Environment-friendly type EPDM (ethylene propylene diene monomer) adhesive for increasing adhesion force between EPDM rubber and curtain lines

A technology of EPDM rubber and adhesive, which is applied in the directions of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., to achieve the effect of simple bonding process, wide range of materials and high bonding strength

Active Publication Date: 2018-10-16
NANJING ORIENTLEADER TECH CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem of the environment and the health of practitioners brought about by the toxic and harmful adhesive used when EPDM rubber is bonded to the cord, and to provide an environmentally friendly EPDM adhesive that does not produce nitrosamines through the use of environmentally friendly adhesives. The formula of the adhesive is designed with cross-linking aids, and all highly toxic solvents are replaced by products without benzene solvents and low toxicity in the process of adhesive preparation, which meet the requirements of bonding technology and meet environmental protection requirements at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly type EPDM (ethylene propylene diene monomer) adhesive for increasing adhesion force between EPDM rubber and curtain lines

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Weigh the following parts by weight raw materials: 100 parts of EPDM rubber 4010M; additives: 5 parts of zinc oxide, 1 part of stearic acid StA, 5 parts of N330 carbon black, 20 parts of N550 carbon black, 10 parts of white carbon black; Mixture: 15 parts of binder RS, 10 parts of binder A; vulcanizing agent: 0.5 parts of sulfur; 10 parts of maleic anhydride-grafted EPDM rubber, wherein the maleic anhydride-grafted EPDM rubber has a grafted amount of maleic anhydride (MA) = 1.0 wt%.

[0043] The internal mixer is cooled with water, and the temperature of the working room of the internal mixer is controlled not to exceed 50°C. Mix EPDM rubber and maleic anhydride grafted EPDM rubber in the internal mixer for 1 minute, and then add zinc oxide in turn. , stearic acid StA, binder RS ​​and A to the internal mixer and knead for 3min, then add N330 carbon black, N550 carbon black, white carbon black and knead for 4min; finally, add sulfur and crosslinking additives and knead f...

Embodiment 2

[0046] Weigh the following parts by weight raw materials: 100 parts of EPDM rubber 4010M; additives: 5 parts of zinc oxide, 1 part of stearic acid StA, 5 parts of N330 carbon black, 20 parts of N550 carbon black, 10 parts of white carbon black, viscose Mixture: 15 parts of binder RS, 10 parts of binder A; vulcanizing agent: 0.5 parts of sulfur, 2 parts of cross-linking aid TBzTD, 1.5 parts of cross-linking aid DTDC, 1.0 parts of cross-linking aid ZBEC; 10 parts of acid anhydride grafted polybutadiene (MA=7.5wt%).

[0047] The internal mixer is cooled by water, and the temperature of the working room of the internal mixer is controlled not to exceed 50°C. Mix EPDM rubber and maleic anhydride grafted polybutadiene in the internal mixer for 0.5min, and then add zinc oxide in sequence , stearic acid StA, binder RS ​​and A to the internal mixer and knead for 3min, then add N330 carbon black, N550 carbon black, white carbon black and knead for 4min; finally, add sulfur and crosslink...

Embodiment 3

[0050] Weigh the following parts by weight raw materials: 100 parts of EPDM 4010M; additives: 5 parts of zinc oxide, 1 part of stearic acid StA, 25 parts of N550 carbon black, 10 parts of white carbon black; adhesive: adhesive 15 parts of RS, 10 parts of binder A; vulcanizing agent: 0.5 parts of sulfur, 2.0 parts of cross-linking auxiliary agent CBBS, 1.0 parts of cross-linking auxiliary agent DTDC, 2.0 parts of cross-linking auxiliary agent TBzTD; maleic anhydride grafted terpolymer 10 parts of propylene rubber (MA=1.0 wt%).

[0051] The internal mixer is cooled with water, and the temperature of the working room of the internal mixer is controlled not to exceed 50°C. Mix EPDM rubber and maleic anhydride grafted EPDM rubber in the internal mixer for 1 minute, and then add zinc oxide in turn. , stearic acid StA, binder RS ​​and A to the internal mixer and knead for 3 minutes, then add N550 carbon black and white carbon black and knead for 5 min; finally, add sulfur and cross-l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly type EPDM (ethylene propylene diene monomer) adhesive for increasing adhesion force between EPDM rubber and curtain lines. The environment-friendly typeEPDM adhesive is mainly prepared from an EPDM mixing glue and a hydrocarbon solvent oil according to a weight ratio of 1 to (2 to 8), wherein the EPDM mixing glue is mixed by the EPDM rubber, a vulcanizer, a crosslinking additive, an adhesive, zinc oxide, stearic acid, carbon black, white carbon black and maleic anhydride-grafted polymer. The environment-friendly type EPDM adhesive has the advantages that the adhesion force between the EPDM rubber and the polyester fiber, vinylon curtain lines as well as manmade yarns is effectively increased; the environment-friendly effect is realized, theproduction of toxic or harmful matters is avoided in the preparation and use process, and the injury to human bodies and environments is extremely low.

Description

technical field [0001] The invention relates to an adhesive formula, in particular to an environment-friendly EPDM adhesive for improving the bonding of EPDM rubber and cords. Background technique [0002] EPDM rubber has excellent aging resistance (including ozone resistance, heat resistance and weather resistance, etc.), good chemical resistance, electrical insulation, impact elasticity, low temperature performance, low density and high filling. And water vapor resistance and other properties, so it is widely used in automotive parts, waterproof materials for building materials, wire and cable sheaths, heat-resistant rubber hoses and other products. EPDM rubber is one of the fastest-growing rubber types in synthetic rubber. Its production capacity and output have been listed as the third among the seven synthetic rubber types, second only to styrene-butadiene rubber and butadiene rubber. However, the main chain molecules of EPDM rubber are in a saturated state, lacking ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/16C09J11/04C09J11/06C09J11/08
CPCC08K2003/2296C09J11/04C09J11/06C09J11/08C09J123/16C08L51/04C08L51/003C08K13/02C08K3/06C08K3/22C08K5/09C08K3/04C08K3/36
Inventor 陶平王亮燕符寿康康鑫任建民
Owner NANJING ORIENTLEADER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap