A kind of powder metallurgy aluminum base material and preparation method thereof

An aluminum-based material and powder metallurgy technology, applied in the field of powder metallurgy, can solve problems such as hindering mass production and sintering deformation, and achieve the effect of simple addition, reducing sintering deformation, and avoiding sintering deformation

Active Publication Date: 2022-01-25
NBTM NEW MATERIALS GRP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the characteristics of aluminum alloy liquid phase sintering lead to serious sintering deformation. At present, mold design is commonly used in the field of powder metallurgy to solve the problem of sintering deformation; however, the sintering deformation of aluminum alloy has inhomogeneity and randomness, which is difficult to eliminate through mold design.
Sintering deformation is one of the key technical problems of powder metallurgy aluminum-based materials, which seriously hinders its mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of powder metallurgy aluminum base material and preparation method thereof
  • A kind of powder metallurgy aluminum base material and preparation method thereof
  • A kind of powder metallurgy aluminum base material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In this embodiment, taking the pure aluminum matrix as an example, the preparation method of the powder metallurgy aluminum-based material is described, which specifically includes the following steps:

[0031] (1) Powder mixing: the aluminum elemental powder with an average particle size of 60 μm and the titanium hydride powder with an average particle size of 45 μm are uniformly ground and mixed with a mortar to obtain a raw material powder, wherein the mass fraction of the titanium hydride powder in the raw material powder is 0.01 %, the balance is aluminum elemental powder. The titanium hydride powder used in this step may preferably have a purity of 99.9%, wherein the mass ratio of titanium element to hydrogen element is 0.5.

[0032] (2) Forming: The powder obtained in step (1) is subjected to compression molding, the pressing pressure is 150 MPa, and the holding time is 15 s.

[0033] (3) Sintering: tube furnace is used for sintering, and the sintering protectiv...

Embodiment 2

[0036] In this embodiment, taking the 2014 aluminum alloy substrate as an example, the preparation method of the powder metallurgy aluminum-based material is described, which specifically includes the following steps:

[0037] (1) Powder mixing: the 2014 aluminum alloy powder with an average particle size of 78 μm and the titanium hydride powder with an average particle size of 10 μm are mixed to obtain a raw material powder, and the raw material powder is ball milled on a planetary ball mill with a rotation speed of 120 r / min for 4 hours and mixed evenly. The mass fraction of titanium hydride powder in the raw material powder is 1%, and the balance is 2014 aluminum alloy powder. The titanium hydride powder used in this step preferably has a purity of 99.9%, wherein the ratio of titanium element to hydrogen element is 0.5.

[0038] (2) Forming: Utilize a V-shaped mixer to mix into the powder obtained in step (1) and account for 0.5wt% zinc stearate as a lubricant as a lubrican...

Embodiment 3

[0043] In this embodiment, taking the 7039 aluminum alloy substrate as an example, the preparation method of the powder metallurgy aluminum-based material is described, which specifically includes the following steps:

[0044] (1) Powder mixing: mix 7039 aluminum alloy powder with an average particle size of 45 μm and titanium hydride powder with an average particle size of 16 μm to obtain a raw material powder, and the raw material powder is ball milled on a planetary ball mill with a rotational speed of 185 r / min for 4.5 hours and mixed evenly , wherein the mass fraction of titanium hydride powder in the raw material powder is 1.5%, and the balance is 7039 aluminum alloy powder. The titanium hydride powder used in this step may preferably have a purity of 95%, wherein the mass ratio of titanium element to hydrogen element is 2.

[0045] (2) Forming: use a spiral mixer to mix zinc stearate that accounts for 0.8% of the mass fraction of the raw material powder into the powder ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a powder metallurgy aluminum-based material. The raw material powder includes titanium hydride with a mass percentage of 0.01% to 5%, and the balance is aluminum matrix powder. The aluminum matrix powder is aluminum simple substance powder or aluminum alloy powder or aluminum matrix composite material powder. The invention also relates to a preparation method for the powder metallurgy aluminum-based material, comprising the following steps: (a) powder mixing; (b) forming; (c) sintering; (d) heat treatment. The sintering deformation of the powder metallurgy aluminum-based material is small, and the preparation method is simple and suitable for mass production.

Description

technical field [0001] The invention relates to the field of powder metallurgy, in particular to a powder metallurgy aluminum-based material and a preparation method thereof. Background technique [0002] Aluminum alloy is a light material with low density and high specific strength. After aluminum alloy replaces iron-based and copper-based parts, it is beneficial to reduce self-weight, energy saving and emission reduction. Aluminum alloy is used in aerospace, automobile, machinery manufacturing, shipbuilding, and chemical industries. and other fields have been widely used. For example, beams of supersonic fighter jets, high-pressure cylinders, automotive cantilever components, engine blades, casings and cylinder liners, automotive engine and gearbox parts, etc. are widely used in aluminum alloy. However, many parts not only require light weight and good mechanical properties, such as hardness, strength, wear resistance, thermal expansion coefficient, high temperature mecha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00B22F3/11C22C21/00
CPCB22F1/0003B22F3/1125C22C21/00B22F2998/10B22F9/04B22F3/02B22F3/10B22F2003/248
Inventor 颜巍巍秦晓冬杨浩包崇玺
Owner NBTM NEW MATERIALS GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com