Wheat straw biomass particles and preparation method thereof

A technology of biomass granules and wheat straw, applied in the direction of biofuel, waste fuel, solid fuel, etc., to achieve the effect of preventing mildew, low price, and not easy to loose

Inactive Publication Date: 2018-11-30
亳州市创亿生物质燃料科技有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the research on the utilization of biomass energy in China mainly focuses on the biogas engineering technology of large and medium-sized livestock

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1

[0027] A kind of wheat straw biomass particles, comprising the following raw materials in parts by weight: 60 parts of wheat straw, 45 parts of rice husk, 30 parts of corn stalks, 15 parts of aquatic plants, 40 parts of sawdust, 35 parts of desulfurized coal slag, and Chinese medicinal slag 60 parts, 5 parts of gypsum, 5 parts of raising agent, 10 parts of paraffin wax, 20 parts of squalane powder, wherein the raising agent is calcium hydrogen phosphate, and the weight parts of the paraffin wax is 12 parts.

[0028] The measured fuel value of biomass particles when burning is 3858.3Kcal\kg.

Example Embodiment

[0029] Example 2

[0030] A kind of wheat straw biomass particles, comprising the following raw materials in parts by weight: 75 parts of wheat straw, 35 parts of rice husk, 32 parts of corn stalks, 15.8 parts of aquatic plants, 22 parts of sawdust, 25 parts of desulfurized coal slag, and Chinese medicinal slag 57 parts, 10 parts of gypsum, 2 parts of leavening agent, 20 parts of paraffin wax, and 15 parts of squalane powder. For the leavening agent, please refer to Example 1. The weight of paraffin wax is 18 parts.

[0031] The measured fuel value of biomass particles when burning is 4305.1Kcal\kg.

Example Embodiment

[0032] Example 3

[0033] A kind of wheat straw biomass particles, comprising the following raw materials in parts by weight: 55 parts of wheat straw, 30 parts of rice husk, 25 parts of corn stalks, 18 parts of aquatic plants, 30 parts of sawdust, 20 parts of desulfurized coal slag, and Chinese medicinal slag 50 parts, 12 parts of gypsum, 0.8 parts of leavening agent, 30 parts of paraffin wax, 8 parts of squalane powder, wherein the leavening agent please refer to Example 1, and the weight parts of paraffin wax is 16 parts.

[0034] The measured fuel value of biomass particles when burning is 3652Kcal\kg.

[0035] The present invention also provides a preparation method of wheat straw biomass particles, including the following steps:

[0036] Step 1. Drying: Put wheat straw, rice husk, corn stalks, aquatic plants, sawdust, desulfurized coal slag, and Chinese herbal medicine dregs in the sun for exposure;

[0037] Step 2. Cut into sections: Put the sun-dried raw material in Step 1 into ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of biofuel, in particular to wheat straw biomass particles. The wheat straw biomass particles comprise 55-75 parts of wheat straw, 30-45 parts of rice husk, 25-32 parts of corn stalk, 15-18 parts of waterweeds, 22-40 parts of sawdust, 20-35 parts of desulfurized coal slag, 50-60 parts of Chinese herbal medicine dregs, 5-12 parts of gypsum, 0.8-5 parts of swelling agent, 10-30 parts of paraffin wax, and 8-20 parts of squalane powder. A preparation method is also provided and comprises the steps of drying, segmenting, pulverizing, mixing, stirring, press forming, drying, granulating and packaging. According to the invention, the desulfurized coal slag and sawdust are added to the raw materials, so that the burning value of the biomass particles are higher than that of conventional biomass particles; the gypsum is added, and the prepared biomass particles are high in molding rate and not easy to loose due to good consolidation property of the gypsum; and the swelling agent is added, so that the biomass particles are loosened and can be fully burned when burned.

Description

technical field [0001] The invention relates to the technical field of biofuels, in particular to a wheat straw biomass particle and a preparation method thereof. Background technique [0002] The research and development of bioenergy technology has become one of the world's major hot topics, and has attracted the attention of governments and scientists around the world. Many countries have formulated corresponding development and research plans, such as the Sunshine Project in Japan, the Green Energy Project in India, and the Energy Farm in the United States, among which the development and utilization of bioenergy occupies a considerable share. Many foreign bioenergy technologies and devices have reached the level of commercial application. Compared with other biomass energy technologies, biomass pellet fuel technology is easier to achieve large-scale production and use. The convenience of using bioenergy particles is comparable to energy such as gas and oil. Taking the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10L5/44C10L9/10
CPCC10L5/442C10L5/445C10L9/10C10L2290/08C10L2290/24C10L2290/28C10L2290/30C10L2290/32Y02E50/10Y02E50/30
Inventor 葛鑫
Owner 亳州市创亿生物质燃料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap