Insert injection moulding decoration transfer printing foil with anti-yellowing performance

A technology of insert injection molding and transfer foil, applied in the directions of printing, copying/marking method, coating, etc., can solve the problem that the INS film cannot meet the reliability test requirements, etc., and achieve the effect of improving the anti-yellowing performance

Inactive Publication Date: 2018-09-28
KURZ STAMPING TECH HEFEI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the application performance is excellent, the existing INS film cannot meet the increasingly stringent reliability test requirements, especially the requirement of not yellowing under specific temperature rise requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The color layer is made of the following components by weight:

[0019] 10 parts of low-density polyethylene;

[0020] 10 parts of high-density polyethylene;

[0021] 1 part polyurethane acrylate;

[0022] 1 part epoxy acrylate;

[0023] 1 part of trimethylolpropane triacrylate;

[0024] 8 parts of methyl methacrylate;

[0025] 20 parts of n-butyl methacrylate;

[0026] Polyethylene wax powder 1 part;

[0027] 10 parts polyamide;

[0028] 10 parts of diluent;

[0029] 10 parts of titanium dioxide;

[0030] Dispersant 0.1 part;

[0031] 1 part of anti-corrosion pigment;

[0032] 5 parts of toughening aid;

[0033] 3 parts of anti-yellowing additive;

[0034] The molecular weight of the methyl methacrylate is lower than 90,000, which can provide sufficient bonding force between the release layer and the aluminum plating layer, and at the same time ensure the definition of the transferred fine lines.

[0035] The toughening aid is ethylene methyl acrylate copo...

Embodiment 2

[0039] The color layer is made of the following components by weight:

[0040] 25 parts of low-density polyethylene;

[0041] 20 parts of high-density polyethylene;

[0042] 10 parts of polyurethane acrylate;

[0043] 5 parts of epoxy acrylate;

[0044] 10 parts of trimethylolpropane triacrylate;

[0045] 12 parts of methyl methacrylate;

[0046] 60 parts of n-butyl methacrylate;

[0047] 10 parts of polyethylene wax powder;

[0048] 20 parts of polyamide;

[0049] 25 parts of diluent;

[0050] 20 parts of titanium dioxide;

[0051] 2 parts of dispersant;

[0052] 30 parts of anti-corrosion pigment;

[0053] 10 parts of toughening aid;

[0054] 8 parts of anti-yellowing additive;

[0055] The molecular weight of the methyl methacrylate is lower than 90,000, which can provide sufficient bonding force between the release layer and the aluminum plating layer, and at the same time ensure the definition of the transferred fine lines.

[0056] The toughening aid is ethy...

Embodiment 3

[0060] The color layer is made of the following components by weight:

[0061] 10 parts of low-density polyethylene;

[0062] 10 parts of high-density polyethylene;

[0063] 1 part polyurethane acrylate;

[0064] 1 part epoxy acrylate;

[0065] 1 part of trimethylolpropane triacrylate;

[0066] 8 parts of methyl methacrylate;

[0067] 20 parts of n-butyl methacrylate;

[0068] Polyethylene wax powder 1 part;

[0069] 10 parts polyamide;

[0070] 10 parts of diluent;

[0071] 10 parts of titanium dioxide;

[0072] Dispersant 0.1 part;

[0073] 1 part of anti-corrosion pigment;

[0074] 5 parts of toughening aid;

[0075] 3 parts of anti-yellowing additive;

[0076] The molecular weight of the methyl methacrylate is lower than 90,000, which can provide sufficient bonding force between the release layer and the aluminum plating layer, and at the same time ensure the definition of the transferred fine lines.

[0077] The toughening aid is ethylene butyl acrylate copol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention provides an insert injection moulding decoration transfer printing foil with anti-yellowing performance. The insert injection moulding decoration transfer printing foil with anti-yellowing performance comprises a base film layer, a release layer, a color layer, an aluminium coated layer, and an adhesive layer which are laminated successively; the color layer is prepared from, by weight, 10 to 25 parts of low density polyethylene, 10 to 20 parts of high density polyethylene, 1 to 10 parts of polyurethane acrylate, 1 to 5 parts of epoxy acrylate, 1 to 10 parts of trimethylolpropanetriacrylate, 8 to 12 parts of methyl methacrylate, 20 to 60 parts of n-butyl methacrylate, 1 to 10 parts of polyethylene wax powder, 10 to 20 parts of polyamide, 10 to 25 parts of a diluent, 10 to 20parts of titanium dioxide, 0.1 to 2 parts of a dispersant, 1 to 30 parts of an anti-corrosive pigment, 5 to 10 parts of a toughening auxiliary agent, and 3 to 8 parts of an anti-yellowing auxiliary agent. According to a preparation method, acrylic resins of different amounts and different kinds are adopted so as to obtain the novel color layer; the toughening auxiliary agent and the anti-yellowing auxiliary agent are added, so that yellowing is avoided under certain heating requirements, and the anti-yellowing performance is improved greatly.

Description

technical field [0001] The invention relates to the technical field of transfer film, in particular to an insert injection molding decorative transfer foil with anti-yellowing performance. Background technique [0002] Insert molding decoration (INS) is still widely used in the automotive industry, although it is not as efficient as in-mold decoration (IMD). Insert injection molding decoration transfer technology is mainly used on injection molded parts with complex surface structures that cannot be applied by ordinary in-mold injection molding decoration technology. Thanks to this technology, surface decoration of many parts with complex surface structures becomes possible. [0003] Insert molding decorative transfer film (INS) with classic formula is widely used in the automotive industry all over the world. The unique flexibility enables the INS film to be applied to almost all surfaces with complex structures. Although the application performance is excellent, the ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/06C09D177/00C09D175/14C09D163/10C09D7/61B41M5/382
CPCB41M5/38214C08K2003/2241C08L2205/025C08L2205/035C08L2207/062C08L2207/066C09D7/61C09D123/06C09D177/00C08L23/06C08L75/14C08L63/10C08L77/00C08K13/02C08K3/22
Inventor 不公告发明人
Owner KURZ STAMPING TECH HEFEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com