A kind of preparation method of nanoscale indium hydroxide

A nano-scale technology of indium hydroxide, applied in the field of ITO targets, can solve the problems of increased washing difficulty and water consumption, poor uniformity of indium hydroxide products, increased preparation costs and operating steps, etc., to reduce the difficulty of washing and washing water consumption, reducing the difficulty of wastewater treatment, and reducing the effect of the production of ammonium nitrate mother liquor

Active Publication Date: 2021-07-30
先导薄膜材料(安徽)有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above method will produce a large amount of ammonium nitrate mother liquor, which will produce a large amount of nitrogen-containing wastewater after washing, which increases the difficulty of wastewater treatment; at the same time, it must be under the action of a dispersant to obtain a small particle size product, which increases the preparation cost and operation on the one hand. Steps, on the other hand, increase the impurities in the slurry, thereby increasing the washing difficulty and washing water consumption; in addition, the uniformity of the indium hydroxide product prepared by it is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of nanoscale indium hydroxide
  • A kind of preparation method of nanoscale indium hydroxide
  • A kind of preparation method of nanoscale indium hydroxide

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The invention provides a method for preparing nanoscale indium hydroxide, comprising the following steps:

[0032] a) passing ammonia gas into the indium nitrate aqueous solution to obtain a precursor slurry;

[0033] b) After washing the precursor slurry, it is spray-dried to obtain indium hydroxide powder.

[0034] According to the present invention, ammonia gas is introduced into the indium nitrate aqueous solution to obtain the precursor slurry.

[0035] In the present invention, the method of obtaining the indium nitrate aqueous solution is not particularly limited, and can be obtained in a manner well known to those skilled in the art; in some embodiments, the indium nitrate solid is mixed with water to obtain an indium nitrate aqueous solution; in other In the embodiment, the indium nitrate solution is diluted with water to obtain an indium nitrate aqueous solution. In the present invention, the molar concentration of indium in the indium nitrate aqueous soluti...

Embodiment 1

[0049] Dilute the indium nitrate solution with water until the molar concentration of indium is 2 mol / L, and feed ammonia gas at 60 mL / min while stirring at 40°C until the pH of the slurry is 10, stop the aeration, and age at 25°C for 8 hours. The slurry was transferred to a storage tank, washed with a filter press, and deionized water with a conductivity of 10 μs / cm was added for circular washing until the conductivity of the slurry was 19.0 μs / cm. Afterwards, a double-flow spray dryer is used for spray drying, with an inlet air temperature of 300°C and an outlet air temperature of 150°C to obtain indium hydroxide powder without sieving.

[0050] After testing, the purity of the obtained indium hydroxide product is 99.99%; the specific surface area is 47.2m 2 / g, D50 is 0.28μm; product moisture content is 0.1%.

[0051] see figure 1 , figure 1 It is the SEM image (magnification is 3000 times) of the product obtained in Example 1 of the present invention; it can be seen tha...

Embodiment 2

[0054] Dilute the indium nitrate solution with water until the molar concentration of indium is 0.4 mol / L, feed ammonia gas at 20 mL / min with stirring at 25°C until the pH of the slurry is 7.5, stop the aeration, and age at 40°C for 8 hours. The slurry was transferred to a storage tank, washed with a filter press, and deionized water with a conductivity of 10 μs / cm was added for circular washing until the conductivity of the slurry was 17.6 μs / cm. Afterwards, a double-flow spray dryer was used for spray drying, with an inlet air temperature of 250° C. and an outlet air temperature of 120° C. to obtain indium hydroxide powder without sieving.

[0055] After testing, the purity of the obtained indium hydroxide product is 99.99%; the specific surface area is 50.02m 2 / g, D50 is 0.48μm; the water content of the product is 0.80%.

[0056] see image 3 , image 3 It is the SEM image (magnification is 3000 times) of the product obtained in Example 2 of the present invention; it ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of nano-scale indium hydroxide, comprising the following steps: a) passing ammonia gas into an indium nitrate aqueous solution to obtain a precursor slurry; b) washing the precursor slurry, spraying Dry to obtain indium hydroxide powder. The preparation method provided by the invention can reduce the production of ammonium nitrate mother liquor, reduce the washing difficulty and water consumption, reduce the generation of nitrogen-containing wastewater, and reduce the difficulty of wastewater treatment; at the same time, the preparation method of the invention can obtain nano-scale The product reduces the preparation cost, simplifies the operation steps, and reduces the impurities in the slurry, thereby reducing the washing difficulty and washing water consumption; moreover, the obtained product has a small particle size and good uniformity, and does not need to be screened. the preparation process.

Description

technical field [0001] The invention relates to the technical field of ITO targets, in particular to a preparation method of nanoscale indium hydroxide. Background technique [0002] Indium Hydroxide (In(OH) 3 ) is an extended product of indium, which is a precursor for manufacturing indium oxide or compound powder containing indium oxide, and can be used to manufacture ITO targets for sputtering that form ITO films (composite oxides with indium-tin as the main component). [0003] ITO film is a transparent electrode film widely used in display devices such as solar cells and liquid crystal displays. With the rapid development of global digital technology, today's optoelectronic equipment is gradually developing in the direction of personalization, ultra-large and special-shaped flat-panel displays, and the demand for transparent conductive films such as sputtering targets has increased significantly. Indium hydroxide is used as the precursor of the main raw material for f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G15/00
CPCC01G15/00C01P2004/03C01P2004/51C01P2004/62C01P2006/12C01P2006/80C01P2006/82
Inventor 凤吾生朱刘何坤鹏张莉兰
Owner 先导薄膜材料(安徽)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com