Metal dry granular glaze, preparation method for metal dry granular glaze and preparation method for metal dry granular overglaze dazzle polished brick

A technology of dry granule glaze and metal, which is applied in the field of ceramics, can solve the problems of weak decorative layering, not bright enough color, single metallic feeling, etc., and achieve the effect of delicate hand feeling, good decorative effect, and warm texture of brick body

Inactive Publication Date: 2019-03-29
GUANGDONG OVERLAND CERAMICS CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the metal ceramic tiles produced by the existing technology have a single sense of metal, and the sense of layering of decoration is not strong, and it is not realistic enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The metal glaze comprises the following components in mass fractions: 35% albite, 16% red lead, 12% manganese oxide, 8% quartz, 7% calcium carbonate, 6% clay, 3% zinc oxide, 4% copper oxide %, nickelous oxide 3%, titanium oxide 2%, cobalt oxide 2%.

[0029] Mix the raw materials according to the proportion of the formula, put them into the mixer and mix them evenly, put the mixed raw materials into the pool kiln at 1500-1650 ℃ and melt them to make molten glass; the molten glass flows into a pool with a water temperature of 20-70 ℃ in a columnar shape In the process, the water flow is crushed into particles, and the melt is quenched in water, dried, crushed and sieved to obtain metal dry particles, and the fineness of the sieved metal dry particles is 30-60 mesh.

[0030] Press the ceramic basic mud body, spray or print the glaze layer with decorative effect on the surface of the ceramic tile after drying to form a decorative glaze layer, the decorative glaze layer can ...

Embodiment 2

[0032] The metal glaze comprises the following components in mass fraction: 38% albite, 12% red lead, 14% manganese oxide, 5% quartz, 9% calcium carbonate, 8% clay, 3% zinc oxide, copper oxide 2%, nickel oxide 1%, titanium oxide 5%, cobalt oxide 3%.

[0033] Mix the raw materials according to the proportion of the formula, put them into the mixer and mix them evenly, put the mixed raw materials into the pool kiln at 1500-1650 ℃ and melt them to make molten glass; the molten glass flows into a pool with a water temperature of 20-70 ℃ in a columnar shape In the process, the water flow is crushed into particles, and the melt is quenched in water, dried, crushed and sieved to obtain metal dry particles, and the fineness of the sieved metal dry particles is 30-60 mesh.

[0034] Press the ceramic basic mud body, spray or print the glaze layer with decorative effect on the surface of the ceramic tile after drying to form a decorative glaze layer, the decorative glaze layer can also b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metal dry granular glaze, a preparation method for the metal dry granular glaze and a preparation method for a metal dry granular glaze overglaze dazzle polished brick. The metal dry granular glaze is prepared from the following components in parts by mass: 30-40% of albite, 10-15% of red lead, 10-15% of manganese oxide, 5-10% of quartz, 5-10% of calcium carbonate, 5-10%of clay, 2-5% of zinc oxide, 2-5% of copper oxide, 2-5% of nickel oxide, 1-5% of titanium oxide and 1-5% of cobaltous oxide. The method for preparing the metal dry granular overglaze dazzle polished brick comprises the following steps of B001, preparing metal dry granules; B002, preparing a ceramic tile green body, and spraying or printing a glaze layer with a decoration effect on the surface of aceramic tile so as to form a decorative glaze layer; B003, distributing the metal dry granules prepared in the step B001 on the surface of the ceramic tile, printing a production graph, and then spraying the transparent glaze for polishing on the surface of a brick body; and B004, putting the brick body into a kiln to be sintered, carrying out dazzle polishing on the surface of the brick body byadopting a diamond dazzle polishing technology so as to obtain the metal dry granular overglaze dazzle polished brick.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a metal dry grain glaze and a preparation method thereof, and a preparation method of a metal dry grain surface glazed glazed polished brick. Background technique [0002] Dry granule glaze is a new type of ceramic tile decoration developed and produced through secondary fabric technology. It is widely used in the decoration of ceramic glazed tile products. It has anti-skid and wear-resistant effects. Dry granule glaze is a matte glaze product. It forms an uneven surface on the glazed surface of the ceramic tiles, producing matt and anti-skid effects. When fired at a temperature of 1200 degrees Celsius, the water absorption of the tiles is less than 0.3%, with high density and good wear resistance. Metal ceramic tiles are usually coated with a layer of metal glaze or metal dry particles on the surface of the bricks. After high-temperature sintering, the surface of the ceramic ti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information