Imitating fancy glaze for jun porcelain light fixtures and preparation process of imitating fancy glaze

A technology for lighting and Jun porcelain, applied in the field of imitation flower glaze for Jun porcelain lighting and its preparation, can solve the problems of high production cost and production difficulty, few formulas and preparation methods, low mechanical strength, etc., and achieves high artistic value and economical. Value, reduce energy consumption, improve the effect of mechanical strength

Inactive Publication Date: 2019-01-04
杨鹏飞
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides an imitation flower glaze for Jun porcelain lamp decoration with novel raw materials and proportion and its preparation method to solve the problem that the existing Jun porcelain lamp decoration imitation flower glaze has few formulas and preparation methods, low mechanical strength, and low yield. Problems of high cost and production difficulty

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An imitation flower glaze for Jun porcelain lighting, prepared from the following raw materials in parts by weight: 42 parts of yellow feldspar, 10 parts of white feldspar, 8 parts of quartz, 11 parts of calcite, 12 parts of spodumene, 4 parts of kaolin, 6 parts of limestone, 2 parts of titanium ore, 8 parts of copper ore, 3 parts of cyanine and 8 parts of talc.

[0021] The preparation method of the imitation flower glaze for Jun porcelain lamp decoration comprises the following steps:

[0022] (1) Grind the above raw materials and mix them into a ball mill for ball milling, add water with 40% of the total weight of the mixed raw materials, wet mill for 20 hours, and pass the wet milled slurry through a 250-mesh sieve to obtain glaze slurry;

[0023] (2) Glaze the green body;

[0024] (3) Firing, the firing temperature is 1250°C.

[0025] Preferably, in the preparation method of the imitation flower glaze for Jun porcelain lamp decoration, the firing process in step ...

Embodiment 2

[0032] An imitation flower glaze for Jun porcelain lighting, prepared from the following raw materials in parts by weight: 46 parts of feldspar, 12 parts of white feldspar, 10 parts of quartz, 13 parts of calcite, 16 parts of spodumene, 5 parts of kaolin, and 8 parts of limestone , 3 parts of titanium ore, 10 parts of copper ore, 4 parts of cyanine and 10 parts of talc.

[0033] The preparation method of the imitation flower glaze for Jun porcelain lamp decoration comprises the following steps:

[0034] (1) After crushing the above raw materials, mix them into a ball mill for ball milling, add water with a total weight of 42% of the mixed raw materials, wet mill for 22 hours, and pass the wet milled slurry through a 280-mesh sieve to obtain a glaze slurry;

[0035] (2) Glaze the green body;

[0036] (3) Firing, the firing temperature is 1280°C.

[0037] Preferably, in the preparation method of the imitation flower glaze for Jun porcelain lamp decoration, the firing process i...

Embodiment 3

[0044] An imitation flower glaze for Jun porcelain lighting, prepared from the following raw materials in parts by weight: 50 parts of feldspar, 14 parts of white feldspar, 12 parts of quartz, 15 parts of calcite, 20 parts of spodumene, 6 parts of kaolin, 10 parts of limestone parts, 4 parts of titanium ore, 12 parts of copper ore, 5 parts of cyanine and 12 parts of talc.

[0045] The preparation method of the imitation flower glaze for Jun porcelain lamp decoration comprises the following steps:

[0046] (1) The above raw materials are pulverized and mixed into a ball mill for ball milling, adding water with a total weight of 44% of the mixed raw materials, wet milling for 24 hours, and passing the wet milled slurry through a 300-mesh sieve to obtain a glaze slurry;

[0047] (2) Glaze the green body;

[0048] (3) Firing, the firing temperature is 1300°C.

[0049] Preferably, in the preparation method of the imitation flower glaze for Jun porcelain lamp decoration, the firin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses imitating fancy glaze for jun porcelain light fixtures and a preparation process of the imitating fancy glaze. Prepared imitating fancy glaze porcelain has high yield, reducedproduction cost and very high artistic value and economic value. Spodumene reacts with kaolin and quartz in the firing process, produced mullite still keeps the appearance of kaolinite. The spodumeneadded to the formula can increase the firing speed and cannot cause product cracking, so that energy consumption can be reduced, the yield is about 88%, and the production cost can be reduced.

Description

technical field [0001] The invention relates to the technical field of Jun porcelain preparation, in particular to an imitation flower glaze for Jun porcelain lamp decoration and a preparation method thereof. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a rich family is not as good as a piece of Jun porcelain". It is a unique national treasure porcelain in Henan Province. With its simple shape, Exquisite craftsmanship, complex glaze matching, the magical kiln transformation of "one color in the kiln, and thousands of colors in the kiln", lakes and mountains, clouds and mist, human beings, animals, flowers, birds, insects and fish, etc., are known as China's "Five Famous Porcelains". "The first. [0003] In the production of Jun porcelain, althou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86
Inventor 杨鹏飞
Owner 杨鹏飞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com