Puncture resistant high-barrier plastic composite film and packaging bag
A composite film, puncture-resistant technology, applied in high-barrier plastic composite film and packaging bags, puncture-resistant field, can solve the problem of puncture resistance, poor impact resistance, weak barrier performance, easy penetration, bag breakage, tearing and other problems, to achieve the effect of strong barrier performance and strong impact resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0040] Example 1
[0041] A reinforced puncture-resistant polyethylene, which uses the following raw materials through melt blending, extrusion and film blowing:
[0042]
[0043]
[0044] Among them, linear polyethylene is a conventional component; low-density polyethylene plays a role in regulating the heat-sealing temperature; metallocene polyethylene enhances firmness; elastomers improve puncture resistance and flexibility. The film has good heat-sealability with the help of polyethylene, and the special composition makes up for the lack of puncture resistance and serves as an inner layer. The elastomer uses any one or more of a styrene-based thermoplastic elastomer, a polyurethane-based thermoplastic elastomer, a polyolefin-based thermoplastic elastomer, and a polyamide-based thermoplastic elastomer. The low density polyethylene has a density of 0.910-0.925g / cm 3 , The density of the linear low-density polyethylene is 0.918~0.935g / cm3, and the density of the metallocene polye...
Example Embodiment
[0050] Example 2
[0051] A puncture-resistant, high-barrier plastic composite film, comprising a multi-layer film, the multi-layer film is a penetration-resistant layer, a stretched layer, a barrier layer, and a printing layer;
[0052] The puncture-resistant layer adopts the reinforced puncture-resistant polyethylene according to claim 1;
[0053] The stretching layer adopts a biaxially oriented nylon film; the biaxially oriented nylon (polyamide, NY) is strong and has good puncture resistance. Although the material has no heat sealability, it cannot be used as an inner layer, but it is compatible with reinforced Puncture PE compound, complementary advantages, further enhance puncture resistance.
[0054] The barrier layer adopts aluminum foil; the aluminum foil has high light and heat reflectance, heat insulation, moisture resistance, opacity, and can effectively block ultraviolet rays, greatly improving its barrier performance and oxidation resistance.
[0055] The printing layer i...
Example Embodiment
[0059] Example 3
[0060] A composite packaging bag is made of the puncture-resistant, high-barrier plastic composite packaging bag film described in Example 2. When making bags, the hot knife temperature of the bag making machine is 112 degrees, and the bag making speed is 40 lines / min.
[0061] In order to ensure that the puncture resistance and high barrier properties meet the standards, the relevant inspection standards for materials, semi-finished products and finished products are as follows:
[0062] 1. PET, NY, PE, AL corona test, the corona value should be 42, 42, and 38 dyne in order. Good corona treatment can ensure the quality of printing and composite.
[0063] 2. The tensile test of PET, NY, PE should be greater than 40 Newtons;
[0064] 3. The friction coefficient test of PET, NY, PE, 025-0.4, 0.1-0.28 respectively;
[0065] 4. NY and PE anti-pendulum puncture strength test should be greater than 0.8 Newton;
[0066] 5. Peel strength test after compounding, the three layer...
PUM
Property | Measurement | Unit |
---|---|---|
Density | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap