A kind of method and product thereof of double ion modified silicone rubber material

A technology of rubber material and modified silicon, applied in the field of dual-ion modified silicone rubber material, can solve the problems of changing antibacterial properties and cytocompatibility, and achieve the enhancement of cell adhesion, inhibition of growth and reproduction, and biological histocompatibility. improved effect

Active Publication Date: 2022-02-11
THE SECOND AFFILIATED HOSPITAL ARMY MEDICAL UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, they all change the properties of silicone rubber in a single way. No research has shown how to inject two kinds of ions into the surface of silicone rubber at the same time, which can not only maintain its original mechanical properties, but also change its antibacterial properties and cytocompatibility at the same time. sex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method and product thereof of double ion modified silicone rubber material
  • A kind of method and product thereof of double ion modified silicone rubber material
  • A kind of method and product thereof of double ion modified silicone rubber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Prepare medical silicone rubber into a silicone rubber sheet with a size of 100mm×100mm×1mm, and inject a dose of 1×10 into the surface of the silicone rubber 11 ions / cm 2 of carbon ions and 3 x 10 11 ions / cm 2 Silver ions, the ion energy is 20keV, and the beam current density is 0.8mA / cm 2 (Carbon ions first and then silver ions, the same below); and then injecting doses of 3×10 15 ions / cm 2 of carbon ions and 3 x 10 16 ions / cm 2 Silver ions, the ion energy is 20keV, and the beam current density is 0.8mA / cm 2 , marked as No. 1 modified silicone rubber material.

Embodiment 2

[0045] Prepare medical silicone rubber into a silicone rubber sheet with a size of 100mm×100mm×1mm, and inject a dose of 1×10 into the surface of the silicone rubber 11 ions / cm2 of carbon ions and 3 x 10 11 ions / cm 2 Silver ions, the ion energy is 20keV, and the beam current density is 0.8mA / cm 2 ; and then injected into the surface of silicone rubber with a dose of 3×10 15 ions / cm 2 of carbon ions and 1 x 10 16 ions / cm 2 Silver ions, the ion energy is 20keV, and the beam current density is 0.8mA / cm 2 , marked as No. 2 modified silicone rubber material.

Embodiment 3

[0047] Prepare medical silicone rubber into a silicone rubber sheet with a size of 100mm×100mm×1mm, and inject a dose of 1×10 into the surface of the silicone rubber 11 ions / cm 2 of carbon ions and 3 x 10 11 ions / cm 2 Silver ions, the ion energy is 20keV, and the beam current density is 0.8mA / cm 2 ; Then inject a dose of 1×10 to the surface of the silicone rubber 16 ions / cm 2 of carbon ions and 1 x 10 16 ions / cm 2 Silver ions, the ion energy is 20keV, and the beam current density is 0.8mA / cm 2 , marked as No. 3 modified silicone rubber material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for modifying silicon rubber materials with double ions. Carbon ions and silver ions are respectively injected into the surface of the silicon rubber by ion implantation. First, low-dose carbon ions and silver ions are respectively injected, and then high-dose are injected respectively. carbon ions and silver ions to modify the surface of silicone rubber. The prepared double-ion modified silicone rubber material can reduce the excessive proliferation of fibroblasts while maintaining the original mechanical properties, and further prepared into implant materials can significantly reduce the formation of the induced capsule and its contracture in the later stage. At the same time, it has obvious bactericidal effect on Escherichia coli, Staphylococcus aureus, and Staphylococcus epidermidis and inhibits their growth and reproduction. By using laser confocal observation of the expression changes of the cell adhesion-related protein Talin protein on the surface of the material, it shows that the double-ion modified silicone rubber The cell adhesion ability on the material is obviously enhanced, and its biocompatibility is improved.

Description

technical field [0001] The invention belongs to the technical field of ion implantation, and relates to a method of double-ion modified silicon rubber material and a product thereof. Background technique [0002] Ion implantation is a surface modification method gradually developed in the early 1970s. It ionizes the atoms of certain elements into ions and accelerates them in a high-voltage electric field of tens of thousands to hundreds of thousands of volts to form a high-energy ion beam. High-speed bombardment and injection into the surface of the substrate to obtain a surface modification technology with special physical, chemical and mechanical properties. The implantation process is a non-equilibrium process. The choice of implanted elements is not limited by metallurgy, and the implanted concentration is not restricted by the equilibrium phase diagram. Any element can be implanted into any material matrix, and since there is no interface between the implanted ions and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/12C08L83/04
CPCC08J7/12C08J2383/04
Inventor 周鑫张一鸣周璇杜依晨陈瑶石小花樊东力
Owner THE SECOND AFFILIATED HOSPITAL ARMY MEDICAL UNIV