Cleaning agent for titanium building material

A technology for detergents and building materials is applied in the field of detergents to achieve the effects of improving washing efficiency, improving cleaning effect and improving surface gloss.

Inactive Publication Date: 2019-04-19
西安庄信新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a cleaning agent for titanium building materials, to solve the problem that the existing cleaning agents for titanium building materials proposed in the above-mentioned background technology generally adopt solvent cleaning, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A cleaning agent for titanium building materials, comprising the following parts by weight: 4 parts by weight of sodium hydroxide, 3 parts by weight of sodium dodecylbenzenesulfonate, 5 parts by weight of N-methylpyrrolidone, and 1 part by weight of higher alcohol , 4 parts by weight of alkylsulfonate, 3 parts by weight of fatty acid polyoxyethylene ether, 2 parts by weight of preservative, 2 parts by weight of defoamer, and 60 parts by weight of deionized water.

[0019] Wherein, described comprises the following steps:

[0020] Step 1: Select sodium hydroxide, sodium dodecylbenzene sulfonate, N-methylpyrrolidone, high-carbon alcohol, alkyl sulfonate, fatty acid polyoxyethylene ether and filter in turn, and mix after removing the agglomerates. Obtain mixed powder, collect and store for future use;

[0021] Step 2: weigh and mix the preservative and deionized water, and send it to the preparation tank for 20 minutes of mixing and stirring at a temperature of 30-35°C to...

Embodiment 2

[0030] A cleaning agent for titanium building materials, comprising the following materials in parts by weight: 6 parts by weight of sodium hydroxide, 4 parts by weight of sodium dodecylbenzene sulfonate, 6 parts by weight of N-methylpyrrolidone, and 2 parts by weight of higher alcohol , 6 parts by weight of alkyl sulfonate, 5 parts by weight of fatty acid polyoxyethylene ether, 3 parts by weight of preservative, 3 parts by weight of defoamer, and 65 parts by weight of deionized water.

[0031] Wherein, described comprises the following steps:

[0032] Step 1: Select sodium hydroxide, sodium dodecylbenzene sulfonate, N-methylpyrrolidone, high-carbon alcohol, alkyl sulfonate, fatty acid polyoxyethylene ether and filter in turn, and mix after removing the agglomerates. Obtain mixed powder, collect and store for future use;

[0033] Step 2: weigh and mix the preservative and deionized water, and send it to the preparation tank for 30 minutes of mixing and stirring at a temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cleaning agent for a titanium building material. A preparation method of the cleaning agent comprises the following steps that 1, sodium hydroxide, sodium dodecyl benzene sulfonate, N-methyl pyrrolidone, high-carbon alcohol, alkane sulfonate and fatty alcohol-polyoxyethy are selected and sequentially sieved and filtered, after cakes are removed, mixing is conducted, so that mixed powder is obtained, and the mixed powder is collected and stored for use; 2, antiseptic and deionized water are weighed, mixed and delivered into a preparation bucket for mixing and stirringtreatment lasting 20-30 minutes at the temperature of 30-35 DEG C, so that an antiseptic solution is obtained; and 3, the mixed powder obtained after treatment in step 1 is added to the antiseptic solution obtained after treatment in step 2, and then, hydrochloric acid is added for a primary high-temperature mixing reaction lasting for 40-50 minutes at the temperature of 70-78 DEG C. In the usingprocess, harmful substances volatilized from the titanium building material are finer compared with existing cleaning agents; the environmental pollution degree is lower; and the cleaning effect of the titanium building material is remarkably improved while the good environment protection performance is achieved.

Description

technical field [0001] The invention belongs to the technical field of detergents, in particular to a detergent for titanium building materials. Background technique [0002] Existing cleaning agents for titanium building materials generally use solvent cleaning and the like. Solvent cleaning mainly utilizes solvent-based cleaning agents for steam cleaning or immersion cleaning with appropriate equipment. However, traditional solvent-based cleaning agents are not only expensive, but also have the disadvantages of being flammable and damaging the skin, and are highly polluting. Contents of the invention [0003] The purpose of the present invention is to provide a cleaning agent for titanium building materials to solve the problem that the existing cleaning agents for titanium building materials generally use solvent cleaning and the like proposed in the background art. Solvent cleaning mainly utilizes solvent-based cleaning agents for steam cleaning or immersion cleaning...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/20
CPCC23G1/205
Inventor 鲁毅罗丽娟孙旭东任怀智郭磊王尧
Owner 西安庄信新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap