High-property additive for cement fiber board and preparation method thereof

A cement fiber board, high-performance technology, applied in the field of cement fiber board, can solve the problem that the strength of fiber board is difficult to reach the corresponding standard, and achieve the effect of reducing the flexural strength and improving the tensile strength

Inactive Publication Date: 2018-11-06
合肥永泰新型建材有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patent literature (publication number: CN106738179A) discloses a fiberboard production additive, which includes the following components in parts by weight: 10-20 parts of adhesive, 5-15 parts of metal oxide fine powder, 3-8 parts of plant fiber, 5-10 parts of aluminum silicate fiber, 2-6 parts of paraffin, and 1-5 parts of rosin. The raw material ratio of the fiberboard additive is simple, which makes it difficult for the fiberboard strength to reach the corresponding standard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-property additive for cement fiber board and preparation method thereof
  • High-property additive for cement fiber board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of high-performance additive for cement fiber board of the present embodiment, comprises the raw material of following weight portion:

[0030] 22 parts of rice husk ash, 6 parts of inorganic composite ultrafine active filler, 3 parts of tailing sand, 9 parts of sulfuric acid slag mixed with steel slag powder, 2 parts of micro-silica fume, and 1 part of inorganic fiber.

[0031] The rice husk ash granularity of present embodiment is 2um, and specific surface area is 14m 2 / g.

[0032] The inorganic composite ultrafine active filler of the present embodiment is ultrafine Mg(OH) 2 , ultrafine diatomaceous earth, ultrafine AL(OH) 3 A mixture composed of 3:1:2 by weight.

[0033] The preparation method of sulfuric acid slag-doped steel slag powder in this embodiment is to mix sulfuric acid slag and steel slag powder, then heat-treat, then roast, then cool to room temperature, add dilute hydrochloric acid with a mass fraction of 20%, react for 22 minutes, and then ...

Embodiment 2

[0042] A kind of high-performance additive for cement fiber board of the present embodiment, comprises the raw material of following weight portion:

[0043] 26 parts of rice husk ash, 10 parts of inorganic composite ultrafine active filler, 6 parts of tailing sand, 13 parts of sulfuric acid slag mixed with steel slag powder, 5 parts of micro-silica fume, and 3 parts of inorganic fiber.

[0044] The rice husk ash granularity of present embodiment is 2um, and specific surface area is 14m 2 / g.

[0045] The inorganic composite ultrafine active filler of the present embodiment is ultrafine Mg(OH) 2 , ultrafine diatomaceous earth, ultrafine AL(OH) 3 A mixture composed of 3:1:2 by weight.

[0046] The preparation method of sulfuric acid slag-doped steel slag powder in this embodiment is to mix sulfuric acid slag and steel slag powder, then heat-treat, then roast, then cool to room temperature, add dilute hydrochloric acid with a mass fraction of 30%, react for 26 minutes, and th...

Embodiment 3

[0055] A kind of high-performance additive for cement fiber board of the present embodiment, comprises the raw material of following weight portion:

[0056] 24 parts of rice husk ash, 8 parts of inorganic composite ultrafine active filler, 4.5 parts of tailings sand, 11 parts of sulfuric acid slag mixed with steel slag powder, 3.5 parts of micro silica fume, 2 parts of inorganic fiber.

[0057] The rice husk ash granularity of present embodiment is 2um, and specific surface area is 14m 2 / g.

[0058] The inorganic composite ultrafine active filler of the present embodiment is ultrafine Mg(OH) 2 , ultrafine diatomaceous earth, ultrafine AL(OH) 3 A mixture composed of 3:1:2 by weight.

[0059] The preparation method of sulfuric acid slag-doped steel slag powder in this embodiment is to mix sulfuric acid slag and steel slag powder, then heat-treat, then roast, then cool to room temperature, add dilute hydrochloric acid with a mass fraction of 25%, react for 24 minutes, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-property additive for a cement fiber board. The high-property additive is prepared from the following raw materials in parts by weight: 22 to 26 parts of rice husk ash,6 to 10 parts of inorganic composite superfine active filler, 3 to 6 parts of tailing sand, 9 to 13 parts of sulfate residue-doped steel slag powder, 2 to 5 parts of micro-silicon powder, and 1 to 3 parts of inorganic fiber. The high-property additive for the cement fiber board and the preparation method have the advantages that the strength of the fiber board can be improved; the density of the fiber board can be correspondingly improved; the use value is higher, and the application prospect is good.

Description

technical field [0001] The invention relates to the technical field of cement fiber boards, in particular to a high-performance additive for cement fiber boards and a preparation method thereof. Background technique [0002] Cement fiberboard is a new type of building material made of silicon and calcareous materials as the main raw material, modified with natural reinforcing fibers and auxiliary materials, after pulping, copying, pressurization, and curing. It is used for exterior walls Hanging boards, indoor partitions, sound-absorbing ceilings, curtain wall linings, composite wall panels, outdoor billboards, metallurgy, electric furnace insulation panels, electrical distribution cabinets, transformer partitions, etc., according to the fibers used in them: currently domestic Most of them use asbestos fiber for reinforcement. This kind of fiber cement board is called chrysotile fiber cement board. Asbestos fiber cement board is not environmentally friendly. This is a shortc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B22/06
CPCC04B40/0039C04B18/101C04B22/066C04B14/08C04B22/06C04B18/12C04B18/142C04B18/0481C04B18/146C04B14/42C04B14/46
Inventor 伍志远
Owner 合肥永泰新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products