Self-support homogeneous forward osmosis membrane capable of eliminating internal concentration polarization, preparation method therefor and application of self-support homogeneous forward osmosis membrane

A forward osmosis membrane, self-supporting technology, applied in chemical instruments and methods, semi-permeable membrane separation, membrane, etc., can solve problems such as difficult cleaning, membrane fouling, internal concentration polarization, etc., and achieve easy cleaning, antifouling and antibacterial Strong performance and good stability

Active Publication Date: 2018-10-16
NANJING UNIV OF SCI & TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems of internal concentration polarization, membrane fouling, difficult cleaning and high energy consumption of traditional asymmetric forward osmosis membrane (TFC), the purpose of the present invention is to provide a self-supporting homogeneous forward osmosis membrane, a preparation method and its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-support homogeneous forward osmosis membrane capable of eliminating internal concentration polarization, preparation method therefor and application of self-support homogeneous forward osmosis membrane
  • Self-support homogeneous forward osmosis membrane capable of eliminating internal concentration polarization, preparation method therefor and application of self-support homogeneous forward osmosis membrane
  • Self-support homogeneous forward osmosis membrane capable of eliminating internal concentration polarization, preparation method therefor and application of self-support homogeneous forward osmosis membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Preparation of copolymer (I)-1

[0043] Pour 4.0010g of dicarboxydiphenyl ether into an appropriate amount of polyphosphoric acid, stir at 100°C for 1 hour; add hydrazine sulfate (2.4188g) into the reaction system, the molar ratio of hydrazine sulfate to dicarboxydiphenyl ether monomer is 1.2:1, Raise the temperature to 160°C, and react at high temperature for 6 hours; pour the viscous solution into 5wt% NaOH solution to precipitate, wash until neutral, and dry in vacuum for later use to obtain 3.4376g of a brownish yellow solid with a yield of about 93.56%; from figure 1 According to NMR and IR spectra, the copolymer (I)-1 was successfully synthesized.

[0044]

Embodiment 2

[0046] Preparation of copolymer (I)-2

[0047] Pour 4.0031g of bis(4-carboxyphenyl)hexafluoropropane into an appropriate amount of polyphosphoric acid, stir at 100°C for 1h; add hydrazine sulfate (1.5908g g) into the reaction system, hydrazine sulfate and bis(4-carboxyphenyl) The molar ratio of hexafluoropropane monomer was 1.2:1, and the reaction was carried out at 160°C for 6 hours; the viscous solution was poured into 5wt% NaOH solution to precipitate, washed to neutrality, and vacuum-dried for later use to obtain 3.2576 g of a brownish-yellow solid with a yield of about 86.20%; from figure 1 According to NMR and IR spectra, the copolymer (I)-1 was successfully synthesized.

[0048]

[0049] Depend on figure 1 The nuclear magnetic pattern of can prove that copolymer (I) has been successfully synthesized.

Embodiment 3

[0051] Preparation of copolymer (II)-1

[0052] 0.6012g copolymer (I)-1 was dissolved in NMP, the system concentration was 5wt%, and a small amount of PPA was added to the reaction system; after the polymer was completely dissolved, it was cooled to room temperature, and then 0.3512g p-aminobenzoic acid was added, React at 195°C for 12 hours; after the reaction, slowly pour the solution cooled to room temperature into hot water, the product precipitates, wash with water to neutrality and then vacuum dry to obtain 0.6952g of copolymer (II)-1, the yield is about 70.90%. Wherein: during the reaction process, the molar ratio of the amino-containing monomer to the polymer A is controlled at 1:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-support homogeneous forward osmosis membrane capable of eliminating internal concentration polarization, a preparation method therefor and an application of the self-support homogeneous forward osmosis membrane. According to the self-support forward osmosis membrane, a polyoxadiazole structure serves as a skeleton and is modified with an amino-containing monomer so as to obtain a polytriazole / oxadiazole copolymer, and a nondefective self-support homogeneous membrane is prepared by using a solvent evaporation method and is applied to forward osmosis. According tothe self-support homogeneous forward osmosis membrane, the preparation method therefor and the application of the self-support homogeneous forward osmosis membrane, forward osmosis membranes of different properties are obtained through adjusting factors such as concentration, volume and membrane-forming temperature of a membrane casting solution, a proper draw solution is selected, and forward osmosis testing is completed; compared with commercial membranes, the membrane disclosed by the invention has the advantages that the material flux loss is low, the dye concentration time is obviously shortened, and the operating efficiency is remarkably increased; in addition, the self-support homogeneous forward osmosis membrane prepared by the method further has the advantages of relatively good stability, pollution resistance, easiness in cleaning and the like and can effectively achieve the requirements on forward osmosis.

Description

technical field [0001] The invention belongs to the technical field of forward osmosis membrane preparation, and relates to a self-supporting homogeneous forward osmosis membrane capable of eliminating internal concentration polarization, a preparation method and application thereof. Background technique [0002] In recent years, with the in-depth introduction of the concept of zero discharge, the recovery and reuse of useful substances in wastewater has been paid more and more attention. In modern industrial production, especially in the synthesis and application of dyes, the discharge of high-salinity dye wastewater has seriously endangered human health and the ecological environment, and has become the most challenging wastewater. High-salinity dye wastewater has high chroma and high salt content (>6% NaCl, >5% Na 2 SO 4 ), pH fluctuation (1-14) and high toxicity (refractory to biodegradation). The recycling of dyes and salts can not only significantly reduce the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D61/00B01D69/12B01D71/80C02F103/08C02F101/34C02F101/38
CPCB01D61/002B01D69/125B01D71/80C02F2101/38C02F2101/40C02F2101/34C02F2103/08B01D71/62B01D65/08B01D69/02B01D71/76C02F1/445B01D2325/48B01D65/02B01D2321/168B01D61/0024
Inventor 张轩李猛王连军
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products