Bulk doped diamond-base normally-off field effect transistor and preparation method thereof

A technology of field effect transistors and diamonds, applied in the direction of transistors, semiconductor/solid-state device manufacturing, semiconductor devices, etc., can solve the problems of channel electrical performance degradation and disappearance, and achieve non-degradation of working characteristics and strong carrier depletion ability Effect

Active Publication Date: 2019-02-22
XI AN JIAOTONG UNIV
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The body-doped diamond-based normally-off field effect transistor of the present invention utilizes the high Schottky barrier produced by the sidewall of the etching region and the gate metal and the Schottky barrier produced by the surface of the channel region and the gate metal. The effect completely depletes the carriers under the gate (in the channel), causing the conductive channel to be pinched off, so that the device shows normally-off characteristics; the two-dimensional hole gas of the hydrogen-terminated diamond is replaced by bulk-doped diamond as the conductive channel It can solve the problem of the degradation or even disappearance of the electrical properties of the two-dimensional hole gas channel under high temperature or oxygen environment, and can also improve the electrical characteristics of the transistor, such as breakdown field strength and current density.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bulk doped diamond-base normally-off field effect transistor and preparation method thereof
  • Bulk doped diamond-base normally-off field effect transistor and preparation method thereof
  • Bulk doped diamond-base normally-off field effect transistor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A method for preparing a bulk-doped diamond-based normally-off field-effect transistor, comprising the following steps:

[0052] 1) The diamond substrate 1 grown by high temperature and high pressure (HPHT) technology is cleaned successively by using the standard cleaning process for diamond substrates, followed by inorganic and organic cleaning, and blown dry with nitrogen gas for later use.

[0053] 2) Deposit a single crystal diamond film 2 on the cleaned diamond substrate using microwave plasma vapor chemical deposition (MPCVD), the plasma power is 1kW, the chamber pressure is 100Torr, and the total gas flow is 500sccm, and the obtained single crystal diamond The thickness of the film is 1μm, the resistivity is greater than 100MΩ·cm, the root mean square surface roughness is less than 0.5nm, and the half-peak width of the Raman curve is less than 2cm -1 , XRD rocking curve half width less than 30arcsec.

[0054] 3) The diamond sample remains in the MPCVD chamber, t...

Embodiment 2

[0059] A method for preparing a bulk-doped diamond-based normally-off field-effect transistor, comprising the following steps:

[0060] 1) The diamond substrate 1 grown by high temperature and high pressure (HPHT) technology is cleaned successively by using the standard cleaning process for diamond substrates, followed by inorganic and organic cleaning, and blown dry with nitrogen gas for later use.

[0061] 2) Deposit a single crystal diamond film 2 on the cleaned diamond substrate using microwave plasma vapor chemical deposition (MPCVD), the plasma power is 1kW, the chamber pressure is 100Torr, and the total gas flow is 500sccm, and the obtained single crystal diamond The thickness of the film is 1μm, the resistivity is greater than 100MΩ·cm, the root mean square surface roughness is less than 0.5nm, and the half-peak width of the Raman curve is less than 2cm -1 , XRD rocking curve half width less than 30arcsec.

[0062] 3) The diamond sample is taken out and placed in a DC...

Embodiment 3

[0067] A method for preparing a bulk-doped diamond-based normally-off field-effect transistor, comprising the following steps:

[0068] 1) The diamond substrate 1 grown by high temperature and high pressure (HPHT) technology is cleaned successively by using the standard cleaning process for diamond substrates, followed by inorganic and organic cleaning, and blown dry with nitrogen gas for later use.

[0069] 2) Deposit a single crystal diamond film 2 on the cleaned diamond substrate using microwave plasma vapor chemical deposition (MPCVD), the plasma power is 1kW, the chamber pressure is 100Torr, and the total gas flow is 500sccm, and the obtained single crystal diamond The thickness of the film is 1μm, the resistivity is greater than 100MΩ·cm, the root mean square surface roughness is less than 0.5nm, and the half-peak width of the Raman curve is less than 2cm -1 , XRD rocking curve half width less than 30arcsec.

[0070] 3) The diamond sample is taken out and placed in the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
surface roughnessaaaaaaaaaa
carrier mobilityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bulk doped diamond-base normally-off field effect transistor and a preparation method thereof. The bulk doped diamond-base normally-off field effect transistor comprises a diamond substrate; a single crystal diamond epitaxial film is disposed on the diamond substrate; a bulk doped single crystal epitaxial film and an etched region are disposed on the single crystal diamond epitaxial film; the etched region is a high Schottky barrier terminal; the bulk doped single crystal epitaxial film is provided with a channel region; the channel region includes a bulk doped singlecrystal epitaxial film as a conductive channel and is a low Schottky barrier terminal; a source electrode and a drain electrode are arranged on both sides of the channel region; and a gate electrodeis disposed in the etched region and the channel region between the source electrode and the drain electrode. The normally-off field effect transistor uses a bulk doped epitaxial single crystal diamond material as the conductive channel so as to exert the advantages of high temperature resistance, radiation resistance and capability of operating in a vicious environment of a diamond material.

Description

Technical field [0001] The invention belongs to the technical field of semiconductor devices, and particularly relates to a normally-off diamond-based field effect transistor and a preparation method thereof. Specifically, it relates to a body-doped diamond-based normally-off field-effect transistor and a preparation method thereof. Background technique [0002] Semiconductor single crystal materials have gone through four generations of development. The first generation of Si and Ge semiconductors brought mankind into the information age, and also promoted the intelligence and informatization of electronic systems. The second generation of semiconductors (GaAs, InP, MCT, etc.) has brought us optoelectronic devices, power electronic devices, radio frequency electronic devices and space anti-radiation devices, etc., triggering revolutions in the information fields such as wireless communications and optical communications. The third generation of wide bandgap semiconductors ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L27/095H01L29/16H01L29/167H01L21/338H01L29/812
CPCH01L27/095H01L29/1602H01L29/167H01L29/66045H01L29/8126
Inventor 王玮王宏兴问峰王艳丰张明辉林芳张景文卜忍安侯洵
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com