Injectable biocompatible bone matrix used for facial bone repair and preparation method thereof
A biocompatibility and bone matrix technology, applied in the field of bioengineering, can solve problems such as cartilage defects, large surgical incisions, and obvious recovery marks, and achieve the effects of good combination, high initial strength, and easy repair
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1:
[0020] An injectable biocompatible bone matrix for facial bone repair, which is composed of decellularized homogenous or heterogeneous cartilage with a mass fraction of 7.5 parts, a mass fraction of 7.5, and degreasing, decalcification, and decellularization processes. Said cartilage homogenous bone tissue, a mass fraction of 10 collagen fibrils, and a mass fraction of 75 parts of distilled water are mixed in a physiological state. This formula contains the decellularized cartilage of the same species or heterogeneity and the mass fraction of collagen fibrils. Therefore, the prepared bone matrix material has better growth and initial strength. The bone matrix material made according to this formula has better growth and initial strength.
Example Embodiment
[0021] Example 2:
[0022] An injectable biocompatible bone matrix for facial bone repair, which consists of 5 parts decellularized homogenous or heterogeneous cartilage, 10 mass fractions and degreasing, decalcification, and decellularization processes. Said cartilage homogenous bone tissue, a mass fraction of 10 collagen fibrils, and a mass fraction of 75 parts of distilled water are mixed in a physiological state. The mass fraction of the same or heterogeneous cartilage that has undergone decellularization used in this formula is relatively small, but the mass fraction of the cartilage of the same species that has undergone degreasing, decalcification, and decellularization has a greater mass fraction. According to this implementation The bone matrix prepared in Example 1 has higher initial strength than Example 1. The bone matrix material made according to this formula has higher initial strength than that of Example 1.
[0023] Further, the physiological state is a pH value ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap