Waterborne epoxy emulsifier as well as preparation and application thereof
A water-based epoxy emulsion, water-based epoxy technology, applied in the direction of epoxy resin glue, epoxy resin coating, adhesive, etc., can solve the problems of affecting coating resistance and protection performance, poor wet adhesion, etc., and achieve good emulsification ability , Improve adhesion and good compatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1
[0031] Put 2000g of ED2003 (Huntsman polyetheramine), 150g of phenyl glycidyl ether and 1500g of propylene glycol methyl ether into the reaction kettle, raise the temperature to 100°C and react for 3 hours, then add 2000g of epoxy resin E-20 to the reaction system and continue the reaction After 2 hours; add 230g phosphoric acid (85%) to the reaction system, maintain the original reaction temperature and react for 3 hours, add 1060g polyethylene glycol diglycidyl ether to the reaction system, and increase the temperature to 110°C and react for 2 hours. Cooling and discharging to obtain water-based epoxy emulsifier A.
Example Embodiment
[0032] Example 2
[0033] Put 900g of ED900 (Huntsman polyetheramine), 130g of butyl glycidyl ether and 1000g of propylene glycol methyl ether into the reaction kettle, raise the temperature to 110°C and react for 4 hours, add 2000g of epoxy resin E-20 to the reaction system and continue the reaction After 2 hours; add 230g phosphoric acid (85%) to the reaction system, maintain the original reaction temperature and react for 3 hours, add 1270g polyethylene glycol diglycidyl ether to the reaction system, raise the temperature to 120°C and react for 2 hours, Cool down the material to obtain water-based epoxy emulsifier B.
Example Embodiment
[0034] Example 3
[0035] Put 4000g of D4000 (Huntsman polyetheramine), 300g of C12-14 alkyl glycidyl ether and 2500g of propylene glycol methyl ether into the reaction kettle, raise the temperature to 110°C and react for 4 hours, then add 2000g of epoxy resin E-20 to the reaction system , Continue the reaction for 2 hours; add 230g phosphoric acid (85%) to the reaction system, maintain the original reaction temperature and react for 3 hours, add 800g polyethylene glycol diglycidyl ether to the reaction system, and heat to 120°C for reaction 2. After hours, the temperature is lowered and the material is discharged to obtain the water-based epoxy emulsifier C.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap