A method for preparing large particle high-purity vanadium pentoxide

A vanadium pentoxide and vanadium precipitation technology, which is applied in the field of vanadium chemical industry, can solve the problems of long process flow, insufficient purity of vanadium pentoxide products, and high production costs, and achieve simple process operation, good application prospects, and easy realization Effect

Active Publication Date: 2020-07-07
HEBEI IRON AND STEEL
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned method has a long process flow, a lot of labor, and high production costs, and the purity of most vanadium pentoxide products cannot meet the requirements of vanadium for some high-end products.
[0005] In addition to the requirements on purity, some customers need larger particles and specific particle size range of vanadium pentoxide products in the application process, which poses new challenges for the preparation of vanadium pentoxide products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing large particle high-purity vanadium pentoxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Such as figure 1 Shown, the present invention prepares large particle high-purity vanadium pentoxide according to the following steps.

[0042] (1) Weigh 300g of ammonium metavanadate with a water content of about 10%, put it into 5L of water, heat to 98°C to dissolve, add ammonia water until the pH value is 7.0, and after 10min, filter to obtain a vanadium-containing vanadium with a vanadium concentration of 23g / L purification fluid;

[0043] (2) Heat the vanadium-dissolved purification solution obtained in step (1) to boiling, gradient acid precipitation, add sulfuric acid dropwise to the vanadium-containing purification solution to adjust the pH, and stop at the pH values ​​of 5.8, 5.6, and 4.4 for 10 minutes to precipitate vanadium , continue to drop sulfuric acid to adjust the pH to 2.1, and precipitate vanadium for 60 minutes. During the entire process of vanadium precipitation, the temperature is controlled at 95-100°C. After the reaction is completed, filter to...

Embodiment 2

[0047] (1) Weigh 150g of ammonium metavanadate with a water content of about 10%, put it into 5L of water, heat to 95°C to dissolve, add ammonia water until the pH value is 7.5, and after 20min, filter to obtain a vanadium concentration of 11.5g / L. Vanadium purification solution;

[0048] (2) Heat the vanadium-dissolved purification solution obtained in step (1) to boiling, gradient acid precipitation, add sulfuric acid dropwise to the vanadium-containing purification solution to adjust the pH, and stop at the pH values ​​of 5.9, 5.5, and 4.7 for 15 minutes to deposit vanadium , continue to drop sulfuric acid to adjust the pH to 2.0, react for 50 minutes, and control the temperature at 90-100°C during the whole process of vanadium precipitation, filter after the reaction, and obtain the mother liquor of vanadium precipitation and high-purity large-particle solid-phase ammonium polyvanadate;

[0049] (3) Washing the high-purity large-particle solid-phase ammonium polyvanadate o...

Embodiment 3

[0052] (1) Weigh 300g of ammonium metavanadate with a water content of about 10%, put it into 5L of water, heat to 98°C to dissolve, add ammonia water until the pH value is 6.5, and after 30min, filter to obtain vanadium with a vanadium concentration of 23g / L purification fluid;

[0053] (2) Heat the vanadium-dissolved purification solution obtained in step (1) to boiling, gradient acid precipitation, add sulfuric acid to the vanadium-containing purification solution to adjust the pH, and stop at the pH values ​​of 6, 5.7, and 4.8 for 20 minutes to precipitate vanadium , continue to add sulfuric acid dropwise to adjust the pH to 2.4, react for 80 minutes, and control the temperature at 90-100°C during the whole process of vanadium precipitation, filter after the reaction, and obtain the mother liquor of vanadium precipitation and high-purity large-particle solid-phase ammonium polyvanadate;

[0054] (3) Washing the high-purity large-particle solid-phase ammonium polyvanadate o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing large-particle high-purity vanadium pentoxide. The method comprises the following steps: after dissolving ammonium metavanadate, adding an impurity removing agent; regulating the pH (Potential of Hydrogen) of a solution to 6.5 to 8.2 and carrying out vanadium dissolving; after the vanadium dissolving is finished, carrying out solid-liquid separationto obtain a vanadium-contained purification solution; heating the vanadium-contained purification solution; then regulating the pH to 6 to 5.8, 5.7 to 5.4, 4.8 to 4.0 and 2.4 to 1.9 in sequence at four phases and carrying out gradient vanadium deposition; after vanadium deposition is finished, carrying out the solid-liquid separation to obtain a vanadium deposition mother solution and solid-phaseammonium polyorthovanadate; carrying out calcination and deamination on the ammonium polyorthovanadate to obtain a vanadium pentoxide product with the purity of greater than or equal to 99.95 weight percent and the granularity of greater than or equal to 150mum. According to the method provided by the invention, a vanadium dissolving and gradient vanadium deposition method is adopted and impurityelements are greatly removed; meanwhile, the granularity of the vanadium pentoxide is accurately controlled, so that the content of particles with the size in a range of 180 to 230mum is greater thanor equal to 60 percent; the requirements of customers are met and the method has a good application prospect.

Description

technical field [0001] The invention relates to the field of vanadium chemical industry, in particular to a method for preparing large-particle high-purity vanadium pentoxide. Background technique [0002] Vanadium is a polyvalent element, its valence is V 2+ to V 5+ Transform between. High-efficiency, green, and emerging energy storage devices, all-vanadium redox flow batteries use this characteristic of vanadium, and use all-vanadium ion solution as the positive and negative electrolytes of the vanadium battery. 4+ / V 5+ , at the negative pole of the battery V 2+ / V 3+ Charge and discharge are mutually converted; the performance of the vanadium ion electrolyte directly affects the performance of the vanadium battery. In order to achieve its high quality, long life, high energy efficiency, and stable working conditions, vanadium pentoxide with a purity of more than 99.9% is generally used to produce its electrolyte. [0003] In the chemical synthesis industry, this c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G31/02
CPCC01G31/02C01P2004/60C01P2006/80
Inventor 李兰杰闫浩祁健赵备备柳朝阳张振全
Owner HEBEI IRON AND STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com