Foamed lightweight wallboard based on graphene and non-ferrous metal tailings and preparation method thereof

A non-ferrous metal and lightweight wallboard technology, which is applied to ceramic products, clay products, and other household appliances, can solve the problems of increased workload, low economic returns, more manpower, financial and material resources, and reduce foaming reactions The temperature, the gap is fine and uniform, and the effect of avoiding the cracking of the matrix

Active Publication Date: 2019-09-06
GUANGXI XUTENG INDUSTRIAL GROUP CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although non-ferrous metal tailings have good potential utilization value, the current technical level cannot make good use of them, and the economic benefits are also very low
The treatment of non-ferrous metal tailings has not only seriously affected the development of the non-ferrous metal mining industry, but also with the increasing number of tailings, its management has become more and more difficult, and the workload has also increased greatly
It takes a lot of manpower, financial and material resources to deal with these non-ferrous metal tailings, and it also causes environmental pollution, waste of resources, potential safety hazards, land occupation and other major social hazards.
[0007] Usually, non-ferrous metal tailings contain other common and associated radioactive elements, such as uranium, thorium, radium, etc. If these tailings containing radioactive elements are made into building wallboards for use, they will bring harm to environmental safety and human health. potential hazard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foamed lightweight wallboard based on graphene and non-ferrous metal tailings and preparation method thereof
  • Foamed lightweight wallboard based on graphene and non-ferrous metal tailings and preparation method thereof
  • Foamed lightweight wallboard based on graphene and non-ferrous metal tailings and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A foamed lightweight wallboard based on graphene and non-ferrous metal tailings, including main materials and auxiliary materials. In parts by weight, the main materials include 82 parts of non-ferrous metal tailings; auxiliary materials include 2 parts of graphene and 8 parts of vermiculite , 15 parts of chopped carbon fiber, 7 parts of aluminum fluoride, 6 parts of aluminum silicate fiber, 10 parts of montmorillonite, 10 parts of zirconium silicate, 5 parts of clay, 2 parts of sodium tripolyphosphate, 10 parts of cosolvent, foam 2 parts of agent and 2 parts of stabilizer.

[0044] The non-ferrous metal tailings refer to magnesium ore tailings, aluminum ore tailings and tungsten ore tailings.

[0045] The clay is high liquid limit earth and diatomaceous earth.

[0046] The fluxing agent is cryolite and bosmanite.

[0047] Described whipping agent is tapioca starch and carbon powder.

[0048] The stabilizer is manganese dioxide.

[0049] The length of the chopped ca...

Embodiment 2

[0063] A foamed lightweight wallboard based on graphene and non-ferrous metal tailings, including main materials and auxiliary materials. In parts by weight, the main materials include 80 parts of non-ferrous metal tailings; auxiliary materials include 1 part of graphene and 10 parts of vermiculite , 13 parts of chopped carbon fiber, 4 parts of aluminum fluoride, 4 parts of aluminum silicate fiber, 7 parts of montmorillonite, 5 parts of zirconium silicate, 4 parts of clay, 2 parts of sodium tripolyphosphate, 15 parts of cosolvent, foam 2 parts of agent and 2 parts of stabilizer.

[0064] The non-ferrous metal tailings refer to gold ore tailings, nickel ore tailings and cobalt ore tailings.

[0065] The clay is white clay and bentonite.

[0066] The flux is boron mud and light-burned magnesia.

[0067] Described whipping agent is tapioca starch and calcium carbonate.

[0068] The stabilizer is cobalt oxide.

[0069] The treatment of non-ferrous metal tailings and the prepar...

Embodiment 3

[0072] A foamed lightweight wallboard based on graphene and non-ferrous metal tailings, including main materials and auxiliary materials. According to parts by weight, the main materials include 85 parts of non-ferrous metal tailings; auxiliary materials include 7 parts of graphene and 13 parts of vermiculite , 18 parts of chopped carbon fiber, 8 parts of aluminum fluoride, 7 parts of aluminum silicate fiber, 13 parts of montmorillonite, 17 parts of zirconium silicate, 8 parts of clay, 4 parts of sodium tripolyphosphate, 7 parts of cosolvent, foam 4 parts of agent, 3 parts of stabilizer.

[0073] The non-ferrous metal tailings refer to magnesium ore tailings, aluminum ore tailings and tin ore tailings.

[0074] The clay is a high liquid limit soil.

[0075] The fluxes are talc, diopside and illite.

[0076] The foaming agent is tapioca starch.

[0077] The stabilizers are manganese dioxide and cobalt oxide.

[0078] The treatment of non-ferrous metal tailings and the prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of enclosure wall materials of buildings, and particularly relates to a graphene and nonferrous metal tailings-based foamed light wallboard and a preparation methodthereof. The graphene and nonferrous metal tailings-based foamed light wallboard comprises a main material and an auxiliary material. The main material comprises the following component in parts by weight: 70-90 parts of nonferrous metal tailings; and the auxiliary material comprises the following components in parts by weight: 0.5-8 part of graphene, 1-15 parts of vermiculite, 2-10 parts of aluminum fluoride, 3-8 parts of aluminum silicate fibers, 5-15 parts of montmorillonite, 1-10 parts of clay, 5-20 parts of a cosolvent, 0.1-5 parts of a foamer and 0.1-5 parts of a stabilizer. The foamed light wallboard provided by the invention has the characteristics of being light, high in strength, light, high in toughness, fireproof, high-temperature-resistant, waterproof, anti-seepage, green, environmentally-friendly and the like.

Description

[0001] 【Technical field】 [0002] The invention relates to the field of building enclosure wall materials, in particular to a foamed lightweight wallboard based on graphene and non-ferrous metal tailings and a preparation method thereof. [0003] 【Background technique】 [0004] The existing concrete aerated blocks, shale hollow bricks, lightweight ceramsite concrete wall panels, and lightweight polyethylene concrete wall panels are of poor quality for the interior and exterior walls of the same volume, low compressive and flexural strength, and sound and heat insulation. Poor performance, poor waterproof and impermeable performance, high water absorption, easy cracking at the interface, easy cracking and falling off of the cement mortar batch layer, easy aging, unsafe and environmentally friendly, when making partition walls with aerated concrete and hollow brick wall panels, there is volume It is large, takes up a lot of building space, is heavy, and requires sporadic masonry....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/132C04B33/36C04B38/02
CPCC04B33/131C04B33/132C04B33/36C04B38/02C04B2235/3248C04B2235/3418C04B2235/3427C04B2235/425C04B2235/5228C04B2235/5248Y02P40/60
Inventor 黄聿新黄昭烨余延波
Owner GUANGXI XUTENG INDUSTRIAL GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com