A technology for thermal insulation coatings and exterior wall insulation, applied in cellulose coatings, glucan coatings, reflective/signal coatings, etc., can solve the problems of low later strength, easy pulverization, affecting the appearance of buildings, etc., and achieve mechanical strength. The effect of increasing and promoting stability

Inactive Publication Date: 2019-05-10
常州蒎圣屋工业自动化技术服务有限责任公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem mainly solved by the present invention is aimed at the disadvantages of poor thermal insulation effect, easy pulverization, and low strength in the later stage of the existing exterior wall thermal insulation coatings, which not only affect the appearance of the building, but also affect the thermal insulation and energy saving effect of the building. , providing a preparation method for exterior wall thermal insulation coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0030] Preparation of the reaction product:

[0031] (1) Weigh the rice straw and put it into a pulverizer for 30 minutes to get crushed rice straw, then put the crushed rice straw into a steam explosion tank, and steam blast it at a pressure of 1.2MPa and a temperature of 200°C for 10 minutes, Get straw blasting products;

[0032] (2) Mix straw blasting waste with β-xylanase, laccase, and water at a mass ratio of 10:1:2:10 and put them into an enzymatic hydrolysis tank. After sealing the enzymatic hydrolysis tank, enzymatically After 6 hours of hydrolysis, after the end of the enzymatic hydrolysis, the enzymatic hydrolysis product was obtained;

[0033] (3) Mix the enzymatic hydrolysis product and potassium permanganate at a mass ratio of 20:1 and put them into a reactor, stir and react at a speed of 200r / min for 20min to obtain a pre-reactant, and then use a concentration of 0.5mol / min L sodium hydroxide solution adjusts the pH of the pre-reaction solution to 7.5, and cont...

example 2

[0040] Preparation of the reaction product:

[0041] (1) Weigh the rice straw and put it into a pulverizer for 35 minutes to get crushed rice straw, then put the rice straw crushed into a steam explosion tank, and steam blast at a pressure of 1.3MPa and a temperature of 210°C for 13 minutes, Get straw blasting products;

[0042] (2) Mix straw blasting waste with β-xylanase, laccase, and water at a mass ratio of 10:1:2:10 and put them into an enzymatic hydrolysis tank. After sealing the enzymatic hydrolysis tank, enzymatically After 7 hours of hydrolysis, after the end of the enzymolysis, the enzymatic hydrolysis product was obtained;

[0043] (3) Mix the enzymatic hydrolysis product and potassium permanganate at a mass ratio of 20:1 and put them into a reactor, stir and react at a speed of 250r / min for 25min to obtain a pre-reactant, and then use a concentration of 0.5mol / min L sodium hydroxide solution adjusts the pH of the pre-reaction solution to 7.8, and continues to sti...

example 3

[0050] Preparation of the reaction product:

[0051] (1) Weigh the rice straw and put it into a pulverizer for 40 minutes to get crushed rice straw, then put the rice straw crushed into a steam explosion tank, and steam blast at a pressure of 1.4MPa and a temperature of 220°C for 15 minutes, Get straw blasting products;

[0052] (2) Mix straw blasting waste with β-xylanase, laccase, and water at a mass ratio of 10:1:2:10 and put them into an enzymatic hydrolysis tank. After sealing the enzymatic hydrolysis tank, enzymatically After 8 hours of hydrolysis, after the end of the enzymolysis, the enzymatic hydrolysis product was obtained;

[0053] (3) Mix the enzymatic hydrolysis product and potassium permanganate at a mass ratio of 20:1 and put them into a reactor, stir and react at a speed of 300r / min for 30min to obtain a pre-reactant, and then use a concentration of 0.5mol / min L sodium hydroxide solution adjusts the pH of the pre-reaction solution to 8.0, and continues to sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method for a heat-insulating coating of an external wall and belongs to the technical field of coating preparation. The preparation method comprises the following steps: taking rice straws as raw material; smashing the rice straws and performing steam explosion treatment; blending exploded fiber and complex enzyme for enzymolysis; performing oxidation and alkali treatment on enzymatic hydrolysate, thereby acquiring a reaction product and standing by; reacting sodium silicate solution with hydrochloric acid, thereby acquiring a reaction liquor; mixing coating emulsion with standby reaction product and reaction liquor, and then adding other auxiliary materials; quickly stirring and reacting, and then rising temperature and reacting, thereby acquiring the heat-insulating coating of the external wall. The heat-insulating coating of the external wall prepared according to the invention has an excellent heat-insulating property, is difficult to pulverize, is high in later strength and has a bright application prospect.

Description

technical field [0001] The invention relates to a preparation method of an exterior wall thermal insulation coating, which belongs to the technical field of coating preparation. Background technique [0002] Today, energy competition is becoming increasingly fierce, and energy issues have become a bottleneck restricting my country's economic development. In order to effectively alleviate energy problems, energy conservation and consumption reduction have been paid more attention to. The use of thermal insulation materials and thermal insulation coatings is one of the important measures for energy conservation. Energy is the premise and foundation for the survival and development of human society, and it provides the driving force for economic development. With the progress and development of science and technology, the contradiction between the increase of energy demand and the relative decrease of energy supply in human society is becoming more and more serious. At present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D189/00C09D183/04C09D101/02C09D105/02C09D5/33D21C5/00
Inventor 陆娜
Owner 常州蒎圣屋工业自动化技术服务有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap