Wear-resistant cathode electrophoresis coating, and preparation method thereof

A technology for cathodic electrophoretic coatings and raw materials, applied in electrophoretic coatings, coatings, etc., can solve problems such as poor wear resistance, and achieve the effects of high gloss, simple operation and excellent corrosion resistance.

Inactive Publication Date: 2019-08-09
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem of poor wear resistance of cathodic electrophoretic coatings in the prior art, the present invention provides a wear-resistant cathodic electrophoretic coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant cathode electrophoresis coating, and preparation method thereof
  • Wear-resistant cathode electrophoresis coating, and preparation method thereof
  • Wear-resistant cathode electrophoresis coating, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An embodiment of the present invention provides a wear-resistant cathodic electrophoretic coating, including color paste, emulsion and purified water, and the color paste includes the following raw materials in parts by weight:

[0025]

[0026] The emulsion comprises the following raw materials in parts by weight:

[0027]

[0028] Among them, the polytetrafluoroethylene fluororesin contains 31% polytetrafluoroethylene particle powder, 4% oleic acid, 5% bisphenol A, 23% isopropanol, 5% diethanolamine and 32% blocked isocyanate curing agent; Trifluoroethyl methacrylate fluororesin contains 33% trifluoroethyl methacrylate, 7% oleic acid, 4% bisphenol A, 16% sec-butanol, 10% diethanolamine and 30% blocked isocyanate curing agent; surfactant is PPG2000, co-solvent is isopropanol, emulsifier is alkylphenol polyoxyethylene ether, neutralizer A is lactic acid, neutralizer B is sulfamic acid, pigments and fillers are 9g kaolin, 8g chromium Yellow 7000 and 6g titanium di...

Embodiment 2

[0034] An embodiment of the present invention provides a wear-resistant cathodic electrophoretic coating, including color paste, emulsion and purified water, and the color paste includes the following raw materials in parts by weight:

[0035]

[0036] The emulsion comprises the following raw materials in parts by weight:

[0037]

[0038] Among them, the polytetrafluoroethylene fluororesin contains 30% polytetrafluoroethylene particle powder, 5% oleic acid, 7% bisphenol A, 20% propylene glycol methyl ether, 7% diethanolamine and 31% blocked isocyanate curing agent; Trifluoroethyl methacrylate fluororesin contains 35% trifluoroethyl methacrylate, 5% oleic acid, 6% bisphenol A, 17% diethylene glycol butyl ether, 8% diethanolamine and 29% blocked Non-toxic isocyanate curing agent; surfactant is PPG4000, co-solvent is diethylene glycol butyl ether, emulsifier is alkylphenol polyoxyethylene ether, neutralizer A is acetic acid, neutralizer B is sulfamic acid, pigments and fil...

Embodiment 3

[0044] An embodiment of the present invention provides a wear-resistant cathodic electrophoretic coating, including color paste, emulsion and purified water, and the color paste includes the following raw materials in parts by weight:

[0045]

[0046] The emulsion comprises the following raw materials in parts by weight:

[0047]

[0048] Among them, the polytetrafluoroethylene fluororesin contains 33% polytetrafluoroethylene particle powder, 3% oleic acid, 5% bisphenol A, 20% propylene glycol phenyl ether, 5% diethanolamine and 34% blocked isocyanate curing agent; Trifluoroethyl methacrylate fluororesin contains 32% trifluoroethyl methacrylate, 4% oleic acid, 3% bisphenol A, 18% propylene glycol phenyl ether, 10% diethanolamine and 33% blocked isocyanate curing agent; surfactant is PPG2000, cosolvent is glycol phenyl ether, emulsifier is alkylphenol polyoxyethylene ether, neutralizer A is formic acid, neutralizer B is sulfamic acid, pigment and filler are 8g kaolin, 12...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of aqueous paint, and especially relates to a wear-resistant cathode electrophoresis coating, and a preparation method thereof. The wear-resistant cathode electrophoresis coating comprises a color paste, an emulsion, and water; the color paste comprises a polytetrafluoroethylene fluororesin, a cosolvent, a neutralizer A, a surfactant, deionized water, kaolin, anda pigment filler; the emulsion comprises a trifluoroethyl methacrylate fluororesin, an emulsifier, a neutralizer B, and deionized water. The wear-resistant cathode electrophoresis coating possesses excellent throwing power, is high in hardness, clunging force, acid and alkali resistance, wear resistance, corrosion resistance, paint film uniformity, and glossiness.

Description

technical field [0001] The invention relates to the field of water-based coatings, in particular to a wear-resistant cathodic electrophoretic coating and a preparation method thereof. Background technique [0002] Cathodic electrophoretic paint is an environmentally friendly paint used for primers improved on the basis of water-based dipping primers. It has the advantages of high painting efficiency, economy, safety, and less pollution, and is convenient for automated scale production. Common cathodic electrophoretic coatings include epoxy resin coatings, alkyd resin coatings, amino resin coatings, phenolic resin coatings, and the like. At present, more than 95% of automotive primers are cathodic electrophoretic coatings. In addition, the protection of building materials, light industry, household appliances and hardware and other industrial fields all use cathodic electrophoretic coatings as the development direction. As a primer, the cathodic electrophoretic coating needs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/16C09D127/18C09D5/44C09D7/61C09D7/63C09D7/65
CPCC09D133/16C09D5/4473C09D5/448C08L2205/035
Inventor 刘树飞刘东郭晓猛胡中源
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap