Cathodic electrophoretic coating and preparation method thereof

A cathodic electrophoretic paint, pigment and filler technology, applied in the field of coatings, can solve the problems of high cost, poor appearance, poor acid and alkali resistance and other problems of cathodic electrophoretic paint, and achieve the effects of low cost, energy reduction and high oil resistance

Inactive Publication Date: 2018-11-02
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of high cost, poor appearance and poor acid and alkali resistance of existing cathodic electrophoretic paint, the invention provides a cathodic electrophoretic paint and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cathodic electrophoretic coating and preparation method thereof
  • Cathodic electrophoretic coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] An embodiment of the present invention provides a cathodic electrophoretic coating, which includes the following components in parts by weight: color paste: 10 parts, emulsion: 30 parts, deionized water: 50 parts;

[0042] The above-mentioned color paste includes the following components in parts by mass: modified resin: 18 parts, environmental protection co-solvent: 5 parts, neutralizer: 1 part, surfactant: 0.4 parts, deionized water: 30 parts, color Filler: 30 parts; Among them, the environmental protection co-solvent is isopropanol, the neutralizer is lactic acid, the surfactant is nonylphenol polyoxyethylene ether, the pigments and fillers include 22.6 parts of kaolin, and 7.4 parts of pigments. The pigments are based on MH- RC: a mixture of chrome yellow 7000: titanium dioxide with a mass ratio of 9:8:6;

[0043] The above-mentioned emulsion includes the following components in parts by mass: modified resin: 40 parts, emulsifier: 6 parts, neutralizer: 3 parts, deio...

Embodiment 2

[0054] An embodiment of the present invention provides a cathodic electrophoretic coating, which includes the following components in parts by weight: color paste: 10 parts, emulsion: 40 parts, deionized water: 40 parts;

[0055] The above-mentioned color paste includes the following components in parts by mass: modified resin: 30 parts, environmental protection co-solvent: 15 parts, neutralizer: 5 parts, surfactant: 0.5 parts, deionized water: 40 parts, color Filler: 30 parts, of which the environmentally friendly co-solvent is propylene glycol methyl ether, the neutralizer is sulfamic acid, the surfactant is PPG2000, the pigment and filler include 28 parts of kaolin, and 2 parts of pigment, of which the pigment is in accordance with MH-RC: chrome yellow 7000: a mixture of titanium dioxide with a mass ratio of 6:5:4;

[0056] The above-mentioned emulsion includes the following components in parts by mass: modified resin: 35 parts, emulsifier: 4 parts, neutralizer: 6 parts, de...

Embodiment 3

[0067] An embodiment of the present invention provides a cathodic electrophoretic coating, which includes the following components in parts by weight: color paste: 15 parts, emulsion: 60 parts, deionized water: 50 parts;

[0068] The above-mentioned color paste includes the following components in parts by mass: modified resin: 35 parts, environmental protection cosolvent: 13 parts, neutralizer: 6 parts, surfactant: 0.5 parts, deionized water: 35 parts, color Filler: 22 parts; among them, the environmentally friendly co-solvent is propylene glycol phenyl ether, the neutralizer is acetic acid, the surfactant is PPG4000, the pigment and filler include 15 parts of kaolin, and 7 parts of pigment, among which the pigment is according to MH-RC: chrome yellow 7000: A mixture of titanium dioxide with a mass ratio of 4:6:5;

[0069] The above-mentioned emulsion includes the following components in parts by mass: modified resin: 30 parts, emulsifier: 2 parts, neutralizer: 4 parts, deion...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of coatings and particularly discloses a cathodic electrophoretic coating and a preparation method thereof. The coating comprises components in parts by weight as follows: 10-20 parts of color paste, 30-60 parts of an emulsion and 40-60 parts of deionized water. The color paste comprises components in parts by weight as follows: 18-35 parts of modifiedresin, 5-15 parts of an environment-friendly cosolvent, 1-6 parts of a neutralizer, 0.1-0.5 parts of a surfactant, 30-40 parts of deionized water and 20-30 parts of pigment and filler. The emulsion comprises components in parts by weight as follows: 35-50 parts of modified resin, 2-8 parts of an emulsifier, 1-8 parts of a neutralizer and 30-50 deionized water. The cathodic electrophoretic coatinghas good gloss and high hardness and adhesion and has excellent impact resistance, corrosion resistance, acid resistance, base resistance and the like.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a cathodic electrophoretic coating and a preparation method thereof. Background technique [0002] Since the advent of cathodic electrophoretic coatings, both the coating itself and the coating application technology have made a lot of progress, and many products and new application technologies have been introduced. So far, almost 100% of the automotive primers use cathodic electrophoretic coatings. [0003] Electrophoretic coatings are the first water-based coatings developed. Its main features are high coating efficiency, economy, safety, and low pollution, and it is convenient for automated large-scale production. After decades of development, products have been constantly updated, and market demand has become increasingly demanding. Electrophoretic coatings are required to have higher throwing power, lower P / B, and better corner coverage. However, at present Current cathod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D5/08C09D5/44
CPCC09D5/08C09D5/4465C09D5/4488
Inventor 刘东胡中源董立志郭晓猛
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap