Anti-fouling and cigarette scald resistant agent UV (ultraviolet) coating of PVC (polyvinyl chloride) floor

A technology of smoke ironing agent and flooring, which is applied in antifouling/underwater coatings, epoxy resin coatings, coatings, etc. It can solve problems such as poor wear resistance, poor anti-skid performance, and coatings that cannot withstand high temperatures. Achieve the effect of meeting environmental protection requirements, solving smoke prevention and improving wear resistance

Inactive Publication Date: 2019-03-15
唐山市丰润区米乐感光新材料有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The coating of the existing PVC floor on the market cannot achieve the effect of high temperature resistance. At present, the high temperature resistance can only reach about 200 degrees Celsius; and the temperature of the center of the cigarette butt is as high as 700 ℃ ~ 800 ℃, so the existing PVC floor is difficult to effectively avoid Smoke burning problem; at the same time, the current existing PVC floor has poor wear resistance and poor slip resistance during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A PVC floor anti-fouling anti-smoke scalding agent UV coating, its components and mass percentages are as follows: 40 parts of photosensitive resin; 30 parts of crosslinking agent; 10 parts of photoinitiator; 20 parts of additives.

[0014] The additive is composed of leveling agent, dispersant, wear-resistant powder and ceramic powder; additive components and mass percentages are as follows: leveling agent 11%, dispersant 60%, wear-resistant powder 19%, ceramic powder 10%.

[0015] The preparation method of the photosensitive resin is: mix the prepolymer and the diluent according to the mass ratio of 3:1 and stir evenly, then add the photosensitizer and additives and stir at high speed. The prepolymer is Jiangsu Sanmu product: prepolymer 6105-80; the diluent is Jiangsu Litian product: diluent NPGDA.

[0016] The leveling agent is polyether siloxane acrylate; the dispersant is silicone modified acrylate; the wear-resistant powder is silicon dioxide powder with a finenes...

Embodiment 2

[0018] A PVC floor anti-fouling anti-smoke scalding agent UV coating, its components and mass percentages are as follows: 50 parts of photosensitive resin; 20 parts of crosslinking agent; 9 parts of photoinitiator; 21 parts of additives.

[0019] The additive is composed of leveling agent, dispersant, wear-resistant powder and ceramic powder; additive components and mass percentages are as follows: leveling agent 34%, dispersant 42%, wear-resistant powder 15%, ceramic powder 9%.

[0020] The preparation method of the photosensitive resin is: mix the prepolymer and the diluent according to the mass ratio of 3:1 and stir evenly, then add the photosensitizer and additives and stir at high speed. The prepolymer is Jiangsu Sanmu product: prepolymer 6105-80; the diluent is Jiangsu Litian product: diluent NPGDA.

[0021] The leveling agent is polyether siloxane acrylate; the dispersant is silicone modified acrylate; the wear-resistant powder is silicon dioxide powder with a fineness ...

Embodiment 3

[0023] A PVC floor anti-fouling anti-smoke scalding agent UV coating, its components and mass percentages are as follows: 48 parts of photosensitive resin; 28 parts of crosslinking agent; 10 parts of photoinitiator; 14 parts of additives.

[0024] The additive is composed of leveling agent, dispersant, wear-resistant powder and ceramic powder; additive components and mass percentages are as follows: leveling agent 24%, dispersant 52%, wear-resistant powder 15%, ceramic powder 9%.

[0025] The preparation method of the photosensitive resin is: mix the prepolymer and the diluent according to the mass ratio of 3:1 and stir evenly, then add the photosensitizer and additives and stir at high speed. The prepolymer is Jiangsu Sanmu product: prepolymer 6105-80; the diluent is Jiangsu Litian product: diluent NPGDA.

[0026] The leveling agent is polyether siloxane acrylate; the dispersant is silicone modified acrylate; the wear-resistant powder is silicon dioxide powder with a fineness...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of UV (ultraviolet) coating and particularly relates to an anti-fouling and cigarette scald resistant agent UV (ultraviolet) coating of a PVC (polyvinyl chloride) floor. The coating comprises the following ingredients by weight percentage: 40%-50% of photosensitive resin, 20%-30% of a cross-linking agent, 5%-10% of a photoinitiator and 8%-25% of an additive, wherein the additive comprises a leveling agent, a dispersing agent, a wear-resisting powder and a ceramic powder. Compared with the prior art, by adding the additive, the high temperature resistance strength is greatly improved, and the problem that the PVC floor is scalded by a cigarette is effectively solved; moreover, the wear-resisting strength of the PVC floor is enhanced, and human and material resources for daily cleaning and maintenance are reduced. The coating is a novel material and has the advantages of meeting requirements of environmental protection and effectively avoidingenvironmental protection issues.

Description

technical field [0001] The invention relates to the technical field of UV coatings, in particular to an anti-fouling and anti-smoke scalding agent UV coating for PVC floors. Background technique [0002] PVC floor is a new type of light-weight ground decoration material that is very popular in the world today, also known as light-weight ground material. It is a popular product in Europe, America, Asia, Japan and South Korea. It is popular abroad. It has entered the Chinese market since the early 1980s. It has been widely recognized in large and medium-sized cities in China and is widely used, such as families, hospitals, Schools, office buildings, factories, public places, supermarkets, commercial and other places. [0003] The coating of the existing PVC floor on the market cannot achieve the effect of high temperature resistance. At present, the high temperature resistance can only reach about 200 degrees Celsius; and the temperature of the center of the cigarette butt is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D5/16C09D7/61C09D7/65
CPCC08K2003/2227C08K2201/014C08L2205/03C09D5/1662C09D5/1687C09D163/00C08L83/12C08L83/04C08K3/36C08K3/22
Inventor 李鑫林海江刘立华
Owner 唐山市丰润区米乐感光新材料有限公司