A kind of polyurethane coating for shoe coating and preparation method thereof

A polyurethane coating and coating technology, applied in polyurea/polyurethane coatings, coatings, antifouling/underwater coatings, etc., can solve problems such as difficulty in achieving high transparency and many bubbles, reduce friction coefficient, accelerate aging, The effect of improving work efficiency

Active Publication Date: 2021-03-12
FOSHAN NANHAI QIHONG SHOES MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a polyurethane coating for shoe coating and its preparation method, aiming to overcome the defects of many bubbles and difficulty in achieving high transparency in the existing polyurethane coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyurethane coating for shoe coating and preparation method thereof
  • A kind of polyurethane coating for shoe coating and preparation method thereof
  • A kind of polyurethane coating for shoe coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The present embodiment relates to a kind of preparation method of the polyurethane coating that is used for shoe coating, wherein, comprises the following steps:

[0035] Step (1): Weigh 6kg of isocyanate, 2.5kg of polyester polyol with a molecular weight of 2000, 0.1kg of carbodiimide (water remover) and 1.4kg of propylene carbonate (diluent), add them to the reaction kettle, and stir Uniform, react at 100°C for 7 hours, remove air bubbles in vacuum (-0.095MPa), cool to obtain component A with NCO content of 10.4%;

[0036] Step (2): Weigh 7.0kg of polyester polyol, 2.0kg of 1,4'-butanediol (chain extender), 0.2kg of dibutyltin dilaurate (catalyst) and glycerin of dehydrated potassium aluminum sulfate dodecahydrate Add 0.8kg of the solution into the reaction kettle, stir evenly, and vacuum (-0.095MPa) for 3 hours to remove air bubbles to obtain component B;

[0037] Step (3): Add 8kg of component A to 10kg of component B, mix well, remove air bubbles in vacuum for 30s...

Embodiment 2

[0041] The present embodiment relates to a kind of preparation method of the polyurethane coating that is used for shoe coating, wherein, comprises the following steps:

[0042]Step (1): Weigh 7kg of isocyanate, 2.0kg of polyester polyol with a molecular weight of 2000, 0.5kg of carbodiimide (water remover) and 0.5kg of propylene carbonate (diluent), add them to the reaction kettle, and stir Evenly, react at 90°C for 7 hours, remove air bubbles (-0.095MPa) in vacuum, and cool to obtain component A with an NCO content of 21.3%;

[0043] Step (2): Weigh 7.5kg of polyester polyol, 1.0kg of 1,4'-butanediol (chain extender), 0.3kg of dibutyltin dilaurate (catalyst) and glycerin of dehydrated potassium aluminum sulfate dodecahydrate Add 1.2kg of the solution into the reaction kettle, stir evenly, vacuumize (-0.095MPa) for 2 hours to remove air bubbles, and obtain component B;

[0044] Step (3): Add 8kg of component A to 10kg of component B, mix evenly, remove air bubbles in vacuum ...

Embodiment 3

[0048] The present embodiment relates to a kind of preparation method of the polyurethane coating that is used for shoe coating, wherein, comprises the following steps:

[0049] Step (1): Weigh 6.5kg of isocyanate, 2.2kg of polyester polyol with a molecular weight of 2000, 0.3kg of carbodiimide (water remover) and 1.0kg of propylene carbonate (diluent), and add them to the reaction kettle. Stir evenly, react at 80°C for 8 hours, remove air bubbles (-0.095MPa) in a vacuum, and cool to obtain component A with an NCO content of 16.2%;

[0050] Step (2): Weigh 8.0kg of polyester polyol, 0.9kg of 1,4'-butanediol (chain extender), 0.1kg of dibutyltin dilaurate (catalyst) and glycerin of dehydrated potassium aluminum sulfate dodecahydrate 1.0kg of the solution was added to the reaction kettle, stirred evenly, and vacuumed (-0.095MPa) for 3 hours to remove air bubbles to obtain component B;

[0051] Step (3): Add 8kg of component A to 10kg of component B, mix evenly, remove air bubbl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyurethane coating for shoe coating and a preparation method thereof, wherein the preparation method comprises the following steps: step (1): adding isocyanate, polyester polyol, water remover and diluent in proportion Put it into the reaction kettle, stir evenly, react at 80-120°C for 6-8 hours, remove air bubbles in a vacuum, and cool to obtain component A; step (2): mix polyester polyol, chain extender, catalyst and dehydration Add the glycerol solution of potassium aluminum sulfate dodecahydrate into the reaction kettle in proportion, stir evenly, and vacuumize for 2 to 3 hours to remove air bubbles to obtain component B; step (3): mix component A and component B in proportion Mix evenly, remove air bubbles in vacuum for 30s to obtain polyurethane coating. The prepared polyurethane coating is used for coating on the surface of shoes and can be molded at one time, and solves the known problem that the sprayed polyurethane elastomer reacts with moisture to cause air bubbles inside the coating.

Description

technical field [0001] The invention relates to a polyurethane coating and a preparation method thereof, in particular to a polyurethane coating for shoe coating and a preparation method thereof. Background technique [0002] Conventional footwear usually includes two main components: the upper and the sole structure. Usually, the sole and the upper are made separately. The sole is a dense and wear-resistant material with waterproof performance; the upper is made of leather or fabric. Breathability is guaranteed. However, in traditional shoes, if the height of the sole is too low, water will enter the shoe through the seams and the upper. Rain boots are shoes used in rainy days. The sole and upper of the rain boots are in one form, and the waterproof effect is very good, but The upper is too dense and loses breathability, which is not conducive to outdoor sports. Therefore, there is a need for a shoe upper coating, which can well cover the sole and part of the upper, while...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/06C09D5/14C09D5/16C08G18/66C08G18/42C08G18/32
Inventor 孙维忠陈誉萱孙新远
Owner FOSHAN NANHAI QIHONG SHOES MATERIAL CO LTD