Metal foil mounted artistic stone and application method thereof
A technology of metal foil and art stone, applied in the field of art stone, can solve the problems of easy deformation, the formation of air bubbles in metal foil and art stone, and the inability to process the shape of art stone, so as to achieve the effect of improving efficiency and surface hardness.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036] The preparation of the thermosetting epoxy resin binder consists of 10-15 parts of aliphatic epoxy resin, 2-5 parts of phenolic resin, 0.01-1 part of diethylaminopropylamine, and 0.1-0.8 parts of Silane coupling agent, prepared after stirring evenly.
[0037] The surface of the art stone is mounted with metal foil, and the ambient temperature is room temperature 25°C.
[0038] From the stones collected from nature, pre-select stones with complete shape and beautiful shape as art stones; the material of art stones can also be selected from metal, or plastic, or ceramics, or glass, depending on the actual situation of the manufacturer;
[0039] a) Surface cleaning step: clean up the dirt on the surface of the art stone and its holes, rinse the art stone with water, dry or blow dry the art stone to make the surface clean;
[0040] b) Steps of fixing the bracket: choose a support column with external threads on the outside of the bracket, choose a suitable position to inst...
Embodiment 2
[0048] The thermosetting epoxy resin adhesive used in this embodiment consists of an epoxy resin composition and a curing agent composition.
[0049] Epoxy resin composition is made up of the raw material of following mass parts:
[0050] 150 parts of aliphatic epoxy resin, 20 parts of propylene oxide butyl ether, 30 parts of dibutyl phthalate, 4 parts of titanate coupling agent, 10 parts of tar, 15 parts of liquid lard, 30 parts of oxalic acid, 50 parts of meerschaum.
[0051] The curing agent composition is made up of the following raw materials in parts by mass:
[0052] 80 parts of phenolic resin, 20 parts of tris-(dimethylaminomethyl)phenol, 4 parts of titanate coupling agent, 80 parts of sepiolite.
[0053] In parts by mass, 150 parts of aliphatic epoxy resin, 20 parts of propylene oxide butyl ether, 30 parts of dibutyl phthalate, 4 parts of titanate coupling agent, 10 parts of tar, 15 parts of liquid lard Parts, 30 parts of oxalic acid, 50 parts of sepiolite. Stir o...
Embodiment 3
[0067] The art stone with metal foil mounting of the present invention.
[0068] Such as figure 1 with figure 2 As shown, the art stone mounted with metal foil includes the base 10, the support 30 and the art stone 40 on the upper part of the support 30. The art stone 40 is closely bonded to the metal foil 41 coated on the outside by the adhesive 42 coated on the surface. Bonding agent 42 is a thermosetting epoxy resin adhesive.
[0069] The bottom of the art stone 40 is fixed to the support 30 through a resin adhesive, and the base 10 is connected to the support 30 through a screw 20 , so that the art stone 40 can be placed on the base 10 . The resin binder is conventional glue such as acrylic resin glue, and can also be thermosetting resin glue.
[0070] It is also possible that the bracket 30 is provided with threads, and the base 10 is provided with threads that are threadedly engaged with the bracket 30 , so that the bracket 30 is suitable for being screwed with the b...