence for mixing Discharge after 30 minutes of stirring.

Example Embodiment

[0057] Example three:

[0058] A preparation method of powder filler includes the following steps:

[0059] (1) Ingredients: weigh 80g of power generator ash cleaning, 5g of activated alumina, 25g of cement clinker powder, 12g of fluorspar powder and 0.4g of sodium dipolyphosphate;

[0060] (2) Drying: Dry the ash of 80g generator furnace at a high temperature of 600℃ for 1h;

[0061] (3) Calcining: 12g of fluorspar powder is calcined in a tubular heating furnace at low temperature, the temperature is 150℃, and the time is 2h;

[0062] (4) Mixing: Put the dried 80g generator furnace dust into the mixing mixer, and add 5g activated alumina, 25g cement clinker powder, 12g fluorspar powder and 0.4g sodium dipolyphosphate in sequence, and mix Discharge after 30 minutes of stirring.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an autoclaved aerated concrete plate and a molding process thereof which are applied to the field of building materials and are used for solving the technical problem of use limitation caused by rough surface of a high-strength granite concrete plate in the prior art. The technical scheme has the key points that the autoclaved aerated concrete plate comprises the followingcomponents in parts by weight: 100-110 parts of cement, 125-140 parts of quick lime, 600-610 parts of coal ash, 6-10 parts of aerated aluminum paste, 200-230 parts of expanded perlites and 30-40 partsof powder filler. The expanded perlites and the powder filler are added into the cement, the quick lime, the coal ash and the aerated aluminum paste, and self-gaps of the expanded perlites and gaps between the adjacent expanded perlites can be filled with the powder filler, so that the autoclaved aerated concrete plate which is uniform in texture and smooth in surface can be favorably prepared, and the use range of the plate is remarkably widened.

Description

technical field [0001] The invention relates to building materials, in particular to an autoclaved aerated concrete plate and its forming process. Background technique [0002] Autoclaved aerated concrete slab is a new type of lightweight porous new green environmental protection building material, which is made of cement, lime, silica sand, etc. , steel structure and other industrial and civil buildings, it has the advantages of light weight, high strength, high thermal insulation, good sound insulation, convenient construction, long-lasting fire resistance, and small freeze-thaw loss. Replacing traditional aerated concrete blocks and cement slag hollow walls with autoclaved aerated concrete slabs, in addition to greatly reducing engineering time, improving engineering installation quality, and reducing construction costs, it can also protect the environment, save energy, and improve wall quality. Surface quality, increase architectural aesthetics, improve indoor environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/02C04B38/02C04B40/02C04B22/16C04B111/40
CPCC04B28/02C04B38/02C04B40/0042C04B40/0245C04B2111/00017C04B2111/40C04B2201/20C04B2201/32C04B2201/50C04B22/064C04B18/08C04B22/04C04B14/185C04B18/10C04B22/06C04B14/02C04B22/16C04B7/00
Inventor 尹晓海
Owner 南京兴陶预制品有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap