High temperature-resistant anticorrosive paint and preparation method thereof

A technology of anti-corrosion coating and high temperature resistance, applied in anti-corrosion coatings, fire retardant coatings, coatings, etc., can solve problems such as harm to the human body, pollute the environment, high temperature resistance, etc., achieve good water resistance, improve adhesion, and improve compatibility. Effect

Inactive Publication Date: 2018-12-21
WUHU ZHANGHONG ENG TECH CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional anti-corrosion coatings have a short lifespan under high temperature conditions because they are not resistant to high temperatures, and contain a large amount of metal compounds, which not only pollute the environment, but also are harmful to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature-resistant anticorrosive paint and preparation method thereof
  • High temperature-resistant anticorrosive paint and preparation method thereof
  • High temperature-resistant anticorrosive paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high temperature resistant anticorrosion coating, comprising the following raw materials in parts by weight:

[0028]

[0029] The solvent is a mixed solvent composed of ethylene glycol, toluene, and benzene in a volume ratio of 1:1:1; the preparation method of the modified boric acid is: heating the boric acid at 210-230° C. for 0.5-1.0 h, cooling After grinding, the particle size is above 500 mesh.

[0030] The preparation method of described high temperature resistant anticorrosion coating comprises the following steps:

[0031] (1) Add the epoxy-modified silicone resin and polytetrafluoroethylene resin in the formula amount into the solvent, and stir at a high speed of 10000~13000r / min evenly;

[0032] (2) Then add SiC micropowder, talcum powder, asbestos powder, modified boric acid and glass powder, stir evenly at a high speed of 10000-13000r / min, and grind to a fineness below 50μm with a sand mill;

[0033] (3) Finally, add a silane coupling agent, a defoam...

Embodiment 2

[0035] A high temperature resistant anticorrosion coating, comprising the following raw materials in parts by weight:

[0036]

[0037] The solvent is a mixed solvent composed of ethylene glycol, toluene, and benzene in a volume ratio of 1:1:1; the preparation method of the modified boric acid is: heating the boric acid at 210-230° C. for 0.5-1.0 h, cooling After grinding, the particle size is above 500 mesh.

[0038] The preparation method of described high temperature resistant anticorrosion coating comprises the following steps:

[0039] (1) Add the epoxy-modified silicone resin and polytetrafluoroethylene resin in the formula amount into the solvent, and stir at a high speed of 10000~13000r / min evenly;

[0040] (2) Then add SiC micropowder, talcum powder, asbestos powder, modified boric acid and glass powder, stir evenly at a high speed of 10000-13000r / min, and grind to a fineness below 50μm with a sand mill;

[0041] (3) Finally, add a silane coupling agent, a defoam...

Embodiment 3

[0043] A high temperature resistant anticorrosion coating, comprising the following raw materials in parts by weight:

[0044]

[0045] The solvent is a mixed solvent composed of ethylene glycol, toluene, and benzene in a volume ratio of 1:1:1; the preparation method of the modified boric acid is: heating the boric acid at 210-230° C. for 0.5-1.0 h, cooling After grinding, the particle size is above 500 mesh.

[0046] The preparation method of described high temperature resistant anticorrosion coating comprises the following steps:

[0047] (1) Add the epoxy-modified silicone resin and polytetrafluoroethylene resin in the formula amount into the solvent, and stir at a high speed of 10000~13000r / min evenly;

[0048] (2) Then add SiC micropowder, talcum powder, asbestos powder, modified boric acid and glass powder, stir evenly at a high speed of 10000-13000r / min, and grind to a fineness below 50μm with a sand mill;

[0049] (3) Finally, add a silane coupling agent, a defoam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high temperature-resistant anticorrosive paint and a preparation method thereof. The high temperature-resistant anticorrosive paint is prepared from the following raw materials: epoxy-modified silicon resin, polytetrafluoroethylene resin, SiC micro powder, talcum powder, asbestos powder, glass powder, modified boric acid, a silane coupling agent, a defoaming agent, a flatting agent and a film-forming agent. The paint not only has excellent high temperature resistance performance and flame retardation performance, but also has good anticorrosive performance of salt fog resistance, water resistance, salt water resistance, ageing resistance and the like, can adapt to different construction modes, and is ideal heat-resistant anticorrosive paint.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a high-temperature-resistant anti-corrosion coating and a preparation method thereof. Background technique [0002] Some equipment used in high-temperature environments, such as: exhaust pipes of automobiles and motorcycles, chimneys, etc., due to long-term exposure to high-temperature and harsh environments, the life of the equipment will be reduced, so it needs to be protected. The commonly used method is spray coating. However, traditional anti-corrosion coatings are not resistant to high temperatures, have a short lifespan under high temperature conditions, and contain a large amount of metal compounds, which not only pollute the environment, but are also harmful to the human body. Contents of the invention [0003] The object of the present invention is to provide a high temperature resistant anticorrosion coating and a preparation method thereof. The coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/06C09D127/18C09D5/08C09D7/61
CPCC08L2201/08C09D5/08C09D5/18C09D183/06C09D7/61C09D7/70C08L27/18C08K13/04C08K3/34C08K7/12C08K3/40
Inventor 不公告发明人
Owner WUHU ZHANGHONG ENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap