A method for growing large-scale fega magnetostrictive single crystals with controlled solid-liquid interface

A magnetostrictive, solid-liquid interface technology, applied in the direction of single crystal growth, crystal growth, single crystal growth, etc., can solve the problems of insufficient heat exchange, weakening of one-way heat conduction, etc., to achieve simple process equipment and good comprehensive usability , enhance the effect of one-way heat conduction

Active Publication Date: 2019-09-20
BEIHANG UNIV +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the air gap between the protective shell and the corundum crucible, the heat exchange between the bottom crystal and the cooling liquid is insufficient, and the one-way heat conduction from the solution to the bottom crystal is weakened, causing the solid-liquid interface to change from flat to concave, and the side wall shape appears. Nucleation, formation of heterocrystals, inhibition of single crystal growth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for growing large-scale fega magnetostrictive single crystals with controlled solid-liquid interface
  • A method for growing large-scale fega magnetostrictive single crystals with controlled solid-liquid interface
  • A method for growing large-scale fega magnetostrictive single crystals with controlled solid-liquid interface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Embodiment 1 prepares 30mmFe 81 Ga 19 single crystal

[0046] The steps adopted in this embodiment are as follows:

[0047] 1) Ingredients

[0048] The purity of the selected raw materials Fe and Ga are both 99.99wt%, and in order to prevent the Ga element from burning during the smelting process, the Fe 81 Ga 19 2wt% Ga was added on the basis of the composition. Specifically, 1547.1 g of Fe and 461.8 g of Ga were weighed for use. Before batching, Fe must be ultrasonically cleaned with absolute ethanol and dried under vacuum to remove the oil on the surface.

[0049] 2) Preparation of master alloy ingot

[0050] Put the above-mentioned weighed raw materials Fe and Ga into the crucible of the vacuum non-consumable arc melting furnace. When placing it, it is necessary to place the Ga element that is easy to burn at the bottom of the crucible, and the Fe element that is not easy to burn at the top of the crucible.

[0051] Vacuumize the vacuum non-consumable arc me...

Embodiment 2

[0063] Embodiment 2 prepares 40mmFe 81 Ga 19 single crystal

[0064] The steps adopted in this embodiment are as follows:

[0065] 1) Ingredients

[0066] The purity of the selected raw materials Fe and Ga is greater than 99.99wt%, and in order to prevent the Ga element from burning during the smelting process, the Fe 81 Ga 19 2wt% Ga was added on the basis of the composition. Specifically, 1547.1 g of Fe and 461.8 g of Ga were weighed for use. Before batching, Fe must be ultrasonically cleaned with absolute ethanol and dried under vacuum to remove the oil on the surface.

[0067] 2) Preparation of master alloy ingot

[0068] Put the above-mentioned weighed raw materials Fe and Ga into the crucible of the vacuum non-consumable arc melting furnace. When placing it, it is necessary to place the Ga element that is easy to burn at the bottom of the crucible, and the Fe element that is not easy to burn at the top of the crucible.

[0069] Vacuumize the vacuum non-consumable...

Embodiment 3

[0080] Embodiment 3 prepares 50mmFe 81 Ga 19 single crystal

[0081] The steps adopted in this embodiment are as follows:

[0082] 1) Ingredients

[0083] The purity of the selected raw materials Fe and Ga is greater than 99.99wt%, and in order to prevent the Ga element from burning during the smelting process, the Fe 81 Ga 19 2wt% Ga was added on the basis of the composition. Specifically, 1547.1 g of Fe and 461.8 g of Ga were weighed for use. Before batching, Fe must be ultrasonically cleaned with absolute ethanol and dried under vacuum to remove the oil on the surface.

[0084] 2) Preparation of master alloy ingot

[0085] Put the above-mentioned weighed raw materials Fe and Ga into the crucible of the vacuum non-consumable arc melting furnace. When placing it, it is necessary to place the Ga element that is easy to burn at the bottom of the crucible, and the Fe element that is not easy to burn at the top of the crucible.

[0086] Vacuumize the vacuum non-consumable...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for controlling the growth of a large-size FeGa magnetostrictive single crystal at a solid-liquid interface, comprising the following steps: 1) batching ingredients according to target components; 2) smelting a master alloy with a vacuum non-consumable arc melting furnace; 3) ) using a magnetic levitation induction melting furnace to melt the master alloy ingot and casting it into a master alloy rod; 4) placing the master alloy rod and the FeGa single crystal seed crystal in a double-layer crucible, putting the double-layer crucible into a directional solidification device, and heating The master alloy rod is completely melted and the upper part of the FeGa single crystal seed crystal is melted, and the molten material is pulled along the lower part of the FeGa single crystal seed crystal into the cooling liquid for directional solidification to obtain a large-size FeGa magnetostrictive material. The method has simple process equipment and convenient operation, the saturation magnetic field of the prepared FeGa single crystal is only 500Oe, the magnetostriction coefficient is as high as 300-320ppm, the comprehensive usability is good, and the application prospect is broad.

Description

technical field [0001] The invention relates to the field of single crystal growth, in particular to a method for growing a large-size FeGa magnetostrictive single crystal by controlling a solid-liquid interface. Background technique [0002] The length and volume of ferromagnetic materials and ferrimagnetic materials can change under the action of an external magnetic field due to the change of their own magnetization state. This phenomenon is called magnetostriction, which was discovered by Joule in 1842. Magnetostrictive materials with this effect are important new magnetically driven smart materials, which can realize the mutual conversion of electromagnetic energy and mechanical energy. Magnetostrictive materials have the advantages of high mechanical energy-electromagnetic energy conversion efficiency, high energy density, and high response frequency, and the prepared magnetostrictive devices have strong reliability and simple driving methods. Magnetostrictive materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More