Ferrochrome slag glass ceramics and preparing method thereof

A technology for glass-ceramic and ferrochromium slag, which is applied in the field of ferrochromium slag glass-ceramic and its preparation, can solve problems such as environmental pollution and safety of ferrochromium tailings, and achieve excellent mechanical properties, reduced melting temperature, and good wear resistance. Effect

Inactive Publication Date: 2018-10-12
HEFEI LIYUTAI GLASS PROD CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a ferrochrome slag glass-ceramic and a preparation method thereof. The prepared glass-ceramic has good wear resistance, corrosion resistance and impact resistance, and solves the environmental problems of the existing ferrochrome tailings. Pollution, safety and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]The ferrochrome slag glass-ceramics of this embodiment, in terms of mass percentage, is composed of: 88% ferrochrome slag, 6.5wt% flux, 4.4wt% clarifier, and 1.1wt% KOH.

[0035] Wherein, the co-solvent is fluorite, boron oxide, dolomite and barite, and the weight ratio among them is 15:8:3:1.

[0036] Wherein, the clarifying agent is sodium nitrate, sodium carbonate or antimony oxide.

[0037] The present invention also provides a preparation method for the above-mentioned ferrochrome slag glass-ceramics, comprising the following steps:

[0038] (1) Pulverize the required amount of ferrochrome slag, flux and clarifying agent, put the sieved ferrochrome slag, flux and clarifying agent into the mixer and mix thoroughly to obtain the basic batch of glass-ceramics;

[0039] (2) Preheat the mixed glass-ceramic basic batch at 650°C for 30 minutes, put it into a high-temperature furnace for melting, the melting temperature is 1300°C, keep it warm for 40 minutes, then add KOH,...

Embodiment 2

[0047] The ferrochrome slag glass-ceramic of this embodiment, in terms of mass percentage, is composed of: 90wt% ferrochrome slag, 5.5wt% flux, 3.3wt% clarifier, and 1.2wt% KOH.

[0048] Wherein, the co-solvent is fluorite, boron oxide, dolomite and barite, and the weight ratio among them is 15:8:3:1.

[0049] Wherein, the clarifying agent is sodium nitrate, sodium carbonate or antimony oxide.

[0050] The present invention also provides a preparation method for the above-mentioned ferrochrome slag glass-ceramics, comprising the following steps:

[0051] (1) Pulverize the required amount of ferrochrome slag, flux and clarifying agent, put the sieved ferrochrome slag, flux and clarifying agent into the mixer and mix thoroughly to obtain the basic batch of glass-ceramics;

[0052] (2) Preheat the mixed glass-ceramic basic batch at 650°C for 40 minutes, put it into a high-temperature furnace for melting, the melting temperature is 1400°C, keep it warm for 60 minutes, then add KO...

Embodiment 3

[0060] The ferrochrome slag glass-ceramics of this embodiment is composed of, by mass percentage, 90 wt% of ferrochrome slag, 6 wt% of flux, 3 wt% of clarifying agent, and 1 wt% of KOH.

[0061] Wherein, the co-solvent is fluorite, boron oxide, dolomite and barite, and the weight ratio among them is 15:8:3:1.

[0062] Wherein, the clarifying agent is sodium nitrate, sodium carbonate or antimony oxide.

[0063] The present invention also provides a preparation method for the above-mentioned ferrochrome slag glass-ceramics, comprising the following steps:

[0064] (1) Pulverize the required amount of ferrochrome slag, flux and clarifying agent, put the sieved ferrochrome slag, flux and clarifying agent into the mixer and mix thoroughly to obtain the basic batch of glass-ceramics;

[0065] (2) Preheat the mixed glass-ceramic basic batch at 650°C for 35 minutes, put it into a high-temperature furnace for melting, the melting temperature is 1350°C, keep it warm for 50 minutes, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses ferrochrome slag glass ceramics,and further provides a preparing method of the ferrochrome slag glass ceramics. The ferrochrome slag glass ceramics are prepared from,by mass,88-92% of ferrochrome slag,5-7% of fluxing agent,2.2-4.4% of clarifying agent and 0.5-1.5% of KOH. The preparing method of the ferrochrome slag glass ceramics comprises the following steps of mixing,heating and melting,moulding by casting,annealing,crystallization treatment and the like. The prepared ferrochrome slag glass ceramics have good abrasive resistance,erosion resistance and impact resistance performance,and the problems of environmental pollution,safety and the like of existing ferrochrome tailings are solved.

Description

technical field [0001] The invention relates to the technical field of glass-ceramic materials, in particular to a ferrochrome slag glass-ceramic and a preparation method thereof. Background technique [0002] Microcrystalline glass, also known as microcrystalline jade or ceramic glass, is a comprehensive glass and a new type of building material newly developed by foreign countries. Its scientific name is glass crystal. Glass-ceramic looks very different from our usual glass. It has the dual characteristics of glass and ceramics. The atomic arrangement inside ordinary glass is irregular, which is one of the reasons why glass is fragile. Glass-ceramic, like ceramics, is composed of crystals, that is to say, its atomic arrangement There are rules. Therefore, glass-ceramic is brighter than ceramics and tougher than glass, and its composition includes silicate. [0003] Tailings are one of the products of sorting operations in mineral processing. Among the products of this o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/06C03C1/00C03B19/02C03B25/00
CPCC03C10/0063C03B19/02C03B25/00C03C1/004
Inventor 武娟
Owner HEFEI LIYUTAI GLASS PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap