High barrier polyethylene film and preparation method thereof
A polyethylene film, high barrier technology, applied in the field of polyethylene film, can solve the problems of difficult film process, poor water resistance, difficult to control the amount of paint, etc., to achieve the effect of reducing operation difficulty and production cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1: Preparation of filler 1
[0023] The preparation steps of the filler in this embodiment are as follows:
[0024] Weigh the raw materials according to the following mass percentages: 10% 304 stainless steel powder, 15% nano titanium, 20% silver nitrate, 5% urea, 0.2% polyvinylpyrrolidone, 0.2% ammonium carbamate, 30% hydrophobic Water agent, 10% 50wt% nitric acid solution, 304 stainless steel powder with a particle size of 80nm, and nano-titanium with a particle size of 15nm;
[0025] Prepare urea into a saturated aqueous urea solution, then add nano-grade 304 stainless steel, heat to 40°C, keep it for 20 minutes, take it out, filter and wash it, add it to a 50wt% nitric acid solution, soak it at 90°C for 10 hours, take it out, and scrub Clean, get pretreated nano-grade 304 stainless steel, ready for use;
[0026] Add silver nitrate to the ethanol solution to prepare a 30wt% silver nitrate ethanol solution, add polyvinylpyrrolidone and stir evenly, then add nano-tita...
Example Embodiment
[0027] Example 2: Preparation of filler 2
[0028] The preparation steps of the filler in this embodiment are as follows:
[0029] Weigh the raw materials according to the following mass percentages: 8% 304 stainless steel powder, 13% nano titanium, 18% silver nitrate, 3% urea, 0.2% polyvinylpyrrolidone, 0.2% ammonium carbamate, 25% hydrophobic Aqueous solution, 10% 55% by weight nitric acid solution, 304 stainless steel powder with a particle size of 60nm, and nano-titanium with a particle size of 12nm;
[0030] Prepare urea into a saturated aqueous urea solution, then add nano-grade 304 stainless steel, heat to 40°C, keep it for 20 minutes, take it out, filter and wash it, add it to 55wt% nitric acid solution, soak it at 90°C for 13h, take it out, and brush it Clean, get pretreated nano-grade 304 stainless steel, ready for use;
[0031] Add silver nitrate to the ethanol solution to prepare a 20wt% silver nitrate ethanol solution, add polyvinylpyrrolidone and stir evenly, then add n...
Example Embodiment
[0032] Example 3: Preparation of filler three
[0033] The preparation steps of the filler in this embodiment are as follows:
[0034] Weigh the raw materials according to the following mass percentages: 9% 304 stainless steel powder, 15% nano titanium, 20% silver nitrate, 4% urea, 0.2% polyvinylpyrrolidone, 0.2% ammonium carbamate, 20% hydrophobic Water agent, 9% 55% by weight nitric acid solution, 304 stainless steel powder with a particle size of 50nm, and nano-titanium with a particle size of 10nm;
[0035] Prepare urea into a saturated aqueous urea solution, then add nano-grade 304 stainless steel, heat to 50°C, keep it for 20 minutes, take it out, filter and wash it, add it to 60wt% nitric acid solution, soak it at 90°C for 16h, take it out, brush it Clean, get pretreated nano-grade 304 stainless steel, ready for use;
[0036] Add silver nitrate to the ethanol solution to prepare a 10wt% silver nitrate ethanol solution, add polyvinylpyrrolidone and stir evenly, then add nano-ti...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap