A kind of antistatic polyester alloy material and preparation method thereof

A polyester alloy and antistatic technology, which is applied in the field of antistatic polyester alloy materials and its preparation, can solve the problems of reducing the amount of conductive carbon black, etc., and achieve the goal of reducing the amount of addition, ensuring stability, and uniform and stable surface resistance Effect

Active Publication Date: 2021-02-02
GUANGDONG KUMHO SUNNY POLYMER MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Another object of the present invention is to propose a method for preparing an antistatic polyester alloy material, which can overcome problems such as delamination and bridging during the blanking process of conductive carbon black, and greatly reduce the amount of conductive carbon black added

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antistatic polyester alloy material and preparation method thereof
  • A kind of antistatic polyester alloy material and preparation method thereof
  • A kind of antistatic polyester alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028]Example 1-A method for preparing an antistatic polyester alloy material, including the following steps:

[0029](1) Prepare conductive particles, mix conductive carbon black and silicone oil for 20 minutes to obtain granular conductive particles; the conductive carbon black has a chain structure with an average particle size of 150nm; the silicone oil has a density of 0.96 Methyl silicone oil;

[0030](2) Add polybutylene terephthalate, polycarbonate, conductive particles, toughening agent, antioxidant, and lubricant to a high-speed mixer and mix to obtain a mixed composition; wherein, the polymer is The viscosity of butylene phthalate is 0.45dl / gr; the weight average molecular weight of the polycarbonate is 25000; the toughening agent is MBS resin with a particle diameter of 300nm; the lubricant is silicone powder;

[0031](3) The mixed composition of step (2) is fed into the twin-screw extruder from the feed port, and a telescopic steel ball with a diameter of 30 cm is set at the mai...

Embodiment 2

[0032]Example 2-A preparation method of an antistatic polyester alloy material, including the following steps:

[0033](1) Prepare conductive particles, mix conductive carbon black and silicone oil for 30 minutes to obtain granular conductive particles; the conductive carbon black has a chain structure with an average particle size of 150nm; the silicone oil has a density of 0.96 Methyl silicone oil;

[0034](2) Add polybutylene terephthalate, polycarbonate, conductive particles, toughening agent, antioxidant, and lubricant to a high-speed mixer and mix to obtain a mixed composition; wherein, the polymer is The viscosity of butylene phthalate is 1.2 dl / gr; the weight average molecular weight of the polycarbonate is 40,000; the toughening agent is an MBS resin with a particle size of 600 nm; the lubricant is pentaerythritol ester;

[0035](3) Feed the mixed composition of step (2) into a twin-screw extruder, and use a telescopic steel ball with a diameter of 30cm set at the main discharge por...

Embodiment 3

[0036]Example 3-A method for preparing an antistatic polyester alloy material, including the following steps:

[0037](1) Prepare conductive particles, mix conductive carbon black and silicone oil for 25 minutes to obtain granular conductive particles; the conductive carbon black has a chain structure with an average particle size of 150nm; the silicone oil has a density of 0.96 Methyl silicone oil;

[0038](2) Add polybutylene terephthalate, polycarbonate, conductive particles, toughening agent, antioxidant, and lubricant to a high-speed mixer and mix to obtain a mixed composition; wherein, the polymer is The viscosity of butylene phthalate is 0.85dl / gr; the weight average molecular weight of the polycarbonate is 35000; the toughening agent is MBS resin with a particle size of 500nm; the lubricant is ethylene double hard Ester amide

[0039](3) Feed the mixed composition of step (2) into a twin-screw extruder, and use a telescopic steel ball with a diameter of 30cm set at the main discharge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

An antistatic polyester alloy material and a preparation method thereof, the polyester alloy material comprises the following components according to the weight ratio: 30-50 parts of polybutylene terephthalate, 50-70 parts of polycarbonate 2.1 to 11 parts of conductive particles, 3 to 15 parts of toughening agent, 0.1 to 1 part of antioxidant and 0.2 to 1 part of lubricant. The conductive particles are composed of 2 to 10 parts of conductive carbon black and 0.1 to 1 part of Granular conductive particles formed by banburying silicone oil, the antistatic polyester alloy material prepared by the present invention has a uniform and stable surface resistance, and can overcome the problems of delamination and bridging during the blanking process of conductive carbon black , greatly reducing the amount of conductive carbon black added.

Description

Technical field[0001]The invention relates to the technical field of polymer material processing, in particular to an antistatic polyester alloy material and a preparation method thereof.Background technique[0002]At present, in home appliances and industrial application scenarios, it is easy to absorb dust when the fan blades, electrical appliances and other equipment are placed and operated. The accumulation of dust for a long time will cause the appearance of dust, which affects the appearance, is difficult to clean, and can also cause poor operation , The problem of attenuation of the damaged life of electrical appliances, so in order to be able to effectively prevent dust, the surface resistance of the material needs to be as high as 10^8-9.[0003]As a high-quality conductive filler, conductive carbon black can change the surface resistance of the substrate. However, because the bulk density of conductive carbon black is quite different from that of powder and granular materials,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L67/02C08L83/04C08K3/04B29C48/285B29C48/92
CPCC08K2201/001C08L69/00C08L2201/04C08L2205/03C08L67/02C08L83/04C08K3/04
Inventor 王璐辛敏强洪浩王正磊
Owner GUANGDONG KUMHO SUNNY POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com