Organosilicone modified copolymer emulsion tipping adhesive and preparation method thereof

A technology of copolymerization emulsion and silicone, which is applied in the direction of monocarboxylate copolymer adhesives, adhesive types, etc., can solve the problems of poor film forming, air leakage, and poor water resistance of the film, so as to improve water resistance and Effect of Adhesive Strength

Inactive Publication Date: 2018-12-21
CHUZHOU GUANGWEI CHEM
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

All these hydrophilic hydroxyl groups cause poor low-temperature film-forming properties of PVAc and poor water resistance of the f...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A silicone modified copolymer emulsion tipping glue, comprising the following materials in parts by weight: 15 parts of vinyl acetate, 3 parts of polyvinyl alcohol, 10 parts of butyl acrylate, 3 parts of isooctyl acrylate, 2 parts of acrylic acid, γ-formazol 3 parts of acryloyloxypropyltrimethoxysilane, 2 parts of vinyltriethoxysilane, 2 parts of vinyltrimethoxysilane, 4 parts of deionized water, 1 part of compound emulsifier, 3 parts of other additives;

[0022] Described composite emulsifier comprises OP-10 and MS-1, and the weight ratio of OP-10 and MS-1 is 4:1;

[0023] Described other auxiliary agent comprises composite plasticizer, tackifier and initiator, and the weight ratio of composite plasticizer, tackifier and initiator is 2:3:1;

[0024] The composite plasticizer comprises tributyl and dibutyl phthalate, and the ratio of tributyl and dibutyl phthalate in parts by weight is 1:1;

[0025] Described tackifier is rosin glyceride; Described initiator is potassi...

Embodiment 2

[0028] A silicone modified copolymer emulsion tipping glue, comprising the following materials in parts by weight: 18 parts of vinyl acetate, 6 parts of polyvinyl alcohol, 17 parts of butyl acrylate, 7 parts of isooctyl acrylate, 3 parts of acrylic acid, γ-formazol 6 parts of acryloyloxypropyltrimethoxysilane, 4 parts of vinyltriethoxysilane, 4 parts of vinyltrimethoxysilane, 8 parts of deionized water, 2 parts of compound emulsifier, 6 parts of other additives;

[0029] Described compound emulsifier comprises OP-10 and MS-1, and OP-10 and MS-1 weight ratio are 5:1;

[0030] Described other auxiliary agent comprises composite plasticizer, tackifier, initiator and defoamer; The weight ratio of described plasticizer, tackifier, initiator and defoamer is 2:2:0.8:1 ;

[0031] The composite plasticizer includes tributyl and dibutyl phthalate, and the ratio of tributyl and dibutyl phthalate in parts by weight is 1:2; the tackifier is rosin glyceride; the The initiator is potassium...

Embodiment 3

[0034] A silicone modified copolymer emulsion tipping glue, comprising the following materials in parts by weight: 22 parts of vinyl acetate, 10 parts of polyvinyl alcohol, 25 parts of butyl acrylate, 12 parts of isooctyl acrylate, 4 parts of acrylic acid, γ-formazol 12 parts of acryloyloxypropyltrimethoxysilane, 5 parts of vinyltriethoxysilane, 6 parts of vinyltrimethoxysilane, 11 parts of deionized water, 3 parts of compound emulsifier, 10 parts of other additives;

[0035] Described composite emulsifier comprises OP-10 and MS-1, and the weight ratio of OP-10 and MS-1 is 6:1;

[0036] Described other auxiliary agent comprises composite plasticizer and initiator; The weight ratio of described composite plasticizer and initiator is 1:1.5;

[0037] Described composite plasticizer comprises tributyl ester and dibutyl phthalate, and tributyl ester and dibutyl phthalate weight ratio are 1:2; Described initiator is the potassium persulfate of equal quality and Ammonium persulfate;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an organosilicone modified copolymer emulsion tipping adhesive which is prepared from the following materials in parts by weight: 15 to 22 parts of vinyl acetate, 3 to 10 partsof polyvinyl alcohol, 10 to 25 parts of butyl acrylate, 3 to 12 parts of 2-ethylhexyl acrylate, 2 to 4 parts of acrylic acid, 3 to 12 parts of gamma-methylacryloyl oxypropyl trimethoxy silane, 2 to 5parts of vinyl triethoxysilane, 2 to 6 parts of vinyl trimethoxy silane, 4 to 11 parts of deionized water, 1 to 3 parts of a compound emulsifier and 3 to 10 parts of other additives. According to theorganosilicone modified copolymer emulsion tipping adhesive disclosed by the invention and a preparation method thereof, the viscosity and the storage stability are improved, and the rejection rate oftipped cigarettes is reduced.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an organosilicon-modified copolymer emulsion tipping glue and a preparation method thereof. Background technique [0002] When PVAc is polymerized, polyvinyl alcohol is used as a protective colloid, so that the emulsion system contains a large number of hydroxyl groups; in addition, during the polymerization of vinyl acetate emulsion, PV Ac macromolecular side chains are hydrolyzed to a certain extent to produce a certain number of hydroxyl groups. All these hydrophilic hydroxyl groups cause poor low-temperature film-forming properties of PVAc and poor water resistance of the film, which limits its application, which will lead to quality problems such as mouth drop, air leakage, and uneven paste. . In order to improve the quality of cigarette adhesives for cigarettes at high-speed tipping machines, a high-speed tipping glue with good adhesive properties is needed. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J131/04C08F218/08C08F220/18C08F220/06C08F230/08
CPCC08F218/08C09J131/04C08F220/1804C08F220/1808C08F220/06C08F230/08
Inventor 李勇
Owner CHUZHOU GUANGWEI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap