A kind of antibacterial ceramics for daily use

A technology for ceramics and daily use, which is applied in applications, household appliances, and other household appliances. It can solve the problems of no improvement in mechanical properties and reduced thermal shock resistance of ceramics, so as to reduce water absorption, improve thermal shock resistance, The effect of changing the organizational structure

Active Publication Date: 2021-01-22
福建省德化铠宇陶瓷有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Zirconium phosphate-loaded silver antibacterial agent is a commonly used inorganic antibacterial agent, but although the existing zirconium phosphate-loaded silver antibacterial agent has certain antibacterial effect, after it is applied in ceramics, zirconium phosphate-loaded silver antibacterial agent has no effect on the mechanical properties of ceramics. There is no promotion effect, and at the same time, when the addition of zirconium phosphate-loaded silver antibacterial agent is increased in order to improve the antibacterial effect, the thermal shock resistance of ceramics will also be reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial ceramics for daily use
  • A kind of antibacterial ceramics for daily use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An antibacterial daily-use ceramic, which contains 6% by mass of zirconium phosphate / sodium alginate modified attapulgite composite silver-loaded antibacterial agent.

[0019] Further, the preparation method of the zirconium phosphate / sodium alginate modified attapulgite composite silver-loaded antibacterial agent is:

[0020] (1) Sodium alginate was formulated into a sodium alginate aqueous solution with a mass fraction of 7.2%, and then the pH of the sodium alginate aqueous solution was adjusted to 8.5, and then n-hydroxysuccinimide was added to the seaweed at a mass ratio of 1:65 Sodium alginate aqueous solution, after stirring at 58 ° C, then add 40% of its mass attapulgite and 0.1% stearic acid to the sodium alginate aqueous solution, stir at 1800r / min for 1 hour, then add alginic acid Sodium aqueous solution with 3.2% mercaptosuccinic acid, adjust the temperature to 82°C, ultrasonically treat for 10 minutes, then stir at 350r / min for 2.5 hours, then dry by rotary ...

Embodiment 2

[0029] An antibacterial daily-use ceramic, the antibacterial daily-use ceramic contains 8% by mass of zirconium phosphate / sodium alginate modified attapulgite composite silver-loaded antibacterial agent.

[0030] Further, the preparation method of the zirconium phosphate / sodium alginate modified attapulgite composite silver-loaded antibacterial agent is:

[0031] (1) Sodium alginate was formulated into a sodium alginate aqueous solution with a mass fraction of 7.2%, and then the pH of the sodium alginate aqueous solution was adjusted to 8.5, and then n-hydroxysuccinimide was added to the seaweed at a mass ratio of 1:65 In the sodium alginate aqueous solution, after stirring at 58 ° C, add attapulgite of 42% by mass and 0.15% stearic acid to the sodium alginate aqueous solution, stir at 1800r / min for 1 hour, and then add alginic acid Sodium aqueous solution quality 3.2% mercaptosuccinic acid, adjust the temperature to 82°C, ultrasonic treatment for 12min, then stir at 350r / min ...

Embodiment 3

[0040] An antibacterial daily-use ceramic, which contains 7% by mass of zirconium phosphate / sodium alginate modified attapulgite composite silver-loaded antibacterial agent.

[0041] Further, the preparation method of the zirconium phosphate / sodium alginate modified attapulgite composite silver-loaded antibacterial agent is:

[0042] (1) Sodium alginate was formulated into a sodium alginate aqueous solution with a mass fraction of 7.2%, and then the pH of the sodium alginate aqueous solution was adjusted to 8.5, and then n-hydroxysuccinimide was added to the seaweed at a mass ratio of 1:65 Sodium alginate aqueous solution, after stirring at 58 ° C, then add attapulgite of 41% by mass and 0.12% stearic acid to the sodium alginate aqueous solution, stir at 1800r / min for 1 hour, then add alginic acid Sodium aqueous solution with 3.2% mercaptosuccinic acid, adjust the temperature to 82°C, ultrasonically treat for 11min, then stir at 350r / min for 2.5 hours, then dry by rotary evapo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses antibacterial domestic ceramics, and relates to the technical field of ceramics. The antibacterial domestic ceramics contains zirconium phosphate / sodium alginate modified attapulgite compound silver-carrying antibacterial agent of which the mass is 6-8%. The prepared antibacterial domestic ceramics not only has excellent thermal shock resistance and impact resistance strength, but also has a significant antibacterial effect and long germicidal duration time.

Description

technical field [0001] The invention belongs to the technical field of porcelain, and in particular relates to an antibacterial daily-use ceramic. Background technique [0002] Daily-use ceramics refer to household porcelain used in people's daily life, including tableware, tea set, coffee set, wine set, table set, etc. Daily-use ceramics are popular because of the following advantages: 1) easy to wash and keep clean; 2) good thermal stability and slow heat transfer; used to hold boiling water or scalding food, it is not too hot to handle. 3) The chemical properties are stable and durable; 4) Porcelain has very few pores and low water absorption; use daily-use porcelain to store food, and after sealing it tightly, it can prevent the moisture in the food from volatilizing, penetrating and external bacteria; 5) Color painting The decoration is rich and colorful, especially high-temperature glaze and blue and white decoration, which are free of lead poisoning hazards, can be u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/04C04B33/13
CPCC04B33/04C04B33/13C04B35/62605C04B2235/3201C04B2235/3248C04B2235/3463C04B2235/3472C04B2235/96
Inventor 姚永祥
Owner 福建省德化铠宇陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com