A kind of preparation method of ultra-coarse tungsten carbide cemented carbide containing trace amount of cobalt

A cemented carbide and trace technology, used in the field of high hardness cemented carbide to prepare high strength, can solve the problems of fracture toughness and hardness contradiction, achieve uniform composition, reduce pores, and improve overall performance.

Active Publication Date: 2021-07-27
HEFEI UNIV OF TECH
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem of conflicting fracture toughness and hardness of existing tungsten carbide cemented carbide, the present invention provides a preparation method of ultra-coarse tungsten carbide cemented carbide containing a small amount of cobalt, aiming to obtain high fracture toughness and high strength at the same time Ultra-coarse-grained tungsten carbide composites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of ultra-coarse tungsten carbide cemented carbide containing trace amount of cobalt
  • A kind of preparation method of ultra-coarse tungsten carbide cemented carbide containing trace amount of cobalt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The ultra-coarse WC cemented carbide composite material of the present embodiment is carried out as follows:

[0031] 1. Select WC powder with a particle size of 20 μm, nano WC-6Co composite powder with a grain size ≤ 200 nm, and cobalt powder with an average particle size of 3 μm. According to the composition of the required WC cemented carbide, weigh coarse-grained WC powder and nano-WC-6Co composite powder, the mass ratio of the two is 3:1, and add 4wt% Co, and use a mixer to mix mechanically for 2 hours to obtain a mixed Uniform cemented carbide mixture powder; according to the required product size, weigh a certain amount of composite powder;

[0032] 2. Fill the cemented carbide mixture powder weighed in step 1 into the graphite mold covered with graphite paper; use a manual hydraulic press to pre-press the graphite mold filled with the composite powder, and the pressure is ~10MPa;

[0033] 3. Wrap ~5mm thick carbon felt on the periphery of the graphite mold fill...

Embodiment 2

[0040] The ultra-coarse WC cemented carbide composite material of the present embodiment is carried out as follows:

[0041] 1. Select WC powder with a particle size of 20 μm, nano WC-6Co composite powder with a grain size ≤ 200 nm, and cobalt powder with an average particle size of 3 μm. According to the composition of the required WC cemented carbide, weigh coarse-grained WC powder and nano-WC-6Co composite powder, the mass ratio of the two is 3:1, and add 4wt% Co, and use a mixer to mix mechanically for 2 hours to obtain a mixed Uniform cemented carbide mixture powder; according to the required product size, weigh a certain amount of composite powder;

[0042] 2. Fill the cemented carbide mixture powder weighed in step 1 into the graphite mold covered with graphite paper; use a manual hydraulic press to pre-press the graphite mold filled with the composite powder, and the pressure is ~10MPa;

[0043] 3. Wrap ~5mm thick carbon felt on the periphery of the graphite mold fill...

Embodiment 3

[0050] The ultra-coarse WC cemented carbide composite material of the present embodiment is carried out as follows:

[0051] 1. Select WC powder with a particle size of 20 μm, nano WC-6Co composite powder with a grain size ≤ 200 nm, and cobalt powder with an average particle size of 3 μm. According to the composition of the required WC cemented carbide, weigh coarse-grained WC powder and nano-WC-6Co composite powder, the mass ratio of the two is 3:1, and add 4wt% Co, and use a mixer to mix mechanically for 2 hours to obtain a mixed Uniform cemented carbide mixture powder; according to the required product size, weigh a certain amount of composite powder;

[0052] 2. Fill the cemented carbide mixture powder weighed in step 1 into the graphite mold covered with graphite paper; use a manual hydraulic press to pre-press the graphite mold filled with the composite powder, and the pressure is ~10MPa;

[0053] 3. Wrap ~5mm thick carbon felt on the periphery of the graphite mold fill...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
crystal sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of ultra-coarse tungsten carbide cemented carbide containing a trace amount of cobalt, which uses WC powder and nanometer WC-6Co composite powder as raw materials, and adds a trace amount of cobalt; Sintering is prepared into ultra-coarse-grained cemented carbide. The invention is a method for preparing ultra-coarse cemented carbide with a short process. The prepared WC grain size is uniform and reaches 30 μm, and the alloy has high strength and hardness, good density and high fracture toughness.

Description

technical field [0001] The invention relates to a preparation method of ultra-coarse tungsten carbide cemented carbide containing a trace amount of cobalt. Ultra-coarse WC cemented carbide and nano WC-6Co composite powder are used as raw materials, and metal Co powder is added to prepare high-strength, high-hardness hard alloy. alloy method. The high-performance cemented carbide prepared by this method can be processed into drill bits, milling cutters or wear-resistant abrasive tools. Background technique [0002] Cemented carbide materials have excellent properties such as high hardness, high strength, and high elastic modulus, and are widely used in various cutting tools, mining tools and wear-resistant parts. However, it is difficult for high hardness and high fracture toughness of cemented carbide to coexist. Hardness and toughness are contradictory bodies in cemented carbide. Some scholars believe that through the method of matching the thickness of tungsten carbide i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/08C22C1/05C22C1/10
CPCC22C1/051C22C29/005C22C29/067C22C29/08
Inventor 张久兴金亚琴胡梦圆潘亚飞
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap