Sole with light transmitting function and preparation method of sole

A functional and transparent technology, applied in the direction of shoe soles, footwear, applications, etc., can solve the problems of poor softness and light transmission of shoe soles, achieve rich void structure, improve oxidation resistance and anti-yellowing properties, and easy production process The effect of the operation

Inactive Publication Date: 2018-10-19
谢冠华
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Through the comprehensive selection of formula and process, the patent can not only transmit light, but also meet the requirements of the sole in terms of elasticity, resistance to yellow edges, compression deformation and other physical parameters, but the softness and Poor light transmission

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of shoe sole with light-transmitting function and its preparation method

[0031] The raw materials for preparing the sole with light transmission function include: EVA210 30kg, EVA40W 5kg, OBC9100 14kg, EPDM rubber 2kg, polyurethane thermoplastic elastomer 8kg, zinc stearate 0.3kg, transparent zinc oxide 0.9kg, crosslinking agent 0.9 kg, transparent blowing agent 2.5kg, auxiliary agent 2kg.

[0032] The raw materials for preparing auxiliary agents include: palygorskite powder 10kg, diatomite 10kg, nonylphenol polyoxyethylene ether 0.2kg, methyl acrylate 0.6kg, dimethyl carbonate 0.8kg, dialkyl zinc dithiophosphate 0.3kg .

[0033] The preparation steps of auxiliary agent comprise:

[0034] Step i, weighing the raw materials for preparing auxiliary agents according to the above parts by weight;

[0035] Step ii, heat treating the above-mentioned palygorskite powder and diatomaceous earth at a temperature of 650° C. for 5 hours;

[0036] In step iii, mix the p...

Embodiment 2

[0043] A kind of shoe sole with light-transmitting function and its preparation method

[0044] The raw materials for preparing the sole with light transmission function include: EVA260 35kg, EVA40W 5kg, OBC9007 10kg, EPDM rubber 4kg, polyurethane thermoplastic elastomer 6kg, zinc stearate 0.7kg, transparent zinc oxide 0.4kg, crosslinking agent 0.3 kg, transparent blowing agent 1.2kg, auxiliary agent 8kg.

[0045] The raw materials for preparing auxiliary agents include: palygorskite powder 12kg, diatomite 6kg, nonylphenol polyoxyethylene ether 0.4kg, methyl acrylate 0.5kg, dimethyl carbonate 0.6kg, dialkyl zinc dithiophosphate 0.4kg .

[0046] The preparation steps of auxiliary agent comprise:

[0047] Step i, weighing the raw materials for preparing auxiliary agents according to the above parts by weight;

[0048] Step ii, heat treating the above-mentioned palygorskite powder and diatomaceous earth at a temperature of 660° C. for 4.5 hours;

[0049] In step iii, mix the pa...

Embodiment 3

[0056] A kind of shoe sole with light-transmitting function and its preparation method

[0057] The raw materials for preparing the sole with light transmission function include: EVA220 50kg, EVA40W 5kg, OBC9100 8kg, EPDM rubber 10kg, polyurethane thermoplastic elastomer 3kg, zinc stearate 0.9kg, transparent zinc oxide 0.2kg, crosslinking agent 0.1 kg, transparent blowing agent 4.5kg, auxiliary agent 4kg.

[0058] The raw materials for preparing auxiliary agents include: palygorskite powder 14kg, diatomite 8kg, nonylphenol polyoxyethylene ether 0.3kg, methyl acrylate 0.8kg, dimethyl carbonate 0.5kg, dialkyl zinc dithiophosphate 0.5kg .

[0059] The preparation steps of auxiliary agent comprise:

[0060] Step i, weighing the raw materials for preparing auxiliary agents according to the above parts by weight;

[0061] Step ii, heat treating the above-mentioned palygorskite powder and diatomaceous earth at a temperature of 670° C. for 4 hours;

[0062] In step iii, mix the pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sole with a light transmitting function and a preparation method of the sole. The sole with the light transmitting function is prepared from the following raw materials in parts by weight: 35 to 60 parts of EVA (Ethyl Vinyl Acetate), 8 to 16 parts of OBC, 2 to 10 parts of ethylene propylene diene monomer, 2 to 8 parts of thermoplastic polyurethane elastomer, 0.1 to 0.9 part of zinc stearate, 0.2 to 1.2 parts of transparent zinc oxide, 0.1 to 0.9 part of a cross-linking agent and 1.2 to 6.0 parts of a transparent foaming agent, wherein the OBC is selected from any oneof OBC 9100 and OBC 9007. The sole with the light transmitting function has the advantages of better light transmittance, high hardness and tensile strength, high rebound rate, good yellowing resistance and comfortableness in wearing; the used raw materials are easy to obtain; the preparation method is simple; the production process flow is easy to operate, so the preparation method is suitable for large-scale popularization.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a shoe sole with a light-transmitting function and a preparation method thereof. Background technique [0002] Ethylene-vinyl acetate copolymer (EVA) is a random copolymer of ethylene and vinyl acetate. Due to the introduction of short-chain branches formed by polar acetic acid groups in the ethylene chain, the original crystalline state has been changed. Compared with polyethylene, EVA becomes more flexible and elastic due to the introduction of vinyl acetate monomer in the molecular chain, and has good plasticity, elasticity and processability, and the foamed material has low density, With good mechanical properties and easy coloring, it is widely used in shoe sole materials. Although the luminous sole can increase the aesthetics and interest of the sole, the luminous layer of the sole is usually made of PU resin luminous powder or PU resin fluorescent ink. Resin lu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L23/16C08L75/04C08K13/04C08K7/26C08K5/098C08K3/22C08K3/34C08J9/10C08J9/08C08J9/32A43B13/04
CPCA43B13/04C08J9/0023C08J9/0061C08J9/0066C08J9/0095C08J9/08C08J9/105C08J9/32C08J2203/02C08J2203/04C08J2203/18C08J2203/20C08J2203/22C08J2323/08C08J2423/08C08J2423/16C08J2475/04
Inventor 谢冠华谢志东
Owner 谢冠华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap