Pressure sensitive composite material used in flexible sensor and preparation method thereof

A pressure-sensitive composite material and flexible sensor technology, applied in the field of sensors, can solve the problems affecting the electrical conductivity and piezoresistive properties of the pressure-sensitive composite material, poor dispersion, etc., and achieve excellent processability, improved mechanical properties, and excellent aging resistance. Effect

Inactive Publication Date: 2019-10-15
SHAOXING UNIV YUANPEI COLLEGE
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The second object of the invention of the present invention is to overcome the prior art when carbon black is used as the conductive particles in the pressure-sensitive silicone rubber, because the larger the specific surface area of ​​the carbon black, the larger the surface energy, so the carbon black is easy to form agglomeration, Dispersion is poor, thereby a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pressure sensitive composite material used in flexible sensor and preparation method thereof
  • Pressure sensitive composite material used in flexible sensor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0046] Example 1:

[0047] Combine 20g Ketjen carbon black ECP600JD, 5g carbon nanotubes, 20g nano SiO 2 And 40g of 2% silane coupling agent Si-69 were added to 115g of naphtha, stirred and ultrasonically dispersed for 30 minutes to form a dispersion. Add 450g of room temperature vulcanized silicone rubber Dow Corning 184 to the dispersion, magnetically stir at room temperature for 3 hours to form a viscous mixture. Place the mixture in a vacuum drying oven at 40°C for 20 minutes to remove bubbles and incompletely volatile naphtha. That is, an uncured pressure-sensitive composite material is prepared.

Example Embodiment

[0048] Example 2:

[0049] Combine 20g Ketjen carbon black ECP600JD, 5g carbon nanotubes, 5g nano SiO 2 And 10g of 2% silane coupling agent Si-69 were added to 85g of naphtha, stirred and ultrasonically dispersed for 30 minutes to form a dispersion. Add 350g room temperature vulcanized silicone rubber Dow Corning 184 to the dispersion, magnetically stir at room temperature for 3 hours to form a viscous mixture. Place the mixture in a vacuum drying oven at 40°C for 20 minutes to remove bubbles and incompletely volatile naphtha. That is, an uncured pressure-sensitive composite material is prepared.

Example Embodiment

[0050] Example 3:

[0051] Combine 75g Ketjen carbon black ECP600JD, 25g carbon nanotubes, 20g nano SiO 2 And 40g 2% silane coupling agent Si-69, add 25g n-hexane, 65g naphtha and 25g absolute ethanol mixed solution, stir and ultrasonically disperse for 60min to form a dispersion. Add 450g room temperature vulcanized silicone rubber Dow Corning 184 to the dispersion, magnetically stir at room temperature for 8 hours to form a viscous mixture. Place the mixture in a vacuum drying oven at 100°C for 30 minutes to remove bubbles and incompletely volatile solvents. Obtain an uncured pressure-sensitive composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

Relating to the sensor field, the invention discloses a pressure sensitive composite material used in a flexible sensor and a preparation method thereof. The pressure sensitive composite material usedin a flexible sensor comprises the following components by weight: 350-450 parts of silicone rubber, 25-100 parts of conductive particles, 5-20 parts of a nano modified material, 15-40 parts of an assistant, and 85-115 parts of a solvent. The conductive particles include carbon black and carbon nanotubes. The preparation method includes: dispersing the conductive particles and the nano modified material in the assistant to form a dispersion solution; adding silicone rubber into the dispersion solution, and stirring the substances evenly to obtain a mixed solution; and performing vacuum dryingon the mixed solution to obtain the pressure sensitive composite material. According to the invention, carbon black and carbon nanotubes are used as the conductive particles together, and the combined use of carbon black and carbon nanotubes in the silicone rubber can play a role of synergistic enhancement, the electrical conductivity and stability of the conductive particles and the mechanical properties of the composite material are all greatly improved, the pressure sensitive composite material has higher perception sensitivity, and the pressure perception range is improved.

Description

technical field [0001] The invention relates to the field of sensors, in particular to a pressure-sensitive composite material in a flexible sensor and a preparation method thereof. Background technique [0002] With the improvement of science and technology and modernization level, people have higher and higher requirements for pressure monitoring. It is no longer limited to pressure monitoring on regular rigid surfaces, and there are various forms. Ordinary rigid sensors can no longer meet people's actual needs. . Flexible pressure sensors can be bent or even folded at will, small in size, thin in thickness, flexible materials are basically non-toxic and harmless, and have good compatibility with the human body. A lot of research and application have been done. [0003] Pressure-sensitive silicone rubber is made of conductive particles filled in a silicone rubber matrix and processed through a series of processes. The insulating polymer material silicone rubber can obta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08K3/04C08K3/36C08K9/06G01L1/18G01L9/06
CPCC08K3/04C08K3/36C08K9/06C08K2201/001C08K2201/011C08K3/041G01L1/18G01L9/06C08L83/04
Inventor 徐志望
Owner SHAOXING UNIV YUANPEI COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap