Environment-friendly high-reflectivity powder coating for lamp cavity .and preparation method thereof

A high reflectivity, powder coating technology, applied in powder coatings, reflective/signal coatings, epoxy coatings, etc., can solve the problem of only 85% reflectivity, improve the reflectivity, increase the surface reflectivity, avoid The effect of pollution

Inactive Publication Date: 2019-08-16
浙江绿能塑粉科技股份有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the surface of lampshades and other lighting decorations is generally made of spray paint and ordinary powder coating, and its reflectivity is only 85%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The weight ratio is 26 parts of epoxy resin, 26 parts of polyester resin, 1.2 parts of leveling agent, 0.6 parts of defoamer, 21 parts of titanium dioxide, 11 parts of precipitated barium sulfate, 3.5 parts of reflective material and 0.06 parts Put the parts of the paint into the mixer and mix and stir evenly. Next, put the uniformly stirred mixture into an extruder for melt extrusion and tableting. Subsequently, the compressed tablets were crushed to a median particle size of 26±1 μm. Finally, the powder is packaged into a finished product.

Embodiment 2

[0027] The weight ratio is 27.5 parts of epoxy resin, 27.5 parts of polyester resin, 1.5 parts of leveling agent, 0.75 parts of defoamer, 22.5 parts of titanium dioxide, 12.5 parts of precipitated barium sulfate, 4 parts of reflective material and 0.07 parts Put the parts of the paint into the mixer and mix and stir evenly. Next, put the uniformly stirred mixture into an extruder for melt extrusion and tableting. Subsequently, the compressed tablets were crushed to a median particle size of 26±1 μm. Finally, the powder is packaged into a finished product.

Embodiment 3

[0029] The weight ratio is 29 parts of epoxy resin, 29 parts of polyester resin, 1.8 parts of leveling agent, 0.9 parts of defoamer, 24 parts of titanium dioxide, 14 parts of precipitated barium sulfate, 4.5 parts of reflective material and 0.08 parts Put the parts of the paint into the mixer and mix and stir evenly. Next, put the uniformly stirred mixture into an extruder for melt extrusion and tableting. Subsequently, the compressed tablets were crushed to a median particle size of 26±1 μm. Finally, the powder is packaged into a finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
reflectanceaaaaaaaaaa
reflectanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly high-reflectivity powder coating for a lamp cavity and a preparation method thereof. The environment-friendly high-reflectivity powder coating comprisesthe following components in parts by weight: 25-30 parts of epoxy resin, 25-30 parts of polyester resin, 1-2 parts of a leveling agent, 0.5-1 part of a defoaming agent, 20-25 parts of titanium dioxide, 10-15 parts of precipitated barium sulfate, 3-5 parts of a light-reflective material and 0.05-0.1 part of a pigment. The preparation method of the environment-friendly high-reflectivity powder coating for the lamp cavity comprises the following steps: mixing formula materials, melting, extruding, tabletting, roughly crushing until the crushed grain diameter to a median diameter of 26um+ / -1um, and packaging into a finished product, the finished product is suitable for the lamp cavity, conforms to ROHS instructions and REACH regulations, can manufacture high-gloss and sub-gloss high-reflectivity coatings, and has stable coating and simple production process.

Description

[0001] 【Technical field】 [0002] The invention relates to the technical field of powder coatings, in particular to the technical field of an environment-friendly high-reflectance powder coating for a cavity of a lamp and a preparation method thereof. [0003] 【Background technique】 [0004] In the past, the surface protection and decoration of the lighting industry usually used electroplating, which has beautiful, diverse, decorative and anti-corrosion properties. However, the material selection requirements of the electroplating solution are relatively high, the cost is high, and the pollution of electroplating is relatively large. In addition, with the rapid development of the decoration industry and supporting products driven by the construction industry and real estate development, consumers are increasingly emphasizing and pursuing unique lamps and lanterns with different styles in public and home decoration, and pay more attention to the overall color tone. harmony. Ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/00C09D5/03C09D5/33C09D7/47C09D7/61
CPCC08K2003/2241C08K2003/3045C08L2205/03C09D5/004C09D5/033C09D163/00C09D167/00C08L67/00C08L33/04C08K3/22C08K3/30C08K9/02C08K7/20C08K13/06C08L63/00
Inventor 周光阳徐锦丽张爱华周天明沈晶秦丰永范若谷杨建芬
Owner 浙江绿能塑粉科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com