Production process of shuttle-shaped environment-friendly bamboo stick

A production process and technology of bamboo sticks, applied in biocides, biocides, plant growth regulators, etc., can solve the problems of easy breakage, incomplete drying, bamboo fiber damage, etc., achieve excellent anti-mildew and anti-bacterial effects, improve Antibacterial and bactericidal ability, the effect of improving impact strength

Inactive Publication Date: 2019-11-12
黄山市黟县宏联竹制工艺有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, bamboo is more used in bamboo sticks. The existing bamboo stick production process: bamboo sticks-sulfur fumigation (hydrogen peroxide cooking)-drying-follow-up production-finished product packaging. Problems and shortcomings: finished bamboo sticks have sour taste, there is A large number of chemical residues. Bamboo sticks are treated with chemicals. The bamboo fiber is damaged, the willfulness is greatly reduced, and it is easy to break. After steaming and cooking, the drying is not complete, and the sugar and a lot of water in the bamboo itself are retained. It is easy to mold and grow insects, and it is also easy to absorb in the environment. Harmful substances and germs, and in the process of production and treatment, produce sewage containing chemicals, etc., which is not environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of shuttle-shaped environment-friendly bamboo stick
  • Production process of shuttle-shaped environment-friendly bamboo stick
  • Production process of shuttle-shaped environment-friendly bamboo stick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The production technology of the shuttle-shaped environmental protection bamboo stick of the present embodiment comprises the following steps:

[0033] (1) Moso bamboo is cut into bamboo strips of 150-250mm length, and bamboo strips are carried out to remove green, yellow and dry;

[0034] (2) the dried bamboo strips are machined into thick bamboo sticks, and made into bamboo sticks through a round stick machine;

[0035] (3) Put the bamboo sticks in the pressure tank, and spray water vapor into the tank, so that the temperature in the pressure tank is 110 degrees, and the pressure is 0.3MPa for 20 minutes, and then the bamboo sticks are immersed in the sterilizing solution. , Cooking for 40min under the condition of pressure 0.4MPa;

[0036] (4) drying the cooking bamboo sticks in the step (3), placing them in the carbonization furnace, heating up and carbonizing under the protection of inert gas;

[0037] (5) Place the carbonized bamboo sticks in the activation solu...

Embodiment 2

[0052] The production technology of the shuttle-shaped environmental protection bamboo stick of the present embodiment comprises the following steps:

[0053](1) Moso bamboo is cut into bamboo strips of 150-250mm length, and bamboo strips are carried out to remove green, yellow and dry;

[0054] (2) the dried bamboo strips are machined into thick bamboo sticks, and made into bamboo sticks through a round stick machine;

[0055] (3) Put the bamboo sticks in the pressure tank, and spray water vapor into the tank, so that the temperature in the pressure tank is 130 degrees, and the pressure is 0.5 MPa. The condition is treated for 30 minutes, and then the bamboo sticks are immersed in the sterilizing solution, and the temperature is 100 degrees. , Cooking for 50min under the condition of pressure 0.6MPa;

[0056] (4) drying the cooking bamboo sticks in the step (3), placing them in the carbonization furnace, heating up and carbonizing under the protection of inert gas;

[0057]...

Embodiment 3

[0072] The production technology of the shuttle-shaped environmental protection bamboo stick of the present embodiment comprises the following steps:

[0073] (1) Moso bamboo is cut into bamboo strips of 150-250mm length, and bamboo strips are carried out to remove green, yellow and dry;

[0074] (2) the dried bamboo strips are machined into thick bamboo sticks, and made into bamboo sticks through a round stick machine;

[0075] (3) Put the bamboo sticks in the pressure tank, and spray water vapor into the tank, so that the temperature in the pressure tank is 120 degrees, and the pressure is 0.4MPa for 25 minutes, and then the bamboo sticks are immersed in the sterilizing solution. , Cooking for 45 minutes under the condition of pressure 0.5MPa;

[0076] (4) drying the cooking bamboo sticks in the step (3), placing them in the carbonization furnace, heating up and carbonizing under the protection of inert gas;

[0077] (5) Place the carbonized bamboo sticks in the activation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of bamboo product processing, in particular to a production process of a shuttle-shaped environment-friendly bamboo stick. The process comprises the following steps: (1) moso bamboo is cut into bamboo canes; (2) the bamboo canes are processed into thick bamboo sticks through a machine, and the thick bamboo sticks are processed into bamboo sticks througha round bar machine; (3) the bamboo sticks are placed in a pressure tank body, water vapor is sprayed into the tank body, and then the bamboo sticks are soaked into the sterilization liquid; (4) thebamboo sticks are placed into a carbonization furnace for heating carbonization under the protection of inert gas; (5) the carbonized bamboo sticks is placed into an activating solution; and (6) the bamboo sticks is placed into an activation furnace and activation treatment is performed in a high-purity N2 atmosphere. The invention provides a production process of a fusiform environment-friendly bamboo stick, which can effectively improve the hardness of the bamboo stick, has high impact strength and realizes excellent mildew-proof and antibacterial effects.

Description

technical field [0001] The invention relates to the technical field of bamboo product processing, in particular to a production process of a shuttle-shaped environmentally friendly bamboo stick. Background technique [0002] Bamboo, also known as bamboo, is a perennial plant. It is a branch of Gramineae. It is distributed in subtropical regions. Some are as low as grass, and some are as tall as trees. Seeds multiply, and its seeds are called bamboo rice, which are mainly distributed in tropical, subtropical to warm temperate regions. Bamboo products refer to products made of bamboo as raw materials for processing. [0003] At present, bamboo is more used in bamboo sticks. The existing bamboo stick production process: bamboo sticks-sulfur fumigation (hydrogen peroxide cooking)-drying-follow-up production-finished product packaging. Problems and shortcomings: finished bamboo sticks have sour taste, there is A large number of chemical residues. Bamboo sticks are treated with c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/318C01B32/342A01N65/42A01N65/26A01N65/22A01N65/20A01N65/08A01P3/00A01P1/00
CPCA01N65/00A01N65/08A01N65/20A01N65/22A01N65/26A01N65/42C01B32/318C01B32/342
Inventor 张红忠
Owner 黄山市黟县宏联竹制工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap