Moisture-proof coating material for power supply equipment, and preparation method thereof

A technology for moisture-proof coatings and power equipment, applied in fire-resistant coatings and other directions, can solve the problems of complex preparation methods, general moisture-proof performance, and high raw material costs, and achieve the effects of high gloss, good moisture-proof effect, and long coating life.

Inactive Publication Date: 2019-01-25
HEFEI SHANGQIANG ELECTRIC TECH CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The moisture-proof coatings provided by the above two existing technologies have general moisture-proof performance, narrow application range, complex preparation methods, and high raw material costs, and are not suitable for industrialized large-scale promotion and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A moisture-proof coating for power equipment, comprising the following raw materials in parts by weight: 10 parts of modified acrylic resin, 9 parts of zinc oxide, 5 parts of calcium oxide, 10 parts of nano-titanium dioxide, 4 parts of hygroscopic filler, and 10 parts of polysiloxane resin 13 parts of silicone resin, 7 parts of amino resin, 9 parts of aminopropyltriethoxysilane, 5 parts of polyurethane emulsion, 11 parts of diatomaceous earth powder, 4 parts of polyethylene glycol, 3 parts of sucrose acetate isobutyrate 6 parts, 6 parts of thickener, 2 parts of stabilizer, 3 parts of wetting agent and 5 parts of auxiliary agent.

[0031] A preparation method for a moisture-proof coating for power equipment, comprising the following preparation steps:

[0032] a. Mix modified acrylic resin, zinc oxide, calcium oxide and nano-titanium dioxide into the reaction kettle, heat and stir at 110°C for 1.1h, then cool down to 85°C, then add hygroscopic fillers, at a speed of 150r...

Embodiment 2

[0043] A moisture-proof coating for power equipment, comprising the following raw materials in parts by weight: 12 parts of modified acrylic resin, 8 parts of zinc oxide, 8 parts of calcium oxide, 7 parts of nano-titanium dioxide, 5 parts of hygroscopic filler, and 7 parts of polysiloxane resin Parts, 11 parts of silicone resin, 7 parts of amino resin, 9 parts of aminopropyltriethoxysilane, 9 parts of polyurethane emulsion, 8 parts of diatomaceous earth powder, 6 parts of polyethylene glycol, 7 parts of sucrose acetate isobutyrate 4 parts, 4 parts of thickener, 5 parts of stabilizer, 5 parts of wetting agent and 4 parts of auxiliary agent.

[0044] A preparation method for a moisture-proof coating for power equipment, comprising the following preparation steps:

[0045] a. Mix the modified acrylic resin, zinc oxide, calcium oxide and nano-titanium dioxide into the reaction kettle, heat and stir at 114°C for 1.3h, then cool down to 90°C, then add hygroscopic filler, at a speed ...

Embodiment 3

[0056] A moisture-proof coating for power equipment, comprising the following raw materials in parts by weight: 13 parts of modified acrylic resin, 7 parts of zinc oxide, 7 parts of calcium oxide, 8 parts of nano-titanium dioxide, 8 parts of hygroscopic filler, and 9 parts of polysiloxane resin Parts, 12 parts of silicone resin, 9 parts of amino resin, 8 parts of aminopropyltriethoxysilane, 6 parts of polyurethane emulsion, 9 parts of diatomaceous earth powder, 5 parts of polyethylene glycol, 5 parts of sucrose acetate isobutyrate 5 parts, 5 parts of thickener, 4 parts of stabilizer, 4 parts of wetting agent and 5 parts of auxiliary agent.

[0057] A preparation method for a moisture-proof coating for power equipment, comprising the following preparation steps:

[0058] a. Mix the modified acrylic resin, zinc oxide, calcium oxide and nano-titanium dioxide into the reaction kettle, heat and stir at 110°C for 1.3h, then cool down to 90°C, then add hygroscopic filler, at a speed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a moisture-proof coating material for power supply equipment, and a preparation method thereof, wherein the moisture-proof coating material is prepared from a modified acrylic resin, zinc oxide, calcium oxide, nanometer titanium dioxide, a moisture absorbing filler, a polysiloxane resin, an organosilicon resin, an amino resin, aminopropyl triethoxysilane, a polyurethane emulsion, diatomaceous earth powder, polyethylene glycol, sucrose acetate isobutyrate, a thickener, a curing agent, a wetting agent and an auxiliary agent. According to the present invention, the preparedcoating material has characteristics of strong chemical resistance, good water resistance, good moisture resistance, high gloss, long service life of coating film and the like, can effectively hinderthe condensation of water vapor, can prevent the surface of power supply equipment from being oxidized, can maintain good thermal insulation performance in a humid environment for a long time, and further has good performances of high temperature resistance, weather resistance, ultraviolet ray aging resistance and the like.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a moisture-proof coating for power supply equipment and a preparation method thereof. Background technique [0002] In today's society where information is developing rapidly, power supply equipment is an indispensable daily necessities for people. Power supply equipment includes mobile phones, computers, network cards, radios and so on. Coatings for power supply equipment must have excellent electrical conductivity, impact resistance, moisture resistance, flexibility, etc. However, most of the existing coatings for power supply equipment focus on their electrical conductivity, impact resistance and corrosion resistance, etc., but the moisture-proof performance is not high, and there are few developments and productions of moisture-proof coatings applied to power supply equipment. If the power supply equipment is operated in a humid environment for a long time, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/61C09D7/63C09D7/65C09D7/44
CPCC09D133/04C08K2003/282C08K2201/011C08K2201/014C08L2201/08C08L2203/20C08L2205/02C08L2205/025C08L2205/035C09D5/18C09D7/44C09D7/61C09D7/63C09D7/65C09D7/70C08L83/04C08L61/20C08L83/12C08K13/04C08K3/28C08K7/08C08K7/24C08K5/544
Inventor 程劲松
Owner HEFEI SHANGQIANG ELECTRIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap