Novel environment-friendly glass powder with nano-metal oxide and preparation method thereof

A nano-metal and oxide technology, applied in the field of new environmentally friendly glass powder and its preparation, can solve problems such as health damage, polluted soil and groundwater, and achieve the effects of convenient operation, simple preparation process, and broad market development prospects

Inactive Publication Date: 2019-02-22
江西合创光电技术有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Lead-containing glass will also cause health damage through contact with human skin or inhalation through the respiratory tract during use; similarly, lead glass will also pollute soil and groundwater after being discarded

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Raw material composition is by mass percentage:

[0043]Bi2O3 is 69%, ZnO is 7.2%, B2O3 is 7.7%, Sb2O3 is 2.5%, SiO2 is 1.5%, Al2O3 is 1.5%, TiO2 is 1.5%, CaO is 1%, MgO is 1%, BaO is 2.1%, Na2O is 0.5%, K2O is 0.5%, Li2O is 0.5%, Y2O3 is 1.5%, and SrO is 2%.

[0044] Raw material introduction

[0045] All raw materials except Al2O3 are chemically pure grade raw materials, among which Bi2O3, ZnO, Sb2O3, SiO2, TiO2 are introduced as oxides, B2O3 is introduced as boric acid, CaO, MgO, BaO, Na2O, K2O, Li2O are all introduced as carbonate Form introduction, Y2O3 is introduced by nano-yttrium oxide with an average particle size of 30nm, and SrO is introduced by nano-strontium oxide with an average particle size of 20nm.

[0046] Preparation

[0047] The first step, take each raw material according to the mass percentage of each component;

[0048] The second step is to fully mix the weighed raw materials, wherein nano-yttrium oxide and nano-strontium oxide are finally ad...

Embodiment 2

[0056] Raw material composition is by mass percentage:

[0057] Bi2O3 is 64%, ZnO is 7%, B2O3 is 11%, Sb2O3 is 1.5%, SiO2 is 2.5%, Al2O3 is 2%, TiO2 is 1%, CaO is 1%, MgO is 2%, BaO is 3.8%, Na2O is 0.7%, K2O is 0.5%, Li2O is 0.5%, Y2O3 is 1.5%, and SrO is 1%.

[0058] Raw material introduction

[0059] All raw materials except Al2O3 are chemically pure grade raw materials, among which Bi2O3, ZnO, Sb2O3, SiO2, TiO2 are introduced as oxides, B2O3 is introduced as boric acid, CaO, MgO, BaO, Na2O, K2O, Li2O are all introduced as carbonate Form introduction, Y2O3 is introduced by nano-yttrium oxide with an average particle size of 30nm, and SrO is introduced by nano-strontium oxide with an average particle size of 20nm.

[0060] Preparation

[0061] The first step, take each raw material according to the mass percentage of each component;

[0062] The second step is to fully mix the weighed raw materials, wherein nano-yttrium oxide and nano-strontium oxide are finally added an...

Embodiment 3

[0070] Raw material composition is by mass percentage:

[0071] Bi2O3 is 73%, ZnO is 8.2%, B2O3 is 5%, Sb2O3 is 2%, SiO2 is 2%, Al2O3 is 1%, TiO2 is 1%, CaO is 0.5%, MgO is 0.5%, BaO is 2%, Na2O is 0.5%, K2O is 0.8%, Li2O is 0.5%, Y2O3 is 1%, and SrO is 2%.

[0072] Raw material introduction

[0073] All raw materials except Al2O3 are chemically pure grade raw materials, among which Bi2O3, ZnO, Sb2O3, SiO2, TiO2 are introduced as oxides, B2O3 is introduced as boric acid, CaO, MgO, BaO, Na2O, K2O, Li2O are all introduced as carbonate Form introduction, Y2O3 is introduced by nano-yttrium oxide with an average particle size of 30nm, and SrO is introduced by nano-strontium oxide with an average particle size of 20nm.

[0074] Preparation

[0075] The first step, take each raw material according to the mass percentage of each component;

[0076] The second step is to fully mix the weighed raw materials, wherein nano-yttrium oxide and nano-strontium oxide are finally added and m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of high-temperature coatings, in particular to novel environment-friendly glass powder added with nano-metal oxide and used for a high-temperature coatingand a preparation method thereof. In the novel environment-friendly glass powder, according to mass percent, Bi2O3 is 60-85%, ZnO is 5-20%, B2O3 is 5-30%, Sb2O3 is 0.5-5%, SiO2 is 1-10%, Al2O3 is 1-10%, TiO2 is 0.5-3%, CaO is 0.5-8%, MgO is 0.5-10%, BaO is 0.5-10%, Na2O is 0-5%, K2O is 0-5%, Li2O is 0-5%, Y2O3 is 0.5-5%, SrO is 0.5-5%. The low-temperature lead-free environment-friendly glass powder does not contain lead oxide, has low softening point, good adhesion, good chemical stability and strong moisture resistance, and can be used for high-temperature resistant coatings.

Description

technical field [0001] The invention relates to a nano-metal oxide added for high-temperature coatings, in particular to a novel environment-friendly glass powder added with nano-metal oxides for high-temperature coatings and a preparation method thereof. Background technique [0002] At present, most of the low-melting glass powders used in high-temperature coatings are lead-containing glass powders, such as PbO-B 2 o 3 -SiO 2 system or PbO-ZnO-B 2 o 3 Department of glass. The softening temperature of these glasses is less than 400°C, and the coefficient of thermal expansion is 90-100×10 -7 / ℃, good chemical stability, good deliquescence resistance. However, the lead oxide content in the glass powder is 30-80wt%, which belongs to high-lead glass. When lead-containing glass is produced, about 10-12wt% PbO enters the atmosphere through volatilization or condenses into fine dust and falls to the ground, causing pollution to the atmosphere, soil, rivers, etc. Lead-cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C12/00
CPCC03C12/00
Inventor 裘慧广李剑吕步云包卫锋
Owner 江西合创光电技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More