A kind of nano-modified PVC composite foam material and preparation method thereof

A composite foaming and nano-modification technology, applied in the field of nano-modified PVC composite foaming materials and their preparation, can solve the problems of insufficient toughness, poor processing performance, insufficient strength of PVC materials, etc., and achieve easy processing, good toughness, Effect of flexural strength and tensile strength improvement

Active Publication Date: 2021-02-12
常州爱特恩新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved in the present invention is to provide a kind of nano-modified PVC composite foaming material and its preparation method, by adding composite nano-modifier, coordinating filler, foaming agent, lubricant, stabilizer and other processing aids, Prepare a PVC composite foam material with high strength, good toughness and excellent processing performance to solve the technical problems of insufficient strength, insufficient toughness and poor processing performance of existing PVC materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The blowing agent of embodiment 1 is azodimethylamide; The blowing agent of embodiment 2 is the mixture (weight ratio 1:1) of barium azodicarboxylate and dinitrosopentamethylenetetramine; Implementation The blowing agent in Example 3 is a mixture of carbonamide, p-methylsulfonamide and 2,2'-azobisisobutyronitrile (weight ratio 1:1:1); the blowing agent in Example 4 It is a mixture of azodimethylamide, 4,4'-oxidized bisbenzenesulfonyl hydrazide and sodium bicarbonate (weight ratio 1:0.5:1); the foaming agent in Example 5 is azodimethylamide , a mixture of barium azodicarboxylate, dinitrosopentamethylenetetramine, carbonamide and p-methylsulfonamide (weight ratio 1:0.5:0.5:0.5:1:0.5);

[0034] The lubricant in Example 1 is metal soap salt; the lubricant in Example 2 is a mixture of metal soap salt and oxidized polyethylene wax (weight ratio 1:1); the lubricant in Example 3 is metal soap salt, oxidized polyethylene wax A mixture of ethylene wax and stearate (weight ratio ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-modified PVC composite foaming material. The raw materials include the following components in parts by weight: 80-100 parts of polyvinyl chloride resin; 10-25 parts of short glass fiber; 2-12 parts of composite nano-modifier ; 0.4-6 parts of foaming agent; 1-6 parts of lubricant; 1-5 parts of stabilizer; 0.5-1.2 parts of processing aid. The PVC composite foam material prepared by the invention has the characteristics of high strength, good toughness and excellent processing performance, which solves the technical problems of insufficient strength, insufficient toughness and poor processing performance of existing PVC materials, and can be widely used in high-speed rail and automobile interior decoration parts, daily necessities, home building materials, packaging, advertising decoration and other fields.

Description

technical field [0001] The invention relates to the technical field of polymer material modification, in particular to a nano-modified PVC composite foaming material and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) resin is a polar non-crystalline high polymer, its products have good physical and chemical properties, and can be widely used in the fields of industry, construction, agriculture and daily necessities. At present, furniture and building materials products with PVC resin as the main raw material have become the second pillar of my country's plastics industry, with an average annual growth rate of more than 15%. This is due to the advantages of low cost, excellent performance and recyclable recycling of PVC composite materials, which is in line with the general trend of environmental sustainable development and circular economy. [0003] Due to the superior performance of PVC materials and the protection of the environment, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08K9/04C08K3/34C08K3/22C08J9/10C08J9/08
CPCC08J9/0066C08J9/009C08J9/08C08J9/10C08J9/102C08J9/103C08J9/105C08J9/107C08J2203/02C08J2203/04C08J2327/06
Inventor 杜崇铭
Owner 常州爱特恩新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com