Epoxy olefin and olefin ether modified polymerized rosin resin

A technology of epoxy-based olefin and polymerized rosin, which is applied in chemical modification of natural resins, adhesive additives, polymer adhesive additives, etc., can solve problems such as increased hardness, decreased initial viscosity, and decreased flexibility, and achieves enhanced Adhesive properties, improved adhesive properties, and enhanced flexibility

Inactive Publication Date: 2019-06-18
广西藤县通轩立信化学有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The quality of rosin can be significantly improved after deep processing. Polymerized rosin is the product of deep processing of rosin. Compared with rosin, it has higher molecular weight and thickening effect. reduced viscosity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy olefin and olefin ether modified polymerized rosin resin
  • Epoxy olefin and olefin ether modified polymerized rosin resin
  • Epoxy olefin and olefin ether modified polymerized rosin resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method for epoxy olefin and olefin ether modified polymerized rosin resin, characterized in that it comprises the following steps:

[0021] S1. In parts by weight, add 100 parts of polymerized rosin resin acid into the solvent, heat up to 150°C, add 2.5 parts of organic alkali ammonium catalyst after the polymerized rosin resin acid melts, and then dropwise add epoxy olefin and olefin ether raw materials , the dropping time is 0.5h, the temperature is raised to 130°C, and the heating is stopped when the acid value of the polymerized rosin resin is 6mg KOH / g;

[0022] S2. Continue to add the solvent, then neutralize the organic base catalyst with an acid agent, and obtain the substrate after washing with water. The substrate is distilled under reduced pressure at 140° C. and then dried to obtain epoxy olefin and olefin ether modified polymerized rosin trees.

[0023] The dimer content in the polymerized rosin resin acid is 50%.

[0024] Described solvent i...

Embodiment 2

[0030] A preparation method for epoxy olefin and olefin ether modified polymerized rosin resin, characterized in that it comprises the following steps:

[0031] S1. In parts by weight, add 100 parts of polymerized rosin resin acid to the solvent, heat up to 110°C, add 0.22 parts of organic alkali ammonium catalyst after the polymerized rosin resin acid melts, and then dropwise add epoxy olefin and olefin ether raw materials , the dropping time is 0.8h, the temperature is raised to 180°C, and the heating is stopped when the acid value of the polymerized rosin resin is 3mg KOH / g;

[0032] S2. Continue to add the solvent, then neutralize the organic base catalyst with an acid agent, and obtain the substrate after washing with water. The substrate is distilled under reduced pressure at 180° C. and then dried to obtain epoxy olefin and olefin ether modified polymerized rosin trees.

[0033] The dimer content in the polymerized rosin resin acid is 60%.

[0034] The solvent is methy...

Embodiment 3

[0040] A preparation method for epoxy olefin and olefin ether modified polymerized rosin resin, characterized in that it comprises the following steps:

[0041] S1. In parts by weight, add 100 parts of polymerized rosin resin acid to the solvent, heat up to 50°C, add 0.2 parts of organic alkali ammonium catalyst after the polymerized rosin resin acid melts, and then dropwise add epoxy olefin and olefin ether raw materials , the dropping time is 1h, the temperature is raised to 50° C., and the heating is stopped when the acid value of the polymerized rosin resin is 1.3 mg KOH / g;

[0042] S2. Continue to add the solvent, then neutralize the organic base catalyst with an acid agent, and obtain the substrate after washing with water. The substrate is distilled under reduced pressure at 100° C. and then dried to obtain epoxy olefin and olefin ether modified polymerized rosin trees.

[0043] The dimer content in the polymerized rosin resin acid is 26%.

[0044] The solvent is a mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of an epoxy olefin and olefin ether modified polymerized rosin resin. The method comprises the following steps: S1, adding 100 parts by weight of polymerized rosin resin acid to a solvent, heating the obtained solution to 50-150 DEG C, adding 0.2-6 parts of an organic alkali ammonium catalyst after the polymerized rosin resin is melted, dropwise addingan epoxy olefin and olefin ether raw material within 0.5-1 h, heating the obtained solution to 50-180 DEG C, and stopping heating when the acid value of the polymerized rosin resin in the reaction isnot more than 6 mg KOH/g; and S2, continuously adding the solvent, neutralizing the organic alkali catalyst with an acid agent, washing the above obtained product with water to obtain a substrate, carrying out reduced pressure distillation on the substrate at 50-180 DEG C, and drying the obtained product to obtain the epoxy olefin and olefin ether modified polymerized rosin resin. The epoxy olefinand olefin ether modified polymerized rosin resin prepared in the invention has the characteristics of good tackifying effect, good initial tack and good flexibility.

Description

technical field [0001] The invention belongs to the field of rosin deep processing, and in particular relates to an epoxy olefin and olefin ether modified polymerized rosin resin and a preparation method thereof. Background technique [0002] With the increasing improvement of global human science and technology life, it will become an inevitable trend of sustainable development for people to look for non-polluting and renewable resources that can replace petrochemicals between resource acquisition and environmental protection. Therefore, the green and recyclable biomass rosin Materials are reprocessed into various polymer materials, which have a wide range of applications due to their special chemical and physical properties. Rosin has the advantages of large output, green and environmental harmony, renewable, biodegradable, etc., and it contains a stable triple ring rigid structure, so it has the potential to replace petrochemical aromatic ring raw materials to prepare fun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09F1/04C09J11/08
Inventor 关炽昌刘涛
Owner 广西藤县通轩立信化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap