Cleaning and finishing agent and application method thereof

A pore agent and cleaning technology, applied in the direction of chemical instruments and methods, detergent compounding agents, detergent compositions, etc., can solve the problems of high cost of electroless copper plating, increase effective adsorption capacity, reduce pores without copper problem, improve the effect of backlight

Active Publication Date: 2019-05-31
湖南互连微电子材料有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the electroless copper plating process, the cost of activated palladium accounts for about 45%. As a precious metal, palladium is also a high-quality catalyst. More and more stringent, in order to make the backlight meet the requirements, usually can only be achieved by increasing the activation concentration, increasing the thickness of electroless copper plating, etc., making the cost of electroless copper plating remain high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cleaning and finishing agent and application method thereof
  • Cleaning and finishing agent and application method thereof
  • Cleaning and finishing agent and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] 1.1. The formula of the cleaning agent is: sodium gluconate 25g / L, ammonium chloride 4g / L, diethylenetriamine 25g / L, isopropanol 20g / L, non-ionic surfactant TRITON X-100 Be the anionic surfactant 0.2g / L of the alkyl diphenyl ether sulfonate group of 0.4g / L, formula one structure, wherein R is C 12 h 25 ; The rest are deionized water, as shown in Table 1.

[0042]1.2. Take 6 pieces of 5×3cm Shengyi Tg170 substrate boards, remove the copper foil on the board surface with etching solution, then soak in the cleaning agent obtained in 1.1, soak at 50°C for 5 minutes, wash with water, and soak them separately In the ionic palladium activation tank with a standard concentration of 10%, 30%, 50%, 70%, 100%, and 150% at a constant temperature of 45°C (the ionic palladium activation standard solution is: 3 pyridinemethanol 1g / L, palladium chloride 0.15 g / L, adjust PH=9.5), take it out after 5 minutes, wash it with water, soak it in a reducing agent solution (dimethylamine boran...

Embodiment 2

[0046] 2.1. The formula of the cleaning agent is: sodium gluconate 25g / L, ammonium chloride 4g / L, diethylenetriamine 25g / L, isopropanol 20g / L, non-ionic surfactant TRITON X-100 Be the anionic surfactant 0.6g / L of the alkyl diphenyl ether sulfonate group of 0.4g / L, formula one structure, wherein R is C 12 h 25 ; The rest are deionized water, as shown in Table 1.

[0047] 2.2. Take 6 pieces of 5×3cm Shengyi Tg170 substrate boards, remove the copper foil on the board surface with etching solution, then soak in the cleaning agent obtained in 2.1, soak at 50°C for 5min, wash with water, and soak them separately In the ionic palladium activation tank with a standard concentration of 10%, 30%, 50%, 70%, 100%, and 150% at a constant temperature of 45°C (the ionic palladium activation standard solution is: 3 pyridinemethanol 1g / L, palladium chloride 0.15 g / L, adjust PH=9.5), take it out after 5 minutes, wash it with water, soak it in a reducing agent solution (dimethylamine borane 0....

Embodiment 3

[0051] 3.1. The formula of the cleaning agent is: sodium gluconate 25g / L, ammonium chloride 4g / L, diethylenetriamine 25g / L, isopropanol 20g / L, non-ionic surfactant TRITON X-100 Be the anionic surfactant 1.0g / L of the alkyl diphenyl ether sulfonate group of 0.4g / L, formula one structure, wherein R is C 12 h 25 ; The rest are deionized water, as shown in Table 1.

[0052] 3.2. Take 6 pieces of 5×3cm Shengyi Tg170 substrate boards, remove the copper foil on the board surface with etching solution, then soak in the cleaning agent obtained in 2.1, soak for 5 minutes at 50°C, wash with water, and soak them separately In the ionic palladium activation tank with a standard concentration of 10%, 30%, 50%, 70%, 100%, and 150% at a constant temperature of 45°C (the ionic palladium activation standard solution is: 3 pyridinemethanol 1g / L, palladium chloride 0.15 g / L, adjust PH=9.5), take it out after 5 minutes, wash it with water, soak it in a reducing agent solution (dimethylamine bora...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

An embodiment of the invention discloses a cleaning and finishing agent and an application method thereof. The cleaning and finishing agent comprises sodium gluconate, ammonium chloride, polyethylenepolyamine, lower alcohol, a non-ionic surfactant, an anionic surfactant and deionized water. Compared with a cleaning and finishing agent in the prior art, the cleaning and finishing agent has the advantages that the sodium gluconate, ammonium chloride, polyethylene playamine, lower alcohol, non-ionic surfactant, anionic surfactant and deionized water are used to treat the surface of a pore ring of a PCB board, and glass fiber exposed in the surface of the pore ring is cleaned through sodium gluconate and ammonium chloride; the surface of pore ring resin can be treated by polyethylene polyamine; pore walls can be wetted through the lower alcohol and non-ionic surfactant; the resin and glass fiber on the pore ring surface can be modified through the anionic surfactant to enable the surfaceof the pore ring to form high Zeta potential, effective adsorption capacity of a palladium activator is increased, backlight of electroless copper plating is improved, and the situation of hole-without-copper is reduced.

Description

technical field [0001] The present application relates to the technical field of surface treatment, in particular to a cleaning agent for electroless copper plating and a method for using the same. Background technique [0002] Printed circuit board (PCB) has the advantages of high operational reliability, light weight, small size, and easy standardization, and is the core component of almost all electronic equipment. Electroless copper plating process is the key technology of printed circuit metallization. Since the base material of the circuit board is mostly composed of non-conductive materials such as non-conductive resin and glass fiber, the hole wall cannot be plated with metal when the printed circuit is plated. Therefore, the electroplating of the hole wall must first prepare a conductive film. At present, the commonly used method is to first electroless copper plating. [0003] Before electroless copper plating, the substrate must be pre-treated, generally includi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C11D1/83C11D3/20C11D3/04C11D3/30C11D3/60C11D11/00
Inventor 肖开球张新学刘龙平张毅邹银超贺炳祥
Owner 湖南互连微电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com