Matte brick and preparation method

A soft light brick and soft light technology, which is applied in the field of ceramic tile preparation, can solve problems such as troublesome tile stain resistance, affecting surface decoration patterns, etc., and achieves broad application prospects, good color development, and the effect of reducing light pollution

Inactive Publication Date: 2019-01-29
肇庆乐华陶瓷洁具有限公司
View PDF6 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Another improved process is the method of soft polishing, which can produce marble tiles with a gloss of about 50 degrees, but there is still a lot of gap with the gloss of natural marble.
[0004] On the other hand, most of the anti-skid tiles commonly used at present are provided with wrinkle stripes or concave-convex points on the brick surface to increase the friction between the floor tile surface and the soles of the human body or soles, so as to prevent slipping and falling. Grooves or ridges are set on the surface of the tiles to increase friction, but this method reduces the stain resistance of the tiles; as an improved technology, Chinese application CN201810023625.8 discloses the use of corrosive agents to corrode the tile surface to increase Anti-slip property, but this requires an additional process, which is troublesome, and the surface decoration pattern will be affected when corroded

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The invention provides a method for preparing soft light bricks, comprising:

[0036] (1) Prepare green body, bottom glaze slurry, surface glaze slurry and inkjet ink respectively;

[0037] Wherein, there are no special restrictions on the specific formula of the green body and the raw materials used, and those skilled in the art can choose according to the corresponding production situation; preferably, the formula of the green body is adopted, and the thermal expansion coefficient of the green body is the same as that of the glaze of the present invention. Fit to ensure that glaze cracking defects do not occur.

[0038] Preferably, the step of preparing green body comprises:

[0039] A) prepare powder and pigment respectively;

[0040] Specifically, it includes: preparing raw materials according to the formula of the green body, ball milling, spraying granulation, and obtaining powder after aging;

[0041] B) fully mixing the powder and the colorant to obtain a mix...

Embodiment 1

[0089] (1) Prepare green body, bottom glaze slurry, surface glaze slurry and inkjet ink respectively;

[0090] Bottom glaze paste formula: 29 parts of potassium feldspar, 20 parts of calcined alumina, 6 parts of kaolin, 8 parts of wollastonite, 4 parts of dolomite, 5 parts of calcined kaolin, 32 parts of high-temperature frit; chemical composition of bottom glaze paste For: SiO 2 54.14%, Al 2 o 3 31.33%, Fe 2 o 3 0.18%, TiO 2 0.08%, CaO 0.92%, MgO 0.05%, K 2 O 4.21%, Na 2 O 3.55%; the balance is impurities. The 325-mesh sieve of the bottom glaze is 0.78%, the specific gravity is 1.85g / mL, and the flow rate is 33 seconds.

[0091] The formula of the surface glaze slurry is: 28 parts of albite, 4 parts of calcined zinc oxide, 5 parts of wollastonite, 9 parts of dolomite, 5.5 parts of calcined talc, 9 parts of barium carbonate, 10 parts of strontium carbonate, 6 parts of kaolin, calcined 4 parts of kaolin, 15 parts of transparent frit; Among them, the composition of t...

Embodiment 2

[0105] (1) Prepare green body, bottom glaze slurry, surface glaze slurry and inkjet ink respectively;

[0106] Bottom glaze paste formula: 28 parts of potassium feldspar, 17 parts of calcined alumina, 8 parts of kaolin, 5 parts of wollastonite, 3 parts of dolomite, 6 parts of calcined kaolin, 34 parts of high-temperature frit; chemical composition of bottom glaze paste For: SiO 2 53.34%, Al 2 o 3 29.38%, Fe 2 o 3 0.26%, TiO 2 0.07%, CaO 0.67%, MgO 0.14%, K 2 O 3.87%, Na 2 O 4.2%; the balance is impurities. The 325-mesh sieve of the bottom glaze is 0.58%, the specific gravity is 1.86g / mL, and the flow rate is 33 seconds.

[0107] The formula of the surface glaze slurry is: 29 parts of albite, 3.5 parts of calcined zinc oxide, 6 parts of wollastonite, 9 parts of dolomite, 7.5 parts of calcined talc, 8 parts of barium carbonate, 7 parts of strontium carbonate, 7.5 parts of kaolin, calcined 5 parts of kaolin, 18 parts of transparent frit; Among them, the composition of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
glossaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a matte brick. The preparation method comprises the steps: preparing ground glaze, decorative patterns and surface glaze on the surface of a green bodysequentially, then performing drying and firing, performing polishing by using a matte grinding block and a fiber grinding block sequentially, and performing wax so as to obtain the matte brick finished product. The matte brick with a glossiness of 28-36 degrees is prepared through adoption of a reasonable surface glaze formula and a polishing technology, and the decorative patterns have good color and clear patterns, so that the brick is more similar to natural marble; and light reflection and light pollution are reduced through the brick, and broad application prospects are achieved.

Description

technical field [0001] The invention belongs to the field of ceramic tile preparation, in particular to a soft light tile and a preparation method thereof. Background technique [0002] Marble tiles refer to a class of ceramic tile products with realistic texture, color, transparency and texture of natural marble, which have realistic decorative effects of natural marble and superior performance of ceramic tiles. Compared with other ceramic tiles, marble tiles must achieve the realistic effect of natural marble in terms of texture, color, transparency, texture and feel while pursuing superior practical performance. Therefore, it is difficult to improve its practical performance. Much higher than other tile categories. [0003] Most of the existing marble tiles are produced by a production process similar to full-glazing, that is, cloth-pressing-bottom glaze-inkjet printing-top glaze-polishing; but the surface gloss of this type of marble tiles is too high. High, can reach ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89C03C8/20
CPCC03C8/20C04B41/52C04B41/89C04B41/5022C04B41/4535C04B41/4543C04B41/478
Inventor 谢岳荣霍振辉徐鹏飞钟鹏胡巧丽徐鑫
Owner 肇庆乐华陶瓷洁具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More