Anti-cracking concrete

A concrete and anti-cracking technology, which is applied in the field of concrete, can solve the problems of easy cracks, performance degradation, and shortened life, and achieve the effects of increasing fluidity, reducing voids, and improving strength

Inactive Publication Date: 2019-01-04
蚌埠市方阵商品混凝土有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, with the vigorous development of the domestic construction industry, the requirements for the strength and crack resistance of the concrete consumed in the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1

[0016] The anti-cracking concrete proposed by the present invention includes raw materials in parts by weight: 68 parts of cement, 70 parts of quartz sand, 40 parts of ceramic sand, 0.5 parts of mixed fibers, 8 parts of cordierite, 0.9 parts of light burnt magnesia, and microsilica 15 parts of powder, 1.8 parts of zeolite, 8 parts of limestone powder, 1 part of lead-zinc tailings composite powder, 1.3 parts of steel slag powder, 1.2 parts of rice husk, 2 parts of alumina hollow spheres, 0.5 parts of calcite powder, 0.28 parts of epoxy resin emulsion , 1 part of waterproofing agent, 28 parts of water, 0.6 parts of water reducing agent, 0.32 parts of sludge.

Example Embodiment

[0017] Example 2

[0018] The anti-cracking concrete proposed by the present invention includes raw materials in parts by weight: 55 parts of cement, 100 parts of quartz sand, 20 parts of ceramic sand, 1.1 parts of mixed fibers, 3 parts of cordierite, 2.7 parts of light burnt magnesium oxide, and microsilica 7 parts of powder, 2.8 parts of zeolite, 4 parts of limestone powder, 3 parts of lead-zinc tailings composite powder, 0.2 parts of steel slag powder, 3.5 parts of rice husk, 0.5 parts of alumina hollow spheres, 2 parts of calcite powder, 0.1 parts of epoxy resin emulsion , 1.8 parts of waterproofing agent, 20 parts of water, 2.6 parts of water reducing agent, 0.1 parts of sludge.

Example Embodiment

[0019] Example 3

[0020] The anti-cracking concrete proposed by the present invention includes raw materials in parts by weight: 67 parts of cement, 78 parts of quartz sand, 33 parts of ceramic sand, 0.7 parts of mixed fibers, 7 parts of cordierite, 1.2 parts of light burnt magnesium oxide, and microsilica 14 parts of powder, 2 parts of zeolite, 7 parts of limestone powder, 1.2 parts of lead-zinc tailings composite powder, 1.1 parts of steel slag powder, 1.7 parts of rice husk, 1.6 parts of alumina hollow spheres, 0.7 parts of calcite powder, 0.26 parts of epoxy resin emulsion , 1.2 parts of waterproofing agent, 27 parts of water, 0.9 parts of water reducing agent, 0.3 parts of sludge;

[0021] Wherein, the mixed fiber is a mixture of steel fiber, polyacrylonitrile fiber, profiled plastic steel fiber, and bagasse fiber, and the weight ratio of steel fiber, polyacrylonitrile fiber, profiled plastic steel fiber, and bagasse fiber is 1:10:3 : 5;

[0022] The specific surface area of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-cracking concrete. The anti-cracking concrete comprises the following raw materials in parts by weight: 55-68 parts of cement, 70-100 parts of quartz sand, 20-40 partsof pottery sand, 0.5-1.1 parts of composite fibers, 3-8 parts of cordierite, 0.9-2.7 parts of light calcined magnesia, 7-15 parts of silica fume, 1.8-2.8 parts of zeolite, 4-8 parts of agstone, 1-3 parts of lead-zinc tailings composite powder, 0.2-1.3 parts of steel slag powder, 1.2-3.5 parts of rice husks, 0.5-2 parts of alumina hollow balls, 0.5-2 parts of calcite in powder, 0.1-0.28 part of epoxy resin latex, 1-1.8 parts of a waterproofing agent, 20-28 parts of water, 0.6-2.6 parts of a water-reducing agent and 0.1-0.32 part of sludge. The anti-cracking concrete is high in strength, good intoughness, anti-cracking and long in service life.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a crack-resistant concrete. Background technique [0002] Concrete is the largest construction material today, and high-performance concrete represents the development direction of concrete technology. In recent years, with the vigorous development of the domestic construction industry, the requirements for the strength and crack resistance of the concrete consumed in the construction process have been continuously improved. Cracks, the appearance and expansion of cracks will reduce the performance, shorten the life, and limit its application. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes an anti-cracking concrete, which has high strength, good toughness, anti-cracking and long service life. [0004] A kind of anti-cracking concrete proposed by the present invention, its raw material c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B111/34
CPCC04B28/00C04B2111/343C04B2201/50C04B14/06C04B18/023C04B14/48C04B16/0616C04B16/06C04B18/248C04B14/043C04B14/304C04B18/146C04B14/047C04B14/28C04B18/12C04B18/142C04B14/303C04B24/281C04B24/085C04B2103/302C04B18/0418
Inventor 袁保强
Owner 蚌埠市方阵商品混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap