Waterborne industrial rustproof color paste and preparation method thereof

An industrial, water-based technology, applied in the direction of anti-corrosion coatings, fire-resistant coatings, pigment paste, etc., can solve the problems of not meeting engineering needs, polluting the environment, labor costs, and high labor intensity, achieving excellent anti-rust functions, reducing environmental pressure, easy-to-operate effect

Pending Publication Date: 2018-10-12
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Large-scale steel installations and facilities, such as oil storage tanks, iron frames, iron bridges, sluice gates, ships, etc., can only be derusted by hand, which is not only labor-intensive and inefficient, but also difficult to remove rust;
[0005] Small and medium-sized steel parts can be derusted by shot blasting. Although the derust...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne industrial rustproof color paste and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0053] The invention also discloses a preparation method of an antirust color paste for water-based industrial coatings, the specific steps are as follows:

[0054] Step 1: Add the stabilizer to deionized water, stir and mix to make a pre-solution;

[0055] Step 2: Add dispersant, humectant, bactericide, acidic complexing agent, conversion agent, and defoamer into the pre-solution, and stir evenly;

[0056] Step 3: Add nano-TiO 2 and carbon black powder, stir;

[0057] Step 4: Add the above-mentioned mixed slurry components into a grinder and grind until a uniform slurry with good fluidity is formed;

[0058] Step 5: adding an appropriate amount of pH regulator to adjust the pH value of the slurry to prepare the antirust color paste for water-based industrial coatings of the present invention.

[0059] In order to further realize the technical effect of the present invention, the stirring time of step 2 is 10-20 minutes, and the stirring time of step 3 is 60-90 minutes.

...

Embodiment 1

[0064] An anti-rust color paste for water-based industrial coatings, which is made of the following raw material ratios: 65% of pigments, 5% of wetting and dispersing agents, 0.3% of pH regulators, 10% of humectants, 0.1% of stabilizers, and 0.3% of defoaming agents %, acidic complexing agent 2%, bactericide 0.3%, deionized water 17%, stabilizer is graphene oxide, dispersant is high molecular weight alkyl ammonium salt copolymer, defoamer is polysiloxane-polyether Copolymer emulsion type defoamer, bactericide is methylisothiazolinone, acidic complexing agent is ethylenediaminetetraacetic acid, pH regulator is 2-amino-2-methyl-1-propanol.

Embodiment 2

[0066] An anti-rust color paste for water-based industrial coatings, which is made of the following raw material ratios: 45% of pigments, 7% of wetting and dispersing agents, 0.2% of pH regulators, 8% of humectants, 0.1% of stabilizers, and 0.5% of defoamers %, acidic complexing agent 1%, bactericide 0.2%, deionized water 38%, stabilizer is graphene oxide, dispersant is high molecular weight alkyl ammonium salt copolymer, defoamer is polysiloxane-polyether Copolymer emulsion type defoamer, bactericide is methylisothiazolinone, acidic complexing agent is ethylenediaminetetraacetic acid, pH regulator is 2-amino-2-methyl-1-propanol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a waterborne industrial rustproof color paste and a preparation method thereof, wherein the rustproof color paste comprises the following raw material components in parts by mass: 45-65% of pigment, 4-7% of wetting dispersant, 5-10% of humectant, 0.05-0.1% of stabilizer, 0.01-0.5% of defoaming agent, 1-2% of acidic complexing agent, 0.05-0.3% of bactericide, 0.2-0.3% of PHregulator and 10-40% of deionized water. The rustproof color paste prepared by using the preparation method is not only suitable for rustproofness of a steel surface with a rusted and hard oxide scale layer or an old paint film, but also suitable for rustproofness of a stainless steel surface if being added into a waterborne industrial coating. In addition, the rustproof color paste prepared by using the preparation method is also environment-friendly when being used and further has good compatibility with various common waterborne industrial coatings such as an alkyd primer and an epoxy ester primer as well as water-soluble resin.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based industrial anti-rust color paste and a preparation method thereof. Background technique [0002] Steel structure engineering is a structure mainly made of steel, which is one of the main types of modern industrial and architectural structures, but its easy to corrode characteristics have brought huge losses to the national economy. [0003] In order to protect steel from rust, a layer of paint is often applied to its surface. In the past, before using paint, the base material must be thoroughly derusted, and even the original color of the metal base must be exposed; [0004] Large-scale steel installations and facilities, such as oil storage tanks, iron frames, iron bridges, sluice gates, ships, etc., can only be derusted by hand, which is not only labor-intensive and inefficient, but also difficult to remove rust; [0005] Small and medium-sized steel parts can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D17/00C09D5/08C09D5/18
CPCC09D17/001C09D5/08C09D5/18
Inventor 宋雪丽薛小倩刘洪亮杨从友温宇行
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap